Bond Strength of Fiber Posts to Composite Core: Effect of Surface Treatment With Er,Cr:YSGG Laser and Thermocycling

In Vitro Fracture Resistance of Endodontically Treated Premolar Teeth Restored with Prefabricated and Custom-Made Fibre-Reinforced Composite Posts

(1) Background: The study aimed to compare and analyse the differences between the features of prefabricated fibre-reinforced composite (FRC) posts and custom-made FRC posts in the form of a tape and confirm the necessity of using FRC posts in teeth treated endodontically in comparison to direct reconstruction with a composite material. (2) Methods: Sixty premolars after endodontic treatment were used. The teeth were divided into four groups (n-15). Group 1: teeth with embedded prefabricated posts (Mirafit White); group 2: teeth with embedded prefabricated posts (Rebilda); group 3 teeth with embedded custom-made posts in the form of a tape (EverStick); group 4: teeth without a post restored with composite material. The compressive strength of the teeth was tested using the Instron-5944 testing machine until the sample broke. The crystal structure of the investigated posts was detected with the X-ray diffractometer (3) Results: During the experiment, the maximum values of forces at which the damage of the restored premolar teeth after endodontic treatment occurred were obtained. The best results were obtained for teeth rebuilt with Rebilda Posts (1119 N), while teeth with cemented Mirafit White posts were the weakest (968 N). Teeth without an embedded FRC post, rebuilt only with light-cured composite material, obtained the lowest value-859 N. (4) Conclusions: The use of FRC posts increases the resistance to damage of an endodontically treated tooth when compared to direct restoration with light-cured composite material.

Effects of motion direction and power of Er,Cr:YSGG laser on pull-out bond strength of fiber post to root dentin in endodontically-treated single-canal premolar teeth

Background

Inadequate retention and gradual debonding of intracanal post from root dentin is a major cause of failure of endodontically treated teeth restored with fiber post.

Main body

This study aimed to assess the effect of surface treatment of quartz fiber posts with different powers and motion directions of Er,Cr:YSGG laser on their pull-out bond strength to root dentin in endodontically treated premolar teeth. In this study, 105 fiber posts were divided into 7 groups according to their surface treatment with different powers of Er,Cr:YSGG laser at 2780 nm wavelength, 20 Hz frequency and 150 μs pulse duration in circumferential (C) or longitudinal (L) motion directions: Control group (no treatment), 0.5 W laser in longitudinally (L0.5), 1.0 W laser in longitudinally (L1), 1.5 W laser in longitudinally (L1.5), 0.5 W laser in circumferentially (C0.5), 1.0 W laser in circumferentially (C1) and 1.5 W laser in circumferentially (C1.5). After cementation, pull-out bond strength was measured in Newton (N). Each sample was inspected under a stereomicroscope at × 25 magnification to determine the mode of failure. Two samples of each group were inspected under a scanning electron microscope (SEM). Data were analyzed using two-way ANOVA and Tukey’s test with significant level of 0.05. The pull-out bond strength of 0.5 W groups had significant differences with the control group (P = 0.009). The bond strength of 1.0 W and 1.5 W groups were not significantly different (P = 0.630) but were higher than the control and 0.5 W groups (P < 0.001). Motion direction of laser irradiation had no significant effect on the bond strength (P = 0.384). The interaction effect of power and motion direction of laser irradiation had no significant effect on the bond strength (P = 0.092).

Conclusion

Fiber posts treated with 0.5, 1.0 and 1.5 W Er,Cr:YSGG laser showed higher bond strength to dentin compared to posts with no surface treatment. However, the motion directions of laser irradiation had no significant effect on the bond strength. In order to minimize damage to post surface and achieving maximum bond strength, longitudinal surface treatment of posts with 1.0 W power of Er,Cr:YSGG laser is recommended.

Effect of laser irradiation on push-out bond strength of dental fiber posts to composite resin core buildups: A systematic review and meta-analysis

BACKGROUND

The bonding of fiber posts (FPs) to composite resin core buildups is a challenge due to limited penetration of resin to the polymeric matrix of FPs. This review article tries to answer this question: "What are the effects of laser surface treatment of FPs, compared to other surface roughening methods, on push-out bond strength (PBS) of FPs bonded to composite resin core buildups?"

METHODS

Searches were run in seven electronic databases with a focus on proper key words. Related titles and abstracts, up to February 2019, were screened, selected, read and subjected to quality assessments.

RESULTS

After the initial search, a total of 2635 articles were included in the study. Finally, 6 studies were reliable enough in methodology to be included. All the studies were in vitro with a total of 359 samples. Er:YAG (-0.05, 95% CI: -2.96 to 2.86; P = 0.97) and Er,Cr:YSGG (0.84, 95% CI: -0.12 to 1.81; P = 0.08) treated samples showed no significant overall mean differences in final PBS compared to the control groups. Moreover, pretreatment with Er,Cr:YSGG laser and sandblasting with 50 μm alumina showed an overall mean difference of -0.42 for PBS (95% CI: -1.23 to 0.39) with no significant differences.

CONCLUSIONS

Laser irradiation of FPs seems to provide no significant increase in PBS values of FPs bonded to composite resin core buildups. Effects of surface treatment of FPs with laser irradiation and sandblasting with 50 μm alumina might be similar in increasing the final PBS, either.