Characterization and Properties of Water-Blown Rigid Polyurethane Foams Reinforced with Silane-Modified Nanosepiolites Functionalized with Graphite

Cooperative Effect of Chemical and Physical Processes for Flame Retardant Additives in Recycled ABS

In the present work, the effectiveness of four non-halogenated flame retardants (FR) (aluminium trihydroxide (ATH), magnesium hydroxide (MDH), Sepiolite (SEP) and a mix of metallic oxides and hydroxides (PAVAL)) in blends with recycled acrylonitrile-butadiene-styrene (rABS) was studied in order to develop a more environmentally friendly flame-retardant composite alternative. The mechanical and thermo-mechanical properties of the obtained composites as well as their flame-retardant mechanism were evaluated by UL-94 and cone calorimetric tests. As expected, these particles modified the mechanical performance of the rABS, increasing its stiffness at the expense of reducing its toughness and impact behavior. Regarding the fire behavior, the experimentation showed that there is an important synergy between the chemical mechanism provided by MDH (decomposition into oxides and water) and the physical mechanism provided by SEP (oxygen barrier), which means that mixed composites (rABS/MDH/SEP) can be obtained with a flame behavior superior to that of the composites studied with only one type of FR. In order to find a balance between mechanical properties, composites with different amounts of SEP and MDH were evaluated. The results showed that composites with the composition rABS/MDH/SEP: 70/15/15 wt.% increase the time to ignition (TTI) by 75% and the resulting mass after ignition by more than 600%. Furthermore, they decrease the heat release rate (HRR) by 62.9%, the total smoke production (TSP) by 19.04% and the total heat release rate (THHR) by 13.77% compared to unadditivated rABS; without compromising the mechanical behavior of the original material. These results are promising and potentially represent a greener alternative for the manufacture of flame-retardant composites.

Behavior Characteristics and Thermal Energy Absorption Mechanism of Physical Blowing Agents in Polyurethane Foaming Process

Polyurethane rigid foam is a widely used insulation material, and the behavior characteristics and heat absorption performance of the blowing agent used in the foaming process are key factors that affect the molding performance of this material. In this work, the behavior characteristics and heat absorption of the polyurethane physical blowing agent in the foaming process were studied; this is something which has not been comprehensively studied before. This study investigated the behavior characteristics of polyurethane physical blowing agents in the same formulation system, including the efficiency, dissolution, and loss rates of the physical blowing agents during the polyurethane foaming process. The research findings indicate that both the physical blowing agent mass efficiency rate and mass dissolution rate are influenced by the vaporization and condensation process of physical blowing agent. For the same type of physical blowing agent, the amount of heat absorbed per unit mass decreases gradually as the quantity of physical blowing agent increases. The relationship between the two shows a pattern of initial rapid decrease followed by a slower decrease. Under the same physical blowing agent content, the higher the heat absorbed per unit mass of physical blowing agent, the lower the internal temperature of the foam when the foam stops expanding. The heat absorbed per unit mass of the physical blowing agents is a key factor affecting the internal temperature of the foam when it stops expanding. From the perspective of heat control of the polyurethane reaction system, the effects of physical blowing agents on the foam quality were ranked in order from good to poor as follows: HFC-245fa, HFC-365mfc, HFCO-1233zd(E), HFO-1336mzzZ, and HCFC-141b.

Changes and Trends-Efficiency of Physical Blowing Agents in Polyurethane Foam Materials

This work developed a novel method for measuring the effective rate of a PBA (physical blowing agent) and solved the problem that the effective rate of a PBA could not be directly measured or calculated in previous studies. The results show that the effectiveness of different PBAs under the same experimental conditions varied widely, from approximately 50% to almost 90%. In this study, the overall average effective rates of the PBAs HFC-245fa, HFO-1336mzzZ, HFC-365mfc, HFCO-1233zd(E), and HCFC-141b are in descending order. In all experimental groups, the relationship between the effective rate of the PBA, rePBA, and the initial mass ratio of the PBA to other blending materials in the polyurethane rigid foam, w, demonstrated a trend of first decreasing and then gradually stabilizing or slightly increasing. This trend is caused by the interaction of PBA molecules among themselves and with other component molecules in the foamed material and the temperature of the foaming system. In general, the influence of system temperature dominated when w was less than 9.05 wt%, and the interaction of PBA molecules among themselves and with other component molecules in the foamed material dominated when w was greater than 9.05 wt%. The effective rate of the PBA is also related to the states of gasification and condensation when they reach equilibrium. The properties of the PBA itself determine the overall efficiency, while the balance between the gasification and condensation processes of the PBA further leads to a regular change in efficiency with respect to w around the overall average level.

Respiratory Adsorption of Organic Pollutants in Wastewater by Superhydrophobic Phenolic Xerogels

Organogel adsorbents are widely used for the adsorption of hard-to-degrade organic pollutants in wastewater due to their natural affinity to the organic phase in water. In this study, phenolic xerogels (PF) synthesised in the ethylene glycol inorganic acid system are used as a backbone and superhydrophobic phenolic xerogels (ASO-PF) are obtained by grafting aminosilanes onto the PF backbone via the Mannich reaction. The modified ASO-PF not only retains the pore structure of the original PF (up to 90% porosity), but also has excellent superhydrophobic properties (water contact angle up to 153°). Owing to the unique pore structure, ASO-PF has excellent compression properties, cycling 50% compression deformation more than 10 times without being damaged, with a maximum compression deformation of up to 80%. A squeeze-suction-squeeze approach is proposed for selective adsorption of organic pollutants in homogeneous solutions based on the recyclable compression properties of ASO-PF. The ASO-PF is put under negative pressure by squeezing, and when the pressure is released, the adsorbed liquid enters the ASO-PF, where the organic pollutants are retained by the adsorption sites in the skeleton, and then the remaining water is discharged by squeezing. This breathing ASO-PF holds great promise for organic pollutant adsorption and recovery applications.

Nanocomposites of Rigid Polyurethane Foam and Graphene Nanoplates Obtained by Exfoliation of Natural Graphite in Polymeric 4,4′-Diphenylmethane Diisocyanate

The influence of graphene nanoplates (GNPs) obtained by the ecofriendly exfoliation of natural graphite has been addressed on the mechanical and thermal insulating properties of rigid polyurethane foams (RPUFs). Few-layer GNPs with few defects were prepared in polymeric 4,4′-diphenylmethane diisocyanate (pMDI) under ultrasonication to obtain a GNP/pMDI dispersion. GNP/pMDI dispersions with different GNP concentrations were used to prepare RPUF nanocomposites via in situ polymerization. An important finding is that the GNP/pMDI dispersion exhibits lyotropic liquid crystalline behavior. It was found that the unique orientation of GNPs above the concentration of 0.1 wt% in the dispersion affected the mechanical and thermal insulation properties of the RPUF nanocomposites. GNP/RPUF nanocomposites with GNP concentrations at 0.2 wt% or more showed better thermal insulating properties than neat RPUF. The lyotropic liquid crystalline ordering of GNPs provides stable nucleation for bubble formation during foaming and prevents bubble coalescence. This decreases the average cell size and increases the closed cell content, producing GNP/RPUF nanocomposites with low thermal conductivity. Furthermore, GNPs incorporated into RPUF act as a barrier to radiant heat transfer through the cells, which effectively reduces the thermal conductivity of the resulting nanocomposites. It is expected that the nanocomposite of RPUF investigated in this study can be applied practically to improve the performance of thermal insulation foams.