Cuspal Deflection and Temperature Rise of MOD Cavities Restored through the Bulk-Fill and Incremental Layering Techniques Using Flowable and Packable Bulk-Fill Composites

Influence of Different Application Modes of a Universal Adhesive System on the Bond Strength of Bulk-Fill Composite Resin to Enamel and Dentin in Primary Teeth

OBJECTIVES

The objective of this study was to assess how the application mode of a universal adhesive system affects the microshear bond strength (μSBS) of bulk-fill and conventional composite resins to enamel and dentin in primary teeth.

METHODS

A total of 80 caries-free primary second molars were randomly assigned to eight experimental groups (n = 10) based on the bonding substrate (enamel or dentin), the application mode of the universal adhesive system (etch and rinse [E&R], or self-etch [SE]), and the type of composite resin used (bulk-fill or conventional). After bonding the composite resin to enamel or dentin, the μSBS of the bonded composite resins was measured.

RESULTS

The mean μSBS value of bulk-fill composite resin was significantly higher than that of conventional composite resin for both enamel and dentin substrates, regardless of the application mode (p < 0.001). An interaction effect between the bonding substrate and the application mode of the adhesive system was observed, indicating a significant relationship (p < 0.001). The highest μSBS values for primary teeth enamel were achieved using the E&R mode with bulk-fill composite resin, while for dentin specimens, the SE mode with bulk-fill composite resin yielded the highest μSBS values. The μSBS of the E&R group was significantly higher than that of the SE group for enamel specimens (p < 0.001), whereas the μSBS of the SE group was significantly higher than that of the E&R group for dentin specimens (p < 0.001).

CONCLUSION

Bulk-fill composite resin demonstrated higher μSBS in comparison to conventional composite resin. The universal adhesive system exhibited superior performance in the SE mode compared to the E&R mode on primary dentin. Pre-etching the enamel before the application of the universal adhesive enhanced the μSBS to primary teeth enamel, highlighting the importance of selectively acid etching the enamel of primary teeth.

Compressive strength and fluoride release profile of a glass ionomer cement reinforced with silver-hydroxyapatite-silica hybrid nanoparticles: An in vitro study

OBJECTIVES

This study aimed to prepare a glass ionomer (GI) cement reinforced with silver-hydroxyapatite-silica (Ag/HA/Si) hybrid nanoparticles and assess its compressive strength and fluoride release profile.

MATERIAL AND METHODS

In this in vitro, experimental study, 60 cylindrical specimens were fabricated with 4mm diameter and 6mm height in 6 groups (n=10) using BracePaste composite, GC Fuji II LC pure RMGI, and RMGI reinforced with 0.1wt%, 0.5wt%, 1wt%, and 2wt% Ag/HA/Si hybrid nanoparticles. The specimens were subjected to compressive force in a universal testing machine to measure their compressive strength (MPa). To assess their fluoride release profile, discs with 3mm diameter and 2mm thickness were fabricated from Fuji II LC pure resin-modified glass ionomer (RMGI), and RMGI with 0.1wt%, 0.5wt%, 1wt%, and 2wt% hybrid nanoparticles, and the concentration of released fluoride was measured by a digital ion-selective electrode. Data were analysed by ANOVA and Scheffe test (alpha=0.05).

RESULTS

The compressive strength was 114.14MPa for BracePaste composite, and 97.14, 97.84, 100.65, 109.5, and 89.33MPa for GI groups with 0%, 0.1%, 0.5%, 1% and 2% hybrid nanoparticles, respectively, with no significant difference among them (P=0.665). Addition of 1% (0.21±0.07μg/mL, P=0.029) and 2% (0.45±0.22μg/mL, P=0.000) hybrid nanoparticles to RMGI significantly increased the amount of released fluoride, compared with the control group (0.09±0.03μg/mL).

CONCLUSIONS

Addition of Ag/HA/Si hybrid nanoparticles to RMGI in the tested concentrations had no significant effect on its compressive strength but addition of 1wt% and 2wt% concentrations of Ag/HA/Si hybrid nanoparticles increased its fluoride release potential.

Thickness-Dependent Light Transmittance and Temperature Rise in Dual-Cure Bioactive and Light-Cure Bulk-Fill Composite Resins

This study aimed to assess the light transmittance (T) and temperature increase through different increments of dual-cure bioactive bulk-fill restorative material (ACTIVA), light-cure bulk-fill, and conventional composite resin materials. Cylindrical specimens with a diameter of 8 mm and heights of 1, 2, 3, and 4 mm of ACTIVA, Tetric-N-Ceram bulk-fill (TBF), Filtek One bulk-fill (FBF), and Filtek Z250 (FZ) (n = 6 per group, 96 in total) were light-cured with a visible blue low-intensity light-emitting diode (LED) (650-800 mW/cm² irradiance). T, and the temperature increase, were measured using an optical power meter and a digital thermometer during curing. The T mean values ranged between 0.012 and 0.239 (76.02 to 98.81% light attenuation), while the temperature rise mean values ranged between 9.02 and 20.80 °C. The parameters, including material type (partial eta squared (ηp²) = 0.284, p < 0.0001), thickness (ηp² = 0.284, p < 0.0001), and their interaction (ηp² = 0.185, p = 0.047), significantly affected the T values, whereas only the material type (ηp² = 0.352, p = 0.047) affected the temperature rise values. The T and temperature rise mean values were highest in ACTIVA increments of 1-mm increments, in particular, showing the highest T mean values, followed by similar increments of TBF. A significantly higher T was found in 1-mm increments compared to thicker increments for all materials (p < 0.0001), and a significant positive correlation existed between T and temperature rise values (r = 0.348, p = 0.001). These findings show that the bioactive material ACTIVA and TBF allow for better T than the other materials, with ACTIVA recording a higher temperature rise. However, the large light attenuation observed for all materials, irrespective of thickness, suggests that curing in more than one location with a low-intensity LED is necessary to optimize the curing process. Furthermore, incremental filling of bulk-fill materials using a low intensity LED could be beneficial.

Mechanical and Biomimetic Characteristics of Bulk-Fill Resin Dental Composites Following Exposure in a Simulated Acidic Oral Environment

During the last 10 years, various companies have marketed different "bulk-fill" resin dental composites for the restoration of posterior stress-bearing teeth; however, the impact of acidic conditions on these relatively newer materials has not been thoroughly investigated. Therefore, an attempt was made to evaluate the effect of acidic beverages on the mechanical biomimetic characteristics of four bulk-fill and one conventional nanohybrid resin-based dental composites (RBCs). The specimens of each RBC were stored in two acidic beverages namely 'Orange Juice' and 'Coca-Cola', whereas 'dry' and 'distilled water' storage of specimens served as controls. After 1 week of storage, flexural and surface hardness properties of specimens were determined using a universal testing machine and Vickers hardness tester, respectively. In general, the 'Coca-Cola' beverage caused the greatest degradation of flexural strength, flexural modulus, and surface hardness characteristics in all RBCs in contrast to the 'dry', 'distilled water' controls and 'Orange Juice' storage conditions. However, the overall mechanical biomimetic performance of nanohybrid RBCs was relatively better than all other bulk-fill RBCs and may, therefore, be considered a suitable candidate for the restoration of posterior stress-bearing permanent dentition.

Fracture Strength and Failure Modes of Endodontically Treated Premolars Restored with Compact and Hollow Composite Posts Subjected to Cyclic Fatigue

Physical and mechanical properties of continuous carbon or glass fiber reinforced endodontic posts are relevant to increase the retention and resistance of the tooth-restoration system. Hollow posts have been recently designed for delivering the luting cement through the post hole, thus enhancing the post-dentin interface by reducing the risk of air bubbles formation. Methods: Three type of endodontic posts, a carbon fiber hollow post, a glass fiber hollow post and a compact glass fiber post were investigated. Mechanical properties of these posts were assessed through bending tests. Teeth were subjected to fatigue cycling and the strength of restored teeth was detected through static tests. Failure modes were investigated through optical and scanning electron microscopy. Results show that composite posts increase the mechanical stability by more than 100% compared to premolars restored with particulate composite. Carbon fiber posts retain the highest strength (1467 N ± 304 N) among the investigated post and core restoration, but an unfavorable type of fracture has been observed, preventing the tooth re-treatment. Instead, more compliant posts (i.e., glass fiber reinforced composite, providing a strength of 1336 N ± 221 N), show a favorable mode of fracture that allows the re-treatment of teeth in the case that failure occurs. Glass fiber hollow posts show a good trade-off between strength and a favorable type of fracture.