Water Temperature Effect on Flexural Strength of Posterior Ankle Splint: An Experimental Study

Introduction

Plaster of Paris splints are commonly utilised for foot and ankle injuries. However, during follow-ups, some of these splints were found to be broken. Various methods, including splint form or augmentation changes, have been explored to enhance flexural strength. However, the impact of water temperature on the splint's flexural strength still needs to be studied. This research aimed to investigate the effect of water temperature on the flexural strength of the Plaster of Paris splint.

Materials and Methods

Three groups were set up based on different water temperatures: cold, hot, and room temperature. Posterior ankle splints were created and immersed in water at these varying temperatures, with five pieces tested per group. The splints were then allowed to harden fully over three days. Each splint underwent a tensile strength test using an axial pressure machine, which recorded their flexural strength data.

Results

There were no statistically significant differences in the general characteristics of the splints. The flexural strengths of the three splint groups (pre-cooled, pre-heated, and room temperature) were 182.6N, 162.45N, and 228.91N, respectively. Statistical analysis revealed that room-temperature splints demonstrated a statistically significant increase in flexural strength compared to pre-heated splints (p<0.05). However, they did not differ significantly from pre-cooled splints.

Conclusion

The highest flexural strength was observed in splints immersed in room-temperature water.

An experimental study on the impact of prosthesis temperature on the biomechanical properties of bone cement fixation

PURPOSE

To investigate the effect of the femoral component and tibial plateau component temperature on the strength of cement fixation during total knee arthroplasty (TKA).

METHODS

Femoral prosthesis, tibial plateau prosthesis, and polypropylene mold base were used to simulate TKA for bone cement fixation. Pre-cooling or pre-warming of femoral and tibial plateau components at different temperatures (4 °C, 15 °C, 25 °C, 37 °C, 45 °C), followed by mixing and stirring of bone cement at laboratory room temperature (22 °C), were performed during research. The prosthesis and the base adhered together, and the bone cement was solidified for 24 h at a constant temperature of 37 °C to verify the hardness of the bone cement with a push-out test.

RESULTS

The push-out force of the femoral prosthesis after fixation was higher than that of the tibial plateau prosthesis, and with the increase of the prosthesis temperature, the push-out force after fixation of the bone cement also increased linearly and the porosity of the prosthetic cement in the tibia and femur decreased as the temperature increased.

CONCLUSION

Without changing the mixing temperature and solidification temperature, the fixation strength of the femoral prosthesis is higher than that of the tibial plateau prosthesis. Properly increasing the temperature of the prosthesis can increase the push-out force of the fixation strength.

Femoral Stem Cementation in Hip Arthroplasty: The Know-How of a "Lost" Art

PURPOSE OF REVIEW

To describe the (1) indications, (2) preoperative precautions, and (3) stepwise technical details of modern femoral stem cemented fixation.

RECENT FINDINGS

Femoral stem cementation provides excellent implant longevity with a low periprosthetic fracture rate among patients with compromised bone quality or aberrant anatomy. Unfamiliarity with the details of modern cementation techniques among trainees who may lack frequent exposure to cementing femoral stems may preclude them from offering this viable option to suitable patients in later stages of their careers. As such, maximizing benefit from cemented femoral stem fixation among suitable candidates is contingent upon the meticulous use of modern cementation techniques. In addition to proper patient selection, modern cementation techniques emphasize the use of (1) pulsatile lavage of the femoral canal, (2) utilization of epinephrine-soaked swabs, (3) vacuum cement mixing, (4) retrograde cement introduction, (5) cement pressurization, and (6) the use of stem centralizers. Furthermore, identifying and optimizing the preoperative status of at-risk patients with pre-existing cardiopulmonary compromise, in addition to intraoperative vigilance, are essential for mitigating the risk of developing bone cement implantation syndrome. Further research is required to assess the utility of cemented femoral stem fixation among younger patients.

Towards the optimization of the preparation procedures of PMMA bone cement

The mechanical properties and thermal history of polymethyl-methacrylate bone cement vary significantly with the preparation procedure used. Because the polymerization reaction is exothermic, many researchers have attempted to minimize thermal osteonecrosis due to heat generation by altering procedures in the preparation of the cement. In most previous studies, only one or two aspects of the preparation procedure were controlled, and there has been little research that comprehensively examines the effects of preparation on the cure kinetics and resulting properties of bone cement. In this study, cement viscosity, cement layer thickness, initial cement temperature, initial metal component temperature, and mixing method were varied to assess the effects on the cement. Maximum temperature, polymerization time, necrosis index, bending strength, and porosity were chosen to evaluate the different preparation procedures, where an optimal procedure would minimize necrosis, reduce cement cure time, and maximize bending strength. Design of Experiments (DOE) was used to examine the main effects and interactions of preparation techniques. Among the most prominent results, it was found that the cure kinetics and the related quantities are primarily controlled by the initial metal component temperature and that the bending strength is most dependent on the mixing method. For the two formulations studied, the optimum preparation procedures should keep cement and metal components at room temperature prior to mixing with a vacuum mixing system. Reducing cement mantle thickness may also be advantageous, as it reduces the maximum temperature and the risk of tissue damage. © 2015 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 34:915-923, 2016.