Strontium hydroxyapatitein situgel-forming system - a new approach for minimally invasive bone augmentation

Animal models of vertical bone augmentation (Review)

Vertical bone augmentation is an important challenge in dental implantology. Existing vertical bone augmentation techniques, along with bone grafting materials, have achieved certain clinical progress but continue to have numerous limitations. In order to evaluate the possibility of using biomaterials to develop bone substitutes, medical devices and/or new bone grafting techniques for vertical bone augmentation, it is essential to establish clinically relevant animal models to investigate their biocompatibility, mechanical properties, applicability and safety. The present review discusses recent animal experiments related to vertical bone augmentation. In addition, surgical protocols for establishing relevant preclinical models with various animal species were reviewed. The present study aims to provide guidance for selecting experimental animal models of vertical bone augmentation.

In vitro and in vivo biocompatibility of calcium-phosphate scaffolds three-dimensional printed by stereolithography for bone regeneration

Stereolithography (SLA) is an interesting manufacturing technology to overcome limitations of commercially available particulated biomaterials dedicated to intra-oral bone regeneration applications. The purpose of this study was to evaluate the in vitro and in vivo biocompatibility and osteoinductive properties of two calcium-phosphate (CaP)-based scaffolds manufactured by SLA three-dimensional (3D) printing. Pellets and macro-porous scaffolds were manufactured in pure hydroxyapatite (HA) and in biphasic CaP (HA:60-TCP:40). Physico-chemical characterization was performed using micro X-ray fluorescence, scanning electron microscopy (SEM), optical interferometry, and microtomography (μCT) analyses. Osteoblast-like MG-63 cells were used to evaluate the biocompatibility of the pellets in vitro with MTS assay and the cell morphology and growth characterized by SEM and DAPI-actin staining showed similar early behavior. For in vivo biocompatibility, newly formed bone and biodegradability of the experimental scaffolds were evaluated in a subperiosteal cranial rat model using μCT and descriptive histology. The histological analysis has not indicated evidences of inflammation but highlighted close contacts between newly formed bone and the experimental biomaterials revealing an excellent scaffold osseointegration. This study emphasizes the relevance of SLA 3D printing of CaP-based biomaterials for intra-oral bone regeneration even if manufacturing accuracy has to be improved and further experiments using biomimetic scaffolds should be conducted.

In Situ Generated Medical Devices

Medical devices play a major role in all areas of modern medicine, largely contributing to the success of clinical procedures and to the health of patients worldwide. They span from simple commodity products such as gauzes and catheters, to highly advanced implants, e.g., heart valves and vascular grafts. In situ generated devices are an important family of devices that are formed at their site of clinical function that have distinct advantages. Among them, since they are formed within the body, they only require minimally invasive procedures, avoiding the pain and risks associated with open surgery. These devices also display enhanced conformability to local tissues and can reach sites that otherwise are inaccessible. This review aims at shedding light on the unique features of in situ generated devices and to underscore leading trends in the field, as they are reflected by key developments recently in the field over the last several years. Since the uniqueness of these devices stems from their in situ generation, the way they are formed is crucial. It is because of this fact that in this review, the medical devices are classified depending on whether their in situ generation entails chemical or physical phenomena.

Osteogenic, anti-osteoclastogenic and immunomodulatory properties of a strontium-releasing hybrid scaffold for bone repair

Strontium (Sr) is known to stimulate osteogenesis, while inhibiting osteoclastogenesis, thus encouraging research on its application as a therapeutic agent for bone repair/regeneration. It has been suggested that it may possess immunomodulatory properties, which might act synergistically in bone repair/regeneration processes. To further explore this hypothesis we have designed a Sr-hybrid system composed of an in situ forming Sr-crosslinked RGD-alginate hydrogel reinforced with Sr-doped hydroxyapatite (HAp) microspheres and studied its in vitro osteoinductive behaviour and in vivo inflammatory response. The Sr-hybrid scaffold acts as a dual Sr²⁺ delivery system, showing a cumulative Sr²⁺ release of ca. 0.3 mM after 15 days. In vitro studies using Sr²⁺concentrations within this range (0 to 3 mM Sr²⁺) confirmed its ability to induce osteogenic differentiation of mesenchymal stem/stromal cells (MSC), as well as to reduce osteoclastogenesis and osteoclasts (OC) functionality. In comparison with a similar Sr-free system, the Sr-hybrid system stimulated osteogenic differentiation of MSC, while inhibiting the formation of OC. Implantation in an in vivo model of inflammation, revealed an increase in F4/80⁺/CD206⁺ cells, highlighting its ability to modulate the inflammatory response as a pro-resolution mediator, through M2 macrophage polarization. Therefore, the Sr-hybrid system is potentially an appealing biomaterial for future clinical applications.

Immunohistochemical evaluation after Sr-enriched biphasic ceramic implantation in rabbits femoral neck: comparison of seven different bone conditions

Strontium (Sr) has shown effectiveness for stimulating bone remodeling. Nevertheless, the exact therapeutic values are not established yet. Authors hypothesized that local application of Sr-enriched ceramics would enhance bone remodeling in constant osteoporosis of rabbits' femoral neck bone. Seven different bone conditions were analyzed: ten healthy rabbits composed a control group, while other twenty underwent ovariectomy and were divided into three groups. Bone defect was filled with hydroxyapatite 30% (HAP) and tricalcium phosphate 70% (TCP) granules in 7 rabbits, 5% of Sr-enriched HAP/TCP granules in 7, but sham defect was left unfilled in 6 rabbits. Bone samples were obtained from operated and non-operated legs 12 weeks after surgery and analyzed by histomorphometry and immunohistochemistry (IMH). Mean trabecular bone area in control group was 0.393 mm2, in HAP/TCP - 0.226 mm2, in HAP/TCP/Sr - 0.234 mm2 and after sham surgery - 0.242 mm2. IMH revealed that HAP/TCP/Sr induced most noticeable increase of nuclear factor kappa beta 105 (NFkB 105), osteoprotegerin (OPG), osteocalcin (OC), bone morphogenetic protein 2/4 (BMP 2/4), collagen type 1α (COL-1α), interleukin 1 (IL-1) with comparison to intact leg; NFkB 105 and OPG rather than pure HAP/TCP or sham bone. We concluded that Sr-enriched biomaterials induce higher potential to improve bone regeneration than pure bioceramics in constant osteoporosis of femoral neck bone. Further studies on bigger osteoporotic animals using Sr-substituted orthopedic implants for femoral neck fixation should be performed to confirm valuable role in local treatment of osteoporotic femoral neck fractures in humans.

Injectable simvastatin gel for minimally invasive periosteal distraction: In vitro and in vivo studies in rat

OBJECTIVES

To evaluate whether the subperiosteal injection of simvastatin (SIM) with a novel in situ gel-forming system, SrHA/Alg (strontium hydroxyapatite/alginate), can stimulate vertical bone augmentation in a rat calvarial model.

MATERIAL AND METHODS

The SrHA/Alg solution was synthesized and combined with different doses of SIM (0.01, 0.02, 0.1, and 0.2 mg) to form the following groups: (1) SrHA/Alg only, (2) SrHA/Alg/0.01, (3) SrHA/Alg/0.02, (4) SrHA/Alg/0.1, and (5) SrHA/Alg/0.2. The SIM release pattern was analyzed, and rat primary periosteum-derived cell (PDC) responses were investigated. Twenty male Wistar rats were enrolled in the calvarial subperiosteal injection experiment with each animal receiving a 200-μl single subperiosteal injection of SrHA/Alg with different amounts of SIM (0, 0.01, 0.02, and 0.1 mg) incorporated (n = 5). The 0.2 mg dose group was not tested in vivo due to the severe toxicity found in vitro. The new bone formation was assessed histologically and radiologically at 8 weeks.

RESULTS

The slow release of SIM was confirmed, and PDC viability decreased in the SrHA/Alg/0.2 group. Alkaline phosphatase positive areas and mineralization areas were significantly greater in the SrHA/Alg/0.01 and SrHA/Alg/0.02 groups (p < .05). The mRNA expression level of Runx2 significantly increased in the SrHA/Alg/SIM-0.02 group by day 7 (p < .05) and significantly higher levels of VEGF were found in the SrHA/Alg/0.01 and SrHA/Alg/0.02 groups at different time points (p < .05). In vivo, no prominent clinical sign of inflammation was observed, and the most significant bone gain was shown in the SrHA/Alg/0.02 group (p < .05). The osteoclast formation within the newly formed bone area was reduced in the SrHA/Alg/0.1 group (p < .05).

CONCLUSIONS

When combined with SrHA/Alg system, the 0.02 mg SIM seemed to be the optimal dose to stimulate subperiosteal bone formation without inducing inflammation. This combination may hold potential therapeutic benefits for clinical bone augmentation in a minimally invasive manner.

New approach for vertical bone regeneration using in situ gelling and sustained BMP-2 releasing poly(phosphazene) hydrogel system on peri-implant site with critical defect in a canine model

An injectable hydrogel system with sustained bone morphogenetic protein 2 (BMP-2) release ability was developed for vertical bone regeneration at peri-implant sites and enhanced osseointegration of dental implants. In three young male beagle dogs, a pair of defects was created on both sides of the mandibular bone. Next, two implants were transplanted into each defect. In situ gelling polymer solutions with or without BMP-2 were applied to cover the implants and mandibular defects. The effects of the in situ gelling and sustained BMP-2 releasing (IGSR) hydrogel system on peri-implant bone regeneration were evaluated by radiologic examination, micro-computed tomography, and histomorphometric analysis. Twelve weeks after the treatment, significant bone generation at the peri-implant site occurred following BMP-2/IGSR hydrogel treatment. Bone volume and mineral density were increased by 1.7- and 1.3-fold, respectively (p < 0.01 and 0.05 vs. control, respectively) for the BMP-2/IGSR hydrogel system. And, 0.57-0.31 mm vertical bone generation was observed at the peri-implant site for the BMP-2/IGSR hydrogel system, while rare vertical bone generation occurred in the control group. The BMP-2/IGSR hydrogel system significantly increased bone to implant contact % between induced bone and existing bone (p < 0.05 and 0.01 vs. control). These vertical bone regeneration and higher osseointegration levels demonstrated the effectiveness of the BMP-2/IGSR hydrogel system. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 751-759, 2018.

Nanoreinforced Hydrogels for Tissue Engineering: Biomaterials that are Compatible with Load-Bearing and Electroactive Tissues

Given their highly porous nature and excellent water retention, hydrogel-based biomaterials can mimic critical properties of the native cellular environment. However, their potential to emulate the electromechanical milieu of native tissues or conform well with the curved topology of human organs needs to be further explored to address a broad range of physiological demands of the body. In this regard, the incorporation of nanomaterials within hydrogels has shown great promise, as a simple one-step approach, to generate multifunctional scaffolds with previously unattainable biological, mechanical, and electrical properties. Here, recent advances in the fabrication and application of nanocomposite hydrogels in tissue engineering applications are described, with specific attention toward skeletal and electroactive tissues, such as cardiac, nerve, bone, cartilage, and skeletal muscle. Additionally, some potential uses of nanoreinforced hydrogels within the emerging disciplines of cyborganics, bionics, and soft biorobotics are highlighted.

Preparation and investigation of a novel levobupivacaine in situ implant gel for prolonged local anesthetics

In this study, levobupivacaine (LBP) was successfully incorporated into implant application based on the concept of in situ gel (PECE). The physicochemical characterization (preparation, phase transition temperature, in vitro release) were investigated. The results of viscosity measurement showed that the preparations behaved like a fluid but formed a rigid gel when exposed to increasing temperature (37 °C). In vitro release, LBP was graduated released from the gels as time lapsed, suggesting that LBP was well entrapped in PECE in situ gels. As is shown in pharmacokinetic parameters, the half-life of LBP injection (2.7 h) was shorter than that of LBP in situ gels (23.9 h), suggesting that LBP injection was taken up by other tissues more rapidly than gels. The area under the curve of LBP in situ gels was 2.18 times the size of that of LBP injection (P< 0.05). In pharmacodynamic test, even after nine hours of injection, gel group could still maintain rather good anesthesia effect and rats' stinging reaction maintained at a relatively low level, which had obvious statistical differences compared to injection group.