Improvement of White Spruce Wood Dimensional Stability by Organosilanes Sol-Gel Impregnation and Heat Treatment

Effects of Heat Treatment on Color, Dimensional Stability, Hygroscopicity and Chemical Structure of Afrormosia and Newtonia Wood: A Comparative Study of Air and Palm Oil Medium

In recent years, China is increasingly dependent on imported wood. Afrormosia and Newtonia are some of the imported species with good utilization potential. However, both of them also have problems with poor dimensional stability. In order to make better use of these two types of wood, the influence of heat treatment under air and palm oil conditions on the color, dimensional stability, and hygroscopicity of Afrormosia and Newtonia was investigated. The Afrormosia and Newtonia wood samples were heated in air or palm oil medium for two hours at 160 °C, 180 °C and 200 °C, respectively. Then, the color, weight changes, swelling, moisture absorption and chemical structure were evaluated for each case. As results, the heat treatments with air or palm oil increased the dark color of Newtonia and Afrormosia wood and this increase was proportional to the treatment temperature. The tangential and radial swelling coefficient for air heat treatment of Afrormosia wood at 200 °C were, respectively, reduced by 24.59% and 19.58%, while this reduction for Newtonia was 21.32% and 14.80%. The heat treatment in palm oil further improved the stability and hygroscopicity of the wood, showing that the Afrormosia samples treated by palm oil at 200 °C underwent a decrease of its tangential and radial swelling coefficient, respectively, by 49.34% and 45.88%, whereas the tangential and radial swelling coefficient of Newtonia treated under the same conditions were reduced by 42.85% and 33.63%, respectively. The heat treatments of Afrormosia and Newtonia samples under air at 200 °C diminished the water absorption by 21.67% and 22.12%. The water absorption of Afrormosia and Newtonia heat-treated under palm oil at 200 °C was reduced, respectively, by 39.40% and 37.49%. Moreover, the FTIR analysis showed the decrease of hydroxyl groups in proportion to the wood treatment temperature.

Effects of High-Temperature Heat Treatment Modification by Impregnation on Physical and Mechanical Properties of Poplar

To expand the application range of fast-growing poplar, a modification method of poplar impregnated with nano-SiO₂ and urea-formaldehyde resin was proposed in this study. Taking the mass ratio of nano-SiO₂ mass to the solid content of urea-formaldehyde resin impregnation solution (W), high-temperature (H), and high-temperature time (T) as influencing factors, the effects of impregnation high-temperature heat treatment modification on the physical and mechanical properties of fast-growing poplar were explored. At the same time, the weight loss rate, oven-dry density, dry shrinkage properties, swelling properties, modulus of rupture (MOR), and modulus of elasticity (MOE) of the modified poplar were measured. The research results show that both the weight loss rate and the coefficient of variation of the oven-dry density have a high correlation with the temperature; the high-temperature immersion heat treatment can reduce the dry shrinkage and swelling of poplar, improve the dimensional stability, MOR, and MOE. W is 0-1%, H is 160 °C, and T is 2-4 h. The impregnated heat-treated wood has good MOR and MOE. Therefore, the combination of nano-SiO₂ and urea-formaldehyde resin impregnation and heat treatment to modify poplar can improve some physical and mechanical properties of fast-growing poplar, expand the use of poplar, increase its added value, and realize high-value utilization.

Evaluation of the Dimensional Stability of Black Poplar Wood Modified Thermally in Nitrogen Atmosphere

Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA).

Flame Retardant Properties and Thermal Decomposition Kinetics of Wood Treated with Boric Acid Modified Silica Sol

This paper presents experimental research on the flame-retardant properties and thermal decomposition kinetics of wood treated by boric-acid-modified silica sol. The poplar wood was impregnated with pure silica sol and boric-acid-modified silica sol. The results showed that modifiers can be observed in the cell wall and cell lumen. The ignition time, second peak of the heat release rate, total heat release, and mass loss of the W-Si/B were delayed obviously. The composite silicon modification had a positive impact on carbonization. Thermogravimetric analysis showed that the residual mass of W-Si/B was enhanced and the thermal degradation rate was considerably decreased. By thermal decomposition kinetics analysis, the boric acid can catalyze the thermal degradation and carbonization of poplar wood. In other words, wood treated with boric-acid-modified silica sol showed significant improvement in terms of flame retardancy, compared with wood treated with common silica sol.