The Impact of Simulated Gastric Acid and Toothbrushing on Surface Characteristics of Resin-Modified Glass-Ionomer Cements

Surface Roughness Examination of Glass Ionomer Restorative Cements Treated with Acidic and Basic Pediatric Medications: An In Vitro Study

Background

Consumption of different types of beverages and liquid drugs can affect of the surface properties of restorative material. This may lead to an increased probability of dental caries and periodontal inflammation.

Aim

This study evaluated and compared the effect of amoxicillin suspension (AMS) and azithromycin suspension (AZS) on the surface roughness (SR) of silver-reinforced glass ionomer (SGI) and nano resin-modified glass ionomer (NGI).

Material and Methods

Thirty disks (2 mm height × 4 mm diameter) of each glass ionomer (GI) type were prepared and subdivided into three groups (n = 10), which were separately exposed to AMS, AZS, and artificial saliva (AS). SR was evaluated by atomic force microscopy before and after three-immersion protocols repeated over a 3-week duration with 2-day intervals. In each protocol, the GI samples were exposed weekly to AMS three times daily, AZS once daily, and a full day to AS.

Results

This study demonstrated, for the first time, the effect of a basic drug (AZS) on the SR of GIs. Intra- and inter-group comparisons showed significant changes (P ˂ 0.05) in the SR pattern of the GIs after immersion cycles in AZS, AMS, and AS. However, the acidic medication (AMS) exhibited significantly higher changes in SGI than in NGI.

Conclusions

The SR of NGIs and SGIs can be significantly affected by the use of AMS and AZS suspensions. SGI demonstrated higher SR deterioration than NGI after immersion cycles in AMS.

The Impact of Gastric Juice on the Surface Roughness of Surface Sealant-Treated Provisional Restorations

BACKGROUND AND AIM

Gastroesophageal reflux disease causes gastric acid to enter the oral cavity, leading to mucosal changes and deterioration of dental hard tissues and materials. The purpose of this in vitro study was to evaluate the impact of gastric juice on the surface roughness of two types of acrylics used in provisional restorations.

MATERIALS AND METHODS

Acrytemp ® and Temdent acrylic resin discs (10 × 2 mm) totaling 80 were manufactured and divided into eight groups (n = 10). Groups were prepared as follows: Group 1 (Temdent + Universal Polish) (control), Group 2 (Temdent + Universal Polish + Biscover LV), Group 3 (Temdent + Universal Polish + Resin Glaze), Group 4 (Temdent + Universal Polish + Fortify Plus), Group 5 (Acrytemp + Universal Polish) (control), Group 6 (Acrytemp + Universal Polish + Biscover LV), Group 7 (Acrytemp + Universal Polish + Resin Glaze), and Group 8 (Acrytemp + Universal Polish + Fortify Plus). The resin discs were immersed in distilled water for 24 h and in gastric juice (pH = 2) for additional 24 h. The initial and final roughness values of samples were measured and analyzed with non-parametric statistics including Mann-Whitney U-test for pairwise comparison, Kruskall Wallis test for comparing more than two groups, and Wilcoxon signed rank test for within-group comparison (P < 0.05).

RESULTS

Surface roughness did not differ significantly between control groups. It notably increased for all samples with surface sealants, both initially and after gastric juice immersion (P < 0.05).

CONCLUSION

Surface sealants noticeably increased the roughness of two types of acrylic resins. After immersing in gastric juice, Group 4 (Temdent + Universal Polish + Fortify Plus) showed the highest roughness, while the untreated control groups remained the smoothest.