Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&Roll" and Non-contact Profilometry

Developing an optimised method for accurate wear testing of dental materials using the 'Rub&Roll' device

Dental materials are challenged by wear processes in the oral environment and should be evaluated in laboratory tests prior to clinical use. Many laboratory wear-testing devices are high-cost investments and not available for cross-centre comparisons. The 'Rub&Roll' wear machine enables controlled application of force, chemical and mechanical loading, but the initial design was not able to test against rigid antagonist materials. The current study aimed to probe the sensitivity of a new 'Rub&Roll' set-up by evaluating the effect of force and test solution parameters (deionized water; water + abrasive medium; acid + abrasive medium) on the wear behaviour of direct and indirect dental resin-based composites (RBCs) compared with human molars against 3D-printed rod antagonists. Molars exhibited greater height loss than RBCs in all test groups, with the largest differences recorded with acidic solutions. Direct RBCs showed significantly greater wear than indirect RBCs in the groups containing abrasive media. The acidic + abrasive medium did not result in increased wear of RBC materials. The developed method using the 'Rub&Roll' wear machine in the current investigation has provided a sensitive wear test method to allow initial screening of resin-based composite materials compared with extracted human molars under the influence of different mechanical and erosive challenges.

In vitro effect of occlusal loading on cervical wall lesion development in a Class II composite restoration

The aim of this study was to determine the effect of simulated occlusal loading on wall lesion development in cervical gaps of class II composite restorations in vitro. Sixty-four extracted human molars received standardized (4.0 × 4.2 × 3.0 mm) box preparations. The teeth were randomly assigned to one of two restoration groups: restoration with a normal or a low E-modulus composite material (CLEARFIL AP-X: E-modulus 16.8 GPa or CLEARFIL MAJESTY ES Flow: E-modulus 6.6 GPa). A metal matrix was placed at the bottom of the box for each restoration, creating a cervical gap of about 100 μm wide. Samples were exposed to simulated caries lesion development in a lactic acid solution (pH 4.8) for 8 weeks in a Rub&Roll device. Half of the samples were subjected to 90 N cyclic loading. After demineralization, the teeth were sectioned. Wall lesion development was measured using microradiography (transversal wavelength-independent microradiography) in two different locations (location 1: 1,000 μm and location 2: 1,600 μm from the gap entrance) and recorded in lesion depth (LD) (μm) and mineral loss (μm × vol%). Linear regression modeling was used to estimate the effect of loading and material on wall lesion development. Mean wall LD in location 1 across all groups was 150.83 μm with a standard deviation (SD) of 61.83 μm. In location 2, mean overall wall LD was 102.98 μm with an SD of 64.92 μm. Linear regression showed no significant effect of either loading or material on wall lesion development. Occlusal loading had no significant effect on secondary caries lesion development in composite class II restoration in this in vitro study.

The effect of occlusal loading on cervical gap deformation: A 3D finite element analysis

OBJECTIVES

Secondary caries can be accelerated by hydrodynamic flow in a gap between the tooth and restorative material. This study investigated whether occlusal loading can lead to increased hydrodynamic flow by deforming a gap between tooth and restorative material.

METHODS

3D finite element analysis was employed to model a molar containing a restoration with an interfacial gap. The model was loaded using direct cusp-to-restoration contact and using a rubber tube model simulating a food bolus. The object exerting pressure was moved across the molar from buccal to lingual side. The applied forces were 50, 100, 200 and 400N. The elastic modulus of the restoration material was varied between 5, 10, 15.9 and 25GPa to resemble different kinds of composite. The primary outcome parameter was the volume of the gap under occlusal pressure.

RESULTS

Occlusal loading resulted in deformation of the gap area. Maximum deformation was seen when loading was applied in the middle of the restoration. Higher forces and lower restoration stiffness led to more deformation of the gap. Maximum deformation with a force of 100N and composite modulus of 15.9GPa was -0.0083mm³ (1.12%).

SIGNIFICANCE

Deformation of the gap between tooth and restorative material could lead to increased hydrodynamic flow and faster secondary caries lesion formation. The measured deformation is small. Further research needs to show whether gap compression through occlusal loading affects secondary caries formation to a clinically relevant degree.

Cup-Shaped Tooth Wear Defects: More than Erosive Challenges?

BACKGROUND/AIM

The underlying mechanism of the development of cups and grooves on occlusal tooth surfaces is still unclear. The aim of this study was to evaluate factors contributing to in vitro cup formation, in order to elucidate the clinical process.

METHODS

A total of 48 extracted human molar teeth were exposed to acidic aqueous solutions at pH of 4.8 and 5.5 in constant motion, in combination with different loading conditions: no load (0N group, control), 30 N (30N group) or 50 N (50N group) (n = 8 per group). Before and after 3 months of exposure (1,422,000 loading cycles), the samples were scanned using a non-contact profilometer. Pre- and post-exposure scans were subtracted and height loss and volume tissue loss were calculated. Representative samples with wear and cupping lesions were imaged using scanning electron microscopy, light microscopy and micro-computed tomography.

RESULTS

Average height and volume tissue loss at pH 5.5 was 54 µm and 3.4 mm3 (0N), 52 µm and 3.4 mm3 (30N) and 58 µm and 3.7 mm3 (50N), respectively, with no statistically significant differences. Average height and volume loss at pH 4.8 were 135 µm and 8.7 mm3 (0N), 172 µm and 12.6 mm3 (30N) and 266 µm and 17.8 mm3 (50N), respectively, with a statistically significant difference between 0N and 50N (p < 0.002). Cup-shaped lesions had formed only at pH of 4.8, in the 30N and 50N groups.

CONCLUSION

The study showed that a cup can arise fully in enamel and that mechanical loading in addition to erosive challenges are required.