1
|
Sharma S, Dwivedi SP, Mohammed KA, Kumar A, Awwad FA, Khan MI, Ismail EAA. Investigation of surface hardness, thermostability, tribo-corrosion, and microstructural morphological properties of microwave-synthesized high entropy alloy FeCoNiMnCu coating claddings on steel. Sci Rep 2024; 14:5160. [PMID: 38431656 PMCID: PMC10908794 DOI: 10.1038/s41598-024-55331-y] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/01/2023] [Accepted: 02/22/2024] [Indexed: 03/05/2024] Open
Abstract
Deposition of high entropy alloy FeCoNiMnCu on SS-304 was carried out by microwave energy for application in "solid oxide fuel-cell (SOFC) interconnects". The ball-milling has been performed by taking "Fe, Co, Ni, Mn, and Cu" in equal 20 wt. % of before deposited on SS-304 substrate. The deposited steel with 20% Fe 20% Co 20% Ni 20% Mn 20% Cu high entropy alloy (HEA) was exposed to thermal-exposure in the air for up to 10 weeks at 800 °C. The uniform cladding distribution of 20% Fe 20% Co 20% Ni 20% Mn 20% Cu HEA particles can be apparently observed on SS-304 substrate by utilizing Scanning Electron Microscope (SEM), and Optical microscopy analysis. Homogeneity in the interfacial layer was evident by employing Scanning Electron Microscope (SEM) characterization. Results have indicated that after the thermal exposure of deposited steel with 20% Fe 20% Co 20% Ni 20% Mn 20% Cu in the air for up to ten weeks at 800 °C, a "protective Cr2O3 layer", and "high-entropy spinel coating" of (Fe, Co, Ni, Mn, Cu)3O4 have been formed. During microwave cladding, the emergence of harder-phases has contributed to the raised hardness. The wear behavior after coating of 20% Fe 20% Co 20% Ni 20% Mn 20% Cu HEA on SS-304 substrate has significantly enhanced due to the strengthened wear resistance and hardness of the coatings. Findings have exhibited that the formation of (Fe, Co, Ni, Mn, Cu)3O4 phase is a potential coating material for "SOFC interconnects" applications. Moreover, the cladding of SS304 with a composition of 20% Fe, 20% Co, 20% Ni, 20% Mn, and 20% Cu has demonstrated remarkable stability under thermal expansion studies. As the findings have revealed that the composite cladding has efficiently withstand significant variations in volume when subjected to elevated temperatures for a prolonged period of time, thus, exhibiting its superior thermal stability for SOFC-interconnect applications. Furthermore, the SEM images of the cladding surface, surface hardness, and tribocorrosion behavior of the coated material have been observed to identify the 20% Fe 20% Co 20% Ni 20% Mn 20% Cu HEA coating effect on SS-304 steel-substrate.
Collapse
Affiliation(s)
- Shubham Sharma
- Centre for Research Impact and Outcome, Chitkara University Institute of Engineering and Technology, Chitkara University, Rajpura, Punjab, 140401, India.
- School of Mechanical and Automotive Engineering, Qingdao University of Technology, Qingdao, 266520, China.
- Department of Mechanical Engineering, Lebanese American University, Kraytem, Beirut, 1102-2801, Lebanon.
| | - Shashi Prakash Dwivedi
- Department of Mechanical Engineering, Lloyd Institute of Engineering & Technology, Knowledge Park II, Greater Noida, Uttar Pradesh, 201306, India.
| | - Kahtan A Mohammed
- Faculty of Pharmacy, Jabir Ibn Hayyan Medical University, Najaf, Iraq
- Department of Medical Physics, Hilla University College, Babylon, Iraq
| | - Abhinav Kumar
- Department of Nuclear and Renewable Energy, Ural Federal University Named After the First President of Russia, Boris Yeltsin, 19 Mira Street, 620002, Ekaterinburg, Russia
| | - Fuad A Awwad
- Department of Quantitative Analysis, College of Business Administration, King Saud University, P.O. Box 71115, 11587, Riyadh, Saudi Arabia.
| | - M Ijaz Khan
- Department of Mechanical Engineering, Lebanese American University, Kraytem, Beirut, 1102-2801, Lebanon
- Department of Mechanics and Engineering Science, Peking University, Beijing, 100871, China
| | - Emad A A Ismail
- Department of Quantitative Analysis, College of Business Administration, King Saud University, P.O. Box 71115, 11587, Riyadh, Saudi Arabia
| |
Collapse
|
2
|
Sharma S, Dwivedi SP, Kumar A, Awwad FA, Khan MI, Ismail EAA. Enhancing tribo-mechanical, microstructural morphology, and corrosion performance of AZ91D-magnesium composites through the synergistic reinforcements of silicon nitride and waste glass powder. Sci Rep 2024; 14:3217. [PMID: 38331942 PMCID: PMC10853170 DOI: 10.1038/s41598-024-52804-y] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/08/2023] [Accepted: 01/23/2024] [Indexed: 02/10/2024] Open
Abstract
The present investigation has employed recycled waste glass powder (WGP) and silicon nitride (Si3N4) as reinforcing-agents within AZ91D-matrix composites. The composites were fabricated by employing the vacuum stir casting technique to mitigate the effects of oxidation and to ensure homogeneity, uniformity, and superior wettability among the AZ91D-matrix and reinforcements. A microscopic study provided confirmation of a uniform dispersion of WGP and Si3N4 particles throughout the AZ91D-matrix. The tensile strength of the AZ91D/WGP/Si3N4 composites rise with the inclusion of WGP particulates by up to 1.5 percent in AZ91D/7.5% Si3N4. However, the tensile strength of the AZ91D/9%Si3N4 composite have showed maximum value as compared to other chosen formulations/combinations in the current investigation. The tensile strength of AZ91D/1.5% WGP/7.5% Si3N4 composites has strengthened up to 12.13 percent with the comparison of base alloy AZ91D-matrix. In A1 formulated composite, the amount of WGP particulate has enhanced the hardness of the AZ91D-alloy by up to 1.5 percent. Findings, nevertheless has exhibited that the A6 formulated composite had superior outcomes in terms of hardness. The incorporation of "reinforcing-constituent particulates" with 1.5%WGP + 7.5%Si3N4 combination within the AZ91D-matrix, has further increased fatigue-strength by around 57.84 percent. A weight-loss of 0.312 mg was being unveiled for the A1 formulated fabricated composite. The weight-loss for the A6 formulated fabricated composite, however, was reported to be 0.294 mg. At 5 N loads, 2 m/s sliding speed, and 1000 m of sliding distance, the developed 1.5%WGP/7.5%Si3N4/AZ91D composites was reported to have a rate of wear, and frictional coefficient of 0.0025 mm3/m and 0.315, respectively. The investigation employing scanning electron microscopy (SEM) identified the presence of corrosion pits on the surfaces that had undergone corrosion. These pits were found to be a result of localised surface assaults occurring in corrosive environments. Additionally, SEM pictures of the worn surfaces indicated the emergence of microcracks, which may be associated to the conditions of cyclic loading. Moreover, the tensile-fractography examination for the developed 1.5%WGP/7.5%Si3N4/AZ91D composites has exhibited the brittle fracture failure, including cracks and debonding phenomena. In addition, the EDS spectra-analysis have revealed an apparent existence of the observed Mg-peak, Si-peak, Al-peak, Ca-peak, and O-peak for the 1.5%WGP/7.5%Si3N4/AZ91D composites. Furthermore, the utilisation of X-ray diffraction analysis effectively determined the existence of hard phases inside the AZ91D-matrix, which significantly contributed to the reported enhancement in wear resistance. The development of harder-phases has included, α-Mg, Al12Mg17, SiO2, Si3N4, MgO, and CaO phases within the composite has been accountable for the enhancement of the tribomechanical, and wear-resistance characteristics of the AZ91D/WGP/Si3N4 composites. The Si3N4 has been discovered to have a substantial impact on enhancing mechanical performance and raising the resistance to wear.
Collapse
Affiliation(s)
- Shubham Sharma
- Centre for Research Impact and Outcome, Chitkara University Institute of Engineering and Technology, Chitkara University, Rajpura, Punjab, 140401, India.
- School of Mechanical and Automotive Engineering, Qingdao University of Technology, Qingdao, 266520, China.
- Department of Mechanical Engineering, Lebanese American University, Kraytem, Beirut, 1102-2801, Lebanon.
- Faculty of Mechanical Engineering, Opole University of Technology, 45-758, Opole, Poland.
| | - Shashi Prakash Dwivedi
- Department of Mechanical Engineering, Lloyd Institute of Engineering & Technology, Knowledge Park II, Greater Noida, Uttar Pradesh, 201306, India.
| | - Abhinav Kumar
- Department of Nuclear and Renewable Energy, Ural Federal University Named After the First President of Russia, Boris Yeltsin, 19 Mira Street, Ekaterinburg, Russia, 620002
| | - Fuad A Awwad
- Department of Quantitative Analysis, College of Business Administration, King Saud University, P.O. Box 71115, 11587, Riyadh, Saudi Arabia.
| | - M Ijaz Khan
- Department of Mechanical Engineering, Lebanese American University, Kraytem, Beirut, 1102-2801, Lebanon
- Department of Mechanics and Engineering Science, Peking University, Beijing, 100871, China
| | - Emad A A Ismail
- Department of Quantitative Analysis, College of Business Administration, King Saud University, P.O. Box 71115, 11587, Riyadh, Saudi Arabia
| |
Collapse
|
3
|
Zhao C, Ma C, Yang J, Li M, Zhao Q, Ma H, Jia X. Numerical Simulation Study of Multi-Field Coupling for Laser Cladding of Shaft Parts. MICROMACHINES 2023; 14:mi14020493. [PMID: 36838193 PMCID: PMC9965465 DOI: 10.3390/mi14020493] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 01/18/2023] [Revised: 02/16/2023] [Accepted: 02/17/2023] [Indexed: 06/01/2023]
Abstract
Since shaft parts operate under harsh environments for a long time, many critical parts suffer from corrosion, wear and other problems, leading to part failure and inability to continue in service. It is imperative to repair failed parts and increase their service life. An orthogonal experimental scheme is designed to numerically simulate the process of laser cladding of Inconel 718 alloy powder on 4140 alloy structural steel based on the ANSYS simulation platform, derive the relationship equation of cladding layer thickness according to the heat balance principle, establish a finite element model, couple three modules of temperature field, stress field and fluid field, and analyze different modules to realize the monitoring of different processes of laser cladding. The optimal cladding parameters were laser power 1000 W, scanning speed 15 rad/s, spot radius 1.5 mm, thermal stress maximum value of 696 Mpa, residual stress minimum value of 281 Mpa, and the degree of influence of three factors on thermal stress maximum value: laser power > spot radius > scanning speed. The pool in the melting process appears to melt the "sharp corner" phenomenon, the internal shows a double vortex effect, with a maximum flow rate of 0.02 m/s. The solidification process shows a different shape at each stage due to the different driving forces. In this paper, multi-field-coupled numerical simulations of the laser cladding process were performed to obtain optimal cladding parameters with low residual stresses in the clad layer. The melt pool grows and expands gradually during melting, but the laser loading time is limited, and the size and shape of the melt pool are eventually fixed, and there is a vortex flowing from the center to both sides of the cross-section inside the melt pool, forming a double vortex effect. The solidification is divided into four stages to complete the transformation of the liquid phase of the melt pool to the solid phase, and the cladding layer is formed. The multi-field-coupled numerical simulation technique is used to analyze the temperature, stress and fluid fields to provide a theoretical basis for the residual stress and surface quality of the clad layer for subsequent laser cladding experiments.
Collapse
|