Embedded ultra-high stability flexible transparent conductive films based on exfoliated graphene-silver nanowires-colorless polyimide

MXene and AgNW based flexible transparent conductive films with sandwich structure for high-performance EMI shielding and electrical heaters

With the popularization of 5G technology and the development of science and technology, flexible and transparent conductive films (TCF) are increasingly used in the preparation of optoelectronic devices such as electromagnetic shielding devices, transparent flexible heaters, and solar cells. Silver nanowires (AgNW) are considered the best material for replacing indium tin oxide to prepare TCFs due to their excellent comprehensive properties. However, the loose overlap between AgNWs is a significant reason for the high resistance. This article investigates a sandwich structured conductive network composed of AgNW and Ti3C2Tx MXene for high-performance EMI shielding and transparent electrical heaters. Polyethylene pyrrolidone (PVP) solution was used to hydrophilic modify PET substrate, and then MXene, AgNW, and MXene were assembled layer by layer using spin coating method to form a TCF with a sandwich structure. One-dimensional AgNW is used to provide electron transfer channels and improve light penetration, while two-dimensional MXene nanosheets are used for welding AgNWs and adding additional conductive channels. The flexible TCF has excellent transmittance (85.1 % at 550 nm) and EMI shielding efficiency (27.1 dB). At the voltage of 5 V, the TCF used as a heater can reach 85.6 °C. This work offers an innovative approach to creating TCFs for the future generation.

Chemically-stable flexible transparent electrode: gold-electrodeposited on embedded silver nanowires

Silver nanowires (AgNWs) with a low diameter, high aspect ratio, stable suspension, and easy synthesis have recently attracted the optoelectronic industry as a low-cost alternative to indium tin oxide transparent conductive films. However, silver nanowires are not chemically stable, and their conductivity diminishes over time due to reactions with atmospheric components. This is a bottleneck for their wide industrial applications. In this study, we aim to address this issue by synthesizing silver nanowires with an average diameter of approximately 65 nm and a length of approximately 13 µm. The prepared Ag nanowires are then applied to fabricate transparent, flexible, and chemically stable conductive films. The fabrication includes spraying of silver nanowires suspension on a glass substrate followed by Dr. blade coating of polystyrene (PS) solution and delamination of the PS-AgNWs film. The resulting film exhibits an optimum sheet resistance of 24 Ω/□ and transmittance of 84%. To further enhance the stability of the transparent conductive film, the facial and scalable double pulse electrodeposition method is used for coating of gold on the exposed surface of the AgNWs embedded in PS. The final transparent film with gold coating demonstrates a remarkable stability under harsh conditions including long exposure to UV light and nitric acid solution. After 100 min of UV/Ozone treatment, the increase in sheet resistance of the optimal PS-AgNW@Au sample is 15.6 times lower than the samples without gold coating. In addition, the change in sheet resistance after 2000 bending cycles in the optimal PS-AgNW@Au electrode is measured and it showed an increase of only 22% of its initial sheet resistance indicating its good flexibility. The proposed electrode performs an excellent chemical stability, good conductivity, transparency, and flexibility that makes it a potential candidate for various optoelectronic devices.