Surface properties and bacterial adhesion on polyurethane central catheters: Impact of ethanol lock solution

It was shown in the literature that ethanol locks have a positive effect on preventing catheter-related infections in patients with central venous catheters without causing any microbial resistance. However, ethanol is known to interact with polyurethanes. The consequences of this interaction on the catheter surface properties were studied as it can impact the biocompatibility of the material and the adhesion phenomena onto the surface. No physical and chemical degradation was put into evidence, but low molecular weight compounds such as additives were extracted from the catheter bulk or migrated and exudated onto its surface. Nevertheless, as far as bacterial adhesion is concerned, after the catheter was locked and the lock removed, the surface modifications promoted no adhesion.

Impact of mechanical stress on flexible tubing used for biomedical applications: Characterization of the damages and impact on the patient's health

Flexible tubing is a key part of a lot of medical devices used in hospital, but may be subjected to a lot of various mechanical stresses that can led to the failure or to complications for the patients. The nature and causes of these mechanical stresses were listed for peristaltic pump tubing, infusion set tubing and catheters. Their consequences in term of tubing damages and particular contamination were reported. The impact of the chemical nature of the tubing, of its size and also the impact of various parameters of the clinical acts were reviewed. Last the consequences for the patient's health were discussed.

Atomic force microscopy and scanning electron microscopy as alternative methods of early identification of pathogens causing catheter-related bloodstream infections of patients in ICU

Introduction

Vascular catheters are an indispensable element of the therapy of patients in intensive care. Their use is associated with the possibility of complications, including infectious. According to various sources, the incidence of catheter-related bloodstream infections (CRBSIs) ranges from 0.1 to 22.7 per 1,000 catheter days.

Materials and Methods

The central venous catheter tip culture samples were collected from 24 patients with suspected catheter-related bloodstream infection, from three intensive care units (ICUs). The results of microscopic examinations: atomic force microscope (AFM) and scanning electron microscope (SEM) were compared with the results of microbiological analysis of the central venous catheter tip and blood collected from the catheter.

Results

The microscopic examination and microbiological analysis of both the blood and central venous catheter samples confirmed the presence of microorganisms in 16 cases (double positive result). Our study was conducted in a short period of time (up to 6 hours) and it gave an initial answer to the question about the type of microorganisms colonising the central venous catheter. In one patient the infection was not caused by removal of the central venous catheter. However, not all results were fully consistent within the two diagnostic methods. The colonisation of the central venous catheter with Pseudomonas aeruginosa and Staphylococcus epidermidis was microbiologically confirmed, but it was not confirmed by the microscopic examination of the sample collected from patient No. 20. However, the examination enabled preliminary assessment of the microorganism colonising the catheter, which may have caused the blood infection. It cannot be ruled out that Pseudomonas aeruginosa bacilli were grown on the catheter that came into contact with blood from another source of infection, e.g. the respiratory, nervous or urinary systems. Information on the presence of cocci-shaped bacteria forming characteristic clusters or rods may enable initial diagnosis of catheter-related bloodstream infection if it is accompanied by typical clinical symptoms. Alternative diagnostics also provides valuable information on the presence of biofilm, which is a factor hindering the body’s response to infection and penetration of antibiotics.

Conclusions

Our pilot study presents new diagnostic possibilities of microscopic imaging with the atomic force microscope (AFM) and scanning electron microscope (SEM) to identify pathogens on routinely used disposable medical devices, such as the central venous catheter. On the other hand, this range of diagnostics reveals the potential to constantly improve medical materials which come into direct contact with patients’ tissues. It is important to create a database of microscopic images, which would be a repeatable diagnostic pattern and fully correlated with the results of microbiological analysis, because it would facilitate initial quick diagnosis of a potential CRBSI.

Surface modification strategies for hemodialysis catheters to prevent catheter-related infections: A review

Insertion of a central venous catheter is one of the most common invasive procedures applied in hemodialysis therapy for end-stage renal disease. The most important complication of a central venous catheter is catheter-related infections that increase hospitalization and duration of intensive care unit stay, cost of treatment, mortality, and morbidity rates. Pathogenic microorganisms, such as, bacteria and fungi, enter the body from the catheter insertion site and the surface of the catheter can become colonized. The exopolysaccharide-based biofilms from bacterial colonies on the surface are the main challenge in the treatment of infections. Catheter lock solutions and systemic antibiotic treatment, which are commonly used in the treatment of hemodialysis catheter-related infections, are insufficient to prevent and terminate the infections and eventually the catheter needs to be replaced. The inadequacy of these approaches in termination and prevention of infection revealed the necessity of coating of hemodialysis catheters with bactericidal and/or antiadhesive agents. Silver compounds and nanoparticles, anticoagulants (e.g., heparin), antibiotics (e.g., gentamicin and chlorhexidine) are some of the agents used for this purpose. The effectiveness of few commercial hemodialysis catheters that were coated with antibacterial agents has been tested in clinical trials against catheter-related infections of pathogenic bacteria, such as Staphylococcus aureus and Staphylococcus epidermidis with promising results. Novel biomedical materials and engineering techniques, such as, surface micro/nano patterning and the conjugation of antimicrobial peptides, enzymes, metallic cations, and hydrophilic polymers (e.g., poly [ethylene glycol]) on the surface, has been suggested recently.

Do bevacizumab solutions interact with silicone or polyurethane catheters during an infusion through implantable venous access ports?

This work aims to evaluate the possible impact of interactions between bevacizumab solutions and an implantable port equipped with a silicone or a polyurethane catheter after infusion through a complete infusion set-up in simulated use conditions. Physico-chemical and structural stability of bevacizumab solution was assessed by visual examination, subvisible particles counting, dynamic light scattering, size exclusion chromatography and ion exchange chromatography. Mechanical properties of the catheters were evaluated by measuring Shore A hardness, strain at break, strain at stress and Young's modulus. The physico-chemical surface state of the catheters was assessed by FTIR-ATR spectroscopy, scanning electron microscopy (SEM) and by water contact angle measurement. The analysis of the bevacizumab solution did not highlight any signs of instability or loss of active substance. Mechanical properties of both materials remained unchanged after the infusion. During material analysis, a decrease in water contact angle observed after infusion and was more pronounced for polyurethane catheters than for silicone, possibly due to bevacizumab adsorption or possible leachable extraction from the materials. Surface modifications were also noted at SEM. This study did not highlight any modifications that could alter the quality of the bevacizumab infusion, nor of the infusion catheter in polyurethane or silicone, despite a modification of surface hydrophilicity. Even if after a single infusion, implantable ports remained safe to use, they aim to be used for several infusion of various drugs during their lifetime, and further studies are needed to assess the impact of repeated infusions.

Recent Advances in Polyesters for Biomedical Imaging

Several synthetic materials exhibiting contrast imaging properties have become vital to the field of biomedical imaging. Polymeric biomaterials and metals are commonly used imaging agents and can assist in the monitoring of therapy response, migration, degradation, changes in morphology, defects, and image-guided surgery. In comparison to metals, most bio and synthetic polymers lack inherent imaging properties. Polymeric biomaterials, specifically polyesters, have gained a considerable amount of attention due to their unique properties including biocompatibility, biodegradation, facile synthesis, and modification capability. Polyester implants and nanomaterials are available on the market or are in clinical trials for many applications including: dental implants, cranio-maxilofacial implants, soft tissue sutures and staples, abdominal wall repair, tendon and ligament reconstruction, fracture fixation devices, and coronary drug eluting stents. This review aims to provide a summary of the recent developments of polyesters with bioimaging contrast properties. The three main approaches to prepare bioimaging polyesters (coating, encapsulation, and functionalization) are discussed in depth. Furthermore, commonly used imaging modalities including X-ray computed tomography, magnetic resonance imaging, ultrasound, fluorescence, and radionucleotide polyester contrast agents are highlighted. In each section, examples of impactful bioimaging polyesters in the five major imaging modalities are evaluated.

Complication Rates Observed in Silicone and Polyurethane Catheters of Totally Implanted Central Venous Access Devices Implanted in the Upper Arm

PURPOSE

To present frequency and types of complications related to silicone (SI) versus polyurethane (PUR) catheters of totally implanted venous access devices (TIVADs) placed in the upper arm.

MATERIAL AND METHODS

A cohort of 2,491 consecutive patients with TIVADs implanted between 2006 and 2015 was retrospectively analyzed. Complications were classified according to SIR guidelines. Pearson χ² test was used for categorical variables, and Student t test was used for continuous variables. Nominal P values were reported, and 2-sided P values < .05 were considered significant.

RESULTS

Of 2,270 patients meeting the inclusion criteria, 538 had an SI catheter, and 1,732 had a PUR catheter. Total dwell time was 584,853 catheter days. Mean total complication rate was 12.25% (SI, 14.87%; PUR, 11.43%; P = .040). Subanalysis revealed significant differences for material failures (eg, catheter fracture [SI, 3.35%; PUR, 0.06%; P < .001] and thrombotic catheter occlusion/venous thromboses [SI, 2.79%/0.74%; PUR, 1.33%/3.17%; P < .001]) but nonsignificant differences for infections (eg, local infection and catheter-related sepsis [SI, 4.64%; PUR, 4.68%; P = 1]) or other nonthrombotic dysfunctions (eg, catheter detachment, line migration, wound dehiscence [SI, 3.35%; PUR, 2.19%; P = .179]).

CONCLUSIONS

The reported data suggest different risk profiles in SI catheters compared with PUR catheters, with more material failures and thrombotic catheter occlusions in SI catheters and more venous thromboses in PUR catheters.

Examination of radio-opacity enhancing additives in shape memory polyurethane foams

Three microparticle additives, tungsten (W), zirconium oxide (ZrO2), and barium sulfate (BaSO4) were selected to enhance the radio-opacity in shape memory polymer (SMP) foam biomaterials. The addition of filler causes no significant alterations of glass transition temperatures, density of the materials increases, pore diameter decreases, and total volume recovery decreases from approximately 70 times in unfilled foams to 20 times (4% W and 10% ZrO2). The addition of W increases time to recovery; ZrO2 causes little variation in time to shape recovery; BaSO4 increases the time to recovery. On a 2.00 mean X-ray density (mean X.D.) scale, a GDC coil standard has a mean X.D. of 0.62; 4% W enhances the mean X.D. to 1.89, 10% ZrO2 to 1.39 and 4% BaSO4 to 0.74. Radio-opacity enhancing additives could be used to produce SMP foams with controlled shape memory kinetics, low density, and enhanced X-ray opacity for medical materials.

Antibacterial coatings on haemodialysis catheters by photochemical deposition of silver nanoparticles

Antibacterial coatings on catheters for acute dialysis were obtained by an innovative and patented silver deposition technique based on the photo-reduction of the silver solution on the surface of catheter, with consequent formation of antibacterial silver nanoparticles. Aim of this work is the structural and morphological characterization of these medical devices in order to analyze the distribution and the size of clusters on the polymeric surface, and to verify the antibacterial capability of the devices treated by this technique against bacterial proliferation. The structure and morphology of the silver nanoparticles were investigated by using scanning and transmission electron microscopy. The antimicrobial capability of the catheters after silver deposition was confirmed by antibacterial tests with Escherichia coli. Both scanning electron microscopy analysis and antibacterial tests were performed also after washing catheters for 30 days in deionized water at 37°C, relating these data to thermogravimetric analysis and to energy dispersive spectroscopy, in order to check the resistance of coating and its antimicrobial capability after the maximum time of life of these devices.