Severe Sulfuric Acid Attack on Self-Compacting Concrete with Granulometrically Optimized Blast-Furnace Slag-Comparison of Different Test Methods

Bio-corrosion in concrete sewer systems: Mechanisms and mitigation strategies

The deterioration of concrete sewer structures due to bio-corrosion presents critical and escalating challenges from structural, economic and environmental perspectives. Despite decades of research, this issue remains inadequately addressed, resulting in billions of dollars in maintenance costs and a shortened service life for sewer infrastructure worldwide. This challenge is exacerbated by the absence of standardized test methods and universally accepted mitigation strategies, leaving industries and stakeholders confronting an increasingly pressing problem. This paper aims to bridge this knowledge gap by providing a comprehensive review of the complex mechanisms of bio-corrosion, focusing on the formation and accumulation of hydrogen sulfide, its conversion into sulfuric acid and the subsequent deterioration of concrete materials. The paper also explores various factors affecting bio-corrosion rates, including environmental conditions, concrete properties and wastewater characteristics. The paper further highlights existing corrosion test strategies, such as chemical tests, in-situ tests and microbial simulations tests along with their general analytical parameters. The conversion of hydrogen sulfide into sulfuric acid is a primary cause of concrete decay and its progression is influenced by environmental conditions, inherent concrete characteristics, and the composition of wastewater. Through illustrative case studies, the paper assesses the practical implications and efficacy of prevailing mitigation techniques. Coating materials provide a protective barrier against corrosive agents among the discussed techniques, while optimised concrete mix designs enhance the inherent resistance and durability of the concrete matrix. Finally, this review also outlines the future prospects and challenges in bio-corrosion research with an aim to promote the creation of more resilient and cost-efficient materials for sewer systems.

New Sensors for Monitoring pH and Corrosion of Embedded Steel in Mortars during Sulfuric Acid Attack

The sulfuric acid attack is a common form of degradation of reinforced concrete in contact with industrial wastewater, mine water, acid rain, or in sewage treatment stations. In this work, new pH-sensitive IrOx electrodes were developed for monitoring the pH inside mortar or concrete. To test their ability, the pH sensors were embedded in mortar samples at different depths and the samples were exposed to sulfuric acid solution. In another set of experiments, iron wires were placed at the same depths inside similar mortar samples and their corrosion was monitored as the acid attacked the mortar. Severe acid attack led to cement dissolution and formation of gypsum. The new pH sensors succeeded in measuring the pH changes inside the mortars. The pH gradient, from the high acid environment to the high alkaline mortar interior, occurred in a narrow region. Corrosion of the iron electrodes started only when the acidic solution was in their close vicinity.

Utilization of Solid Waste from Brick Industry and Hydrated Lime in Self-Compacting Cement Pastes

The huge amount of solid waste from the brick manufacturing industry can be used as a cement replacement. However, replacement exceeding 10% causes a reduction in strength due to the slowing of the pozzolanic reaction. Therefore, in this study, the pozzolanic potential of brick waste is enhanced using ultrafine brick powder with hydrated lime (HL). A total of six self-compacting paste mixes were studied. HL 2.5% by weight of binder was added in two formulations: 10% and 20% of waste burnt brick powder (WBBP), to activate the pozzolanic reaction. An increase in the water demand and setting time was observed by increasing the replacement percentage of WBBP. It was found that the mechanical properties of mixes containing 5% and 10% WBBP performed better than the control mix, while the mechanical properties of the mixes containing 20% WBBP were found to be almost equal to the control mix at 90 days. The addition of HL enhanced the early-age strength. Furthermore, WBBP formulations endorsed improvements in both durability and rheological properties, complemented by reduced early-age shrinkage. Overall, it was found that brick waste in ultrafine size has a very high degree of pozzolanic potential and can be effectively utilized as a supplementary cementitious material.