Adsorption Characteristics of Acetaldehyde on Activated Carbons Prepared from Corn-Based Biomass Precursor

Effective Removal of Acetaldehyde Using Piperazine/Nitric Acid Co-Impregnated Bead-Type Activated Carbon

Acetaldehyde (CH₃CHO) in the atmosphere is associated with adverse health effects. Among the various options for use in removing CH₃CHO, adsorption is often employed because of its convenient application and economical processes, particularly when using activated carbon. In previous studies, the surface of activated carbon has been modified with amines to remove CH₃CHO from the atmosphere via adsorption. However, these materials are toxic and can have harmful effects on humans when the modified activated carbon is used in air-purifier filters. Therefore, in this study, a customized bead-type activated carbon (BAC) with surface modification options via amination was evaluated for removing CH₃CHO. Various amounts of non-toxic piperazine or piperazine/nitric acid were used in amination. Chemical and physical analyses of the surface-modified BAC samples were performed using Brunauer-Emmett-Teller measurements, elemental analyses, and Fourier transform infrared and X-ray photoelectron spectroscopy. The chemical structures on the surfaces of the modified BACs were analyzed in detail using X-ray absorption spectroscopy. The amine and carboxylic acid groups on the surfaces of the modified BACs are critical in CH₃CHO adsorption. Notably, piperazine amination decreased the pore size and volume of the modified BAC, but piperazine/nitric acid impregnation maintained the pore size and volume of the modified BAC. In terms of CH₃CHO adsorption, piperazine/nitric acid impregnation resulted in a superior performance, with greater chemical adsorption. The linkages between the amine and carboxylic acid groups may function differently in piperazine amination and piperazine/nitric acid treatment.

MgO modified zeolite facilitated low temperature chemisorptive removal of gaseous acetaldehyde into value added intermediate as desorption product

The adsorptive removal of acetaldehyde is more compatible for real-world applications. However, it must be upgraded from simple adsorption to a high efficiency process with value added products. This study develops a modified zeolite with Mg²⁺ ions that possesses acid-base sites for the removal of acetaldehyde at room temperature. Through a modified procedure, MgO is coated on commercial zeolite (13x), achieving a porosity of 501 m² g^-1 with MgO particles of 100 nm and pore diameter of 2.6 nm, and high breakthrough capacity of 50.00 mg/g. The initial pH and concentration of Mg²⁺ ion 12.5 and 0.2 M, respectively, with a maximum breakthrough capacity of 12.72 mg/g at 10% humidity. Significant variations in breakthrough capacity with respect to humidity in the presence of H₂S and NH₃ demonstrate the effects of water and gases on adsorption efficiency. Desorptive oxidation of adsorbed acetaldehyde at 250 °C yielded a high molecular weight intermediate ethylene oxide formation. The oxidation is followed by aldol condensation and hydrogenation. The higher breakthrough capacity and the intermediate product yielded using the developed MgO-zeolite proves the acid-base reaction sites involved in acetaldehyde removal follows chemisorption and possible process scale-up.