Effects of Coefficient of Thermal Expansion and Moisture Absorption on the Dimensional Accuracy of Carbon-Reinforced 3D Printed Parts

An Insight into the Characteristics of 3D Printed Polymer Materials for Orthoses Applications: Experimental Study

Knee orthoses assist patients with impaired gait through the amendment of knee abnormalities, restoration of mobility, alleviation of pain, shielding, and immobilization. The inevitable issues with laborious traditional plaster molding procedures for orthoses can be resolved with 3D printing. However, a number of challenges have limited the adoption of 3D printing, the most significant of which is the proper material selection for orthoses. This is so because the material used to make an orthosis affects its strength, adaptability, longevity, weight, moisture response, etc. This study intends to examine the mechanical, physical, and dimensional characteristics of three-dimensional (3D) printing materials (PLA, ABS, PETG, TPU, and PP). The aim of this investigation is to gain knowledge about these materials' potential for usage as knee orthosis materials. Tensile testing, Olympus microscope imaging, water absorption studies, and coordinate measuring machine-based dimension analysis are used to characterize the various 3D printing materials. Based on the investigation, PLA outperforms all other materials in terms of yield strength (25.98 MPa), tensile strength (30.89 MPa), and shrinkage (0.46%). PP is the least water absorbent (0.15%) and most flexible (407.99%); however, it is the most difficult to fabricate using 3D printing. When producing knee orthoses with 3D printing, PLA can be used for the orthosis frame and other structural elements, PLA or ABS for moving parts like hinges, PP for padding, and TPU or PP for the straps. This study provides useful information for scientists and medical professionals who are intrigued about various polymer materials for 3D printing and their effective utilization to fabricate knee orthoses.

Analyzing Surface Roughness Variations in Material Extrusion Additive Manufacturing of Nylon Carbon Fiber Composites

In recent years, fused deposition modeling (FDM) based on material extrusion additive manufacturing technology has become widely accepted as a cost-effective method for fabricating engineering components with net-shapes. However, the limited exploration of the influence of FDM process parameters on surface roughness parameters, i.e., Ra (average surface roughness), Rq (root mean square surface roughness), and Rz (maximum height of the profile) across different sides (bottom, top, and walls) poses a challenge for the fabrication of functional parts. This research aims to bridge the knowledge gap by analyzing surface roughness under various process parameters and optimizing it for nylon carbon fiber printed parts. A definitive screening design (DSD) was employed for experimental runs. The Pareto chart highlighted the significant effects of layer height, part orientation, and infill density on all surface roughness parameters and respective sides. The surface morphology was analyzed through optical microscopy. Multi-response optimization was performed using an integrated approach of composited desirability function and entropy. The findings of the present study hold significant industrial applications, enhancing the quality and performance of 3D printed parts. From intricate prototypes to durable automotive components, the optimized surfaces contribute to production of functional and visually appealing products across various sectors.

Environmental Stability of Additively Manufactured Thermoplastic Polyamide Composites

As the adoption of additive manufacturing technologies for end-use parts continues to progress, the evaluation of environmental durability is essential for the qualification of manufactured articles in industries such as automotive, aerospace, and electrical. This study explores the effects of UV and water-spray exposure on the mechanical properties of an additively manufactured polyamide 6 blend reinforced with short carbon fiber and continuous carbon fiber. Fused-filament-fabrication-printed test samples were exposed to a Xenon-arc UV source following ASTM G155 Cycle 1 conditions for a duration of 1000 h. Tensile, flexural, and Izod impact tests were performed on exposed and unexposed test samples. While Exposed tensile and flexural samples maintained their strength (84-100% and 88-100%, of Control samples, respectively), Izod impact strength increased (104-201% of Controls). This study also examines the influence of coatings and finds that samples coated with Krylon® Fusion All-In-One® and JetFlex® Polyurethane Primer maintain similar mechanical properties and exhibit a better visual appearance as compared to uncoated, exposed samples.

Flexural Fatigue in a Polymer Matrix Composite Material Reinforced with Continuous Kevlar Fibers Fabricated by Additive Manufacturing

Fatigue bending tests, under controlled displacement, were performed on a polymer matrix composite material reinforced with continuous Kevlar fibers. The samples were fabricated using the Fused Filament Fabrication (FFF) technique in a Markforged Two^® 3D printer. The static characterization delivered a flexural modulus of elasticity of 4.73 GPa and flexural strength of 110 MPa. The applied loading corresponded to 92.3, 88.5, 86.2, and 84.7% of the static flexural displacement, giving 15, 248, 460, and 711 cycles for failure. Additionally, two numerical models were created: one using orthotropic properties for static loading conditions; and a second one using isotropic in-bulk properties for fatigue modeling. The second model was able to reproduce the experimental fatigue results. Finally, morphological analysis of the fractured surface revealed fiber breakage, fiber tearing, fiber buckling, matrix cracking, and matrix porosity.

Investigation into Thermomechanical Response of Polymer Composite Materials Produced through Additive Manufacturing Technologies

This paper presents the static mechanical behavior and the dynamic thermomechanical properties of four market-available reinforced and non-reinforced thermoplastics and photopolymer materials used as precursors in different additive manufacturing technologies. This article proposes a characterization approach to further address development of aeronautic secondary structures via 3D-printed composite materials replacing conventional manufactured carbon fiber reinforced polymer (CFRP) composites. Different 3D printing materials, technologies, printing directions, and parameters were investigated. Experimental results showed that carbon-reinforced ONYX_R material exhibits a transition point at 114 °C, a 600 MPa tensile strength, and an average tensile strain of 2.5%, comparable with conventional CFRP composites manufactured via autoclave, making it a suitable candidate for replacing CFRP composites, in the aim of taking advantage of 3D printing technologies. ONYX material exhibits higher stiffness than Acrylonitrile-Butadiene-Styrene Copolymer (ABS), or conventional Nylon 6/6 polyamide, the flexural modulus being 2.5 GPa; nevertheless, the 27 °C determined transition temperature limits its stability at higher temperature. Daylight High Tensile (further called HTS) resin exhibits a tensile strength and strain increase when shifting the printing direction from transversal to longitudinal, while no effect was observed in HighTemp DL400 resin (further called HTP).