Stable Resin Bonding to Y-TZP Ceramic with Air Abrasion by Alumina Particles Containing 7% Silica

Zirconia bond strength durability following artificial aging: A systematic review and meta-analysis of in vitro studies

The present study systematically reviewed the literature regarding the bond strength durability of zirconia ceramics to resin-based luting cements after application of different bonding protocols and aging conditions. Electronic searches in PubMed, Scopus, and Web of Science databases were performed for relevant literature published between January 1st 2015 and November 15th 2022. Ninety-three (93) English language in-vitro studies were included. The percentage of the mean bond strength change was recorded prior to and after artificial aging, and the weighted mean values and 95% confidence intervals were calculated. Bonding protocols were classified based on the combination of MDP/non-MDP containing cement/primer and surface pretreatment, as well as the level of artificial aging performed. Alumina sandblasting (SA) was identified as the most frequently used surface pre-treatment while an insufficient number of studies was identified for each category of alternative surface treatments. The combination of MDP cement with tribochemical silica coating (TSC) or SA yielded more durable results after aging, while the application of SA and TSC improved bond durability when a non-MDP cement and a non-MDP primer were used. TSC may lead to increased bond durability compared to SA, whereas MDP cements may act similarly when combined with SA or TSC.

Aspects and Principles of Material Connections in Restorative Dentistry-A Comprehensive Review

The combination of two dissimilar materials has always been a serious problem in dentistry. In order to meet this challenge, it is necessary to combine both chemical methods (treatment with silanes, (meth)acrylic functional monomers) and the development of the surface of the joined material in a physical way, e.g., by sandblasting with alumina, alumina with silica, acid etching, the use of lasers and other means. The purpose of this literature review is to present all methods of joining dental composites with other materials such as ceramics, metal, another composite material. This review covers articles published within the period 2012-2022 in journals indexed in the PubMed database, written in English and describing joining different dental materials to each other. All the critical steps of new joint preparation have been addressed, including proper cleaning of the joint surface, the application of appropriate primers capable of forming a chemical bond between ceramics, zirconium oxide or metals and alloys, and finally, the application of new composite materials.

Effect of the nanofilm-coated zirconia ceramic on resin cement bond strength

Background. New surface treatments have been proposed to expand the clinical indications of zirconia prostheses. This study aimed to evaluate the effect of silica and fluorine nanofilms on zirconia ceramic on the resin cement bond strength. Methods. Zirconia blocks and discs underwent different surface treatments: untreated zirconia (CON), sandblasted, silica-coated alumina particles (30 µm) (SC), silica nanofilm (SN), and fluorine nanofilm (FN). Nanofilm deposition was performed through plasma enhanced chemical vapor deposition (PECVD). Zirconia surfaces were characterized on disks by morphology (atomic force microscopy, AFM), chemical analysis (x-ray photoelectron spectroscopy, XPS), and contact angle analysis. A silane coupling agent was applied on each treated surface, and a cylinder of resin cement was built up. Half of the specimens in each group were submitted to 6000 thermal cycles (TC). Bond strength was analyzed using the shear test, and the fractographic analysis was performed with stereomicroscopy and SEM/EDS. Statistical analysis was performed through one-way ANOVA and Tukey test in the non-aged and aged specimens. Results. Nanofilms modified the zirconia surface, which became more hydrophilic and chemically reactive. Chemical bonding between Si-O was found in SN, and FN promoted a fluorination process on the ceramic surface, converting zirconia into zirconium oxyfluoride. Specimens of the SN (TC) group failed on pre-testing. FN (TC) bond strength (3.8 MPa) was lower than SC (TC) and CON (TC) after shearing. Adhesive failure predominated in the experimental groups. Silica nanofilm failure occurred after aging. Conclusion. Silica and fluorine nanofilms deposited by PECVD did not promote effective bonding between zirconia and resin cement.