Cyclic fatigue and torsional resistance evaluation of Reciproc R25 instruments after simulated clinical use

Effect of simulated clinical use and sterilization on the cyclic fatigue resistance of nickel titanium files

Aim

Assess the effect of simulated clinical use and sterilization on the cyclic fatigue resistance of Race Evo and Tia Tornado Blue nickel titanium (NiTi) files.

Materials and Methods

For this study, a total of sixty-four NiTi files were selected, with thirty-two files each from two different manufacturers. Files from each manufacturer were subdivided into four subgroups (n = 8) based on the test parameters. The control groups included files that were neither used nor sterilized. Files from the test groups were used to prepare the root canals of extracted mandibular premolars and then sterilized. This procedure was repeated once, twice, or thrice, depending on the test group. All files were then subjected to a cyclic fatigue test. Data was statistically analyzed using the Kruskal-Wallis and Mann-Whitney U tests.

Results

No significant difference was observed in the number of cycles to failure (NCF) among the subgroups for both types of files (P = 0.869 for Tia Tornado Blue, P = 0.626 for Race Evo). Tia Tornado Blue files displayed significantly higher NCF values in the control (P = 0.021), once (P = 0.027), and thrice (P = 0.031) usage groups when compared to Race Evo files.

Conclusions

Repeated clinical use and sterilization for up to three cycles did not affect the cyclic fatigue resistance of Race Evo and Tia Tornado Blue files.

Influence of NiTi Wire Diameter on Cyclic and Torsional Fatigue Resistance of Different Heat-Treated Endodontic Instruments

We compared the mechanical properties of 2Shape mini TS2 (Micro-Mega, Besançon, France) obtained from 1.0 diameter nickel-titanium (NiTi) wires and 2Shape TS2 from 1.2 diameter nickel-titanium (NiTi) wires differently thermally treated at room and body temperature. We used 120 NiTi TS2 1.0 and TS2 1.2 files made from controlled memory (CM) wire and T-wire (n = 10). Cyclic fatigue resistance was tested by recording the number of cycles to fracture (NCF) at room and body temperatures using a customized testing device. Maximum torque and angle of rotation at failure were recorded, according to ISO 3630-1. Data were analyzed by a two-way ANOVA (p < 0.05). The CM-wire files had significantly higher NCFs at both temperatures, independent of wire dimensions. Testing at body temperature negatively affected cyclic fatigue of all files. The 1.0-mm diameter T-wire instruments showed higher NCF than the 1.2-mm diameter, whereas no significant differences emerged between the two CM wires at either temperature. The maximum torque was not significantly different across files. The TS2 CM-wire files showed significantly higher angular rotation to fracture than T-wire files. The TS2 CM-wire prototypes showed higher cyclic fatigue resistance than T-wire prototypes, regardless of wire size, exhibiting suitable torsional properties. Torsional behavior appears to not be affected by NiTi wire size.

Torsional, Static and Dynamic Cyclic Fatigue Resistance of Reciprocating and Continuous Rotating NiTi Instruments

INTRODUCTION

To evaluate torsional, dynamic and static cyclic fatigue resistance of the reciprocating One Reci (OR, Micromega, Besançon, France), WaveOne Gold (WOG, Dentsply Maillefer, Ballaigues, Switzerland), rotary One Curve (OC, MicroMega, Besançon, France) and ProTaper Next X2 (PTN X2, Dentsply Sirona, Ballaigues, Switzerland) instruments.

METHODS

A total of 120 NiTi instruments (n = 30) OR, WOG, OC and PTN X2 were used. Torque and rotation angle until failure under static torsion loading were measured according to the ISO 3630-1. Static and dynamic fatigue resistance was measured as the time to fracture (TTF) in an artificial stainless-steel canal with a 60° angle and 5-mm radius of curvature at intracanal temperature. The results were analyzed with one-way ANOVA and post-hoc Tukey tests. The alpha-type error was set at 5%. Fracture instruments from torsion and fatigue tests were examined with scanning electron microscope.

RESULTS

The OR showed higher static fatigue resistance and rotation angle at fracture than the WOG, OC and PTN X2 (P < .05). The WOG exhibited higher torsional resistance than the others (P < .05). Dynamic cyclic fatigue resistance tests had highest TTF than static for the PTN X2 and the WOG groups (P < .05). In the dynamic tests, the OR and WOG showed higher TTF than the OC and PTN X2 (P < .05).

CONCLUSIONS

Under these experimental condition, One Reci exhibited suitable mechanical properties with the highest cyclic fatigue resistance and angle of rotation among the tested instruments.

A comparative study of cyclic fatigue of 6 endodontic systems. An in vitro study

Background

Mechanical preparation and the formation of space for adequate obturation are included in root canal shaping, but the complex root canal anatomy may be affect it. Manufacturers have created different alloys like M-Wire, Blue-Wire, Gold-Wire or R-phase. Objective: This investigation was performed to verify the null hypothesis that there were not significant differences between size 25 instruments ESP Files Thermoflex, Protaper Ultimate, Protaper Next, Blueshaper, One Curve and 2Shape about cyclic fatigue and length of broken fragments.

Material and Methods

180 new size 25 files of the systems investigated were selected (n=30). Files were used with Endo Mate DT endo motor with speed and torque recommended by manufacturers, holding the instruments with clamping mechanism, with passive adjustment, glycerine and without pressure in a stainless-steel block. The time was calculated in seconds until fracture. Number of fatigue cycles was determined as (Resistance (s) x Speed)/60. Separated fragment lengths were calculated with digital Vernier caliper. Statistical analysis was carried out with the SPSS 18 programme at a 95% confidence level, using Levene´s Test to compare variances, Welch’s Test to compare means, and Games-Howell´s Test to reveal differences between groups.

Results

Levene’s Test determined no equal variances (P<0.05). Welch’s Test and ANOVA (P<0.05) showed significant differences in cyclic fatigue and separated fragment lengths. Games-Howell’s and Bonferroni´s Test established significant differences in multiple comparisons (P<0.05).

Conclusions

ESP Files Thermoflex was superior in cyclic fatigue. About separated fragment lengths, ESP Files Thermoflex, Protaper Ultimate and Blueshaper obtained longer lengths.

Key words:Cyclic fatigue, continuous movement, separated fragment lengths, rotary systems.