Evaluation of pH and dimensional stability of mineral trioxide aggregate and biodentine with and without triple antibiotic medicament: An in vitro study

Effect of different root canal irrigants on surface roughness and microhardness of Biodentine combined with triple antibiotic paste: An in vitro study

Background

Biodentine is widely used for endodontic applications; recently, it has been incorporated with triple antibiotic paste (TAP). The effect of endodontic irrigants on the physical characteristics of this new combination needs to be studied.

Aims

The aim of the study was to evaluate the surface roughness and microhardness of Biodentine incorporated with TAP subjected to various endodontic irrigants.

Materials and Methods

Hundred cylindrical discs (6 mm × 3 mm) were prepared by mixing the Biodentine with TAP (3:1). The specimens were subjected to different irrigating solutions for 5 min in 5 groups (n = 20): Group 1: distilled water (control), Group 2: 2.5% sodium hypochlorite, Group 3: 17% ethylenediaminetetraacetic acid, Group 4: 2% chlorhexidine (CHX), and Group 5: 2% chitosan nanoparticles (CSNs). Half of the specimens in each group were subjected to surface roughness (n = 10) and another half to microhardness (n = 10). Surface roughness was measured using a surface roughness tester, and digital Vickers microhardness testing was performed on each specimen.

Statistical Analysis

One-way ANOVA and post hoc Tukey's tests (P ≤ 0.05) were used.

Results

The highest microhardness was found with 2% CSN, whereas 2% CSN and 2% CHX had a minimal effect on the surface roughness of Biodentine incorporated with TAP (P ≤ 0.05).

Conclusion

The root canal irrigant 2% CSN exhibited the highest microhardness and least surface roughness of modified Biodentine with TAP.

Specimen Shape and Elution Time Affect the Mineralization and Differentiation Potential of Dental Pulp Stem Cells to Biodentine

The liquid extract method is commonly used to evaluate the cytotoxicity and bioactivity of materials. Although ISO has recommended guidelines for test methods, variations in elution period, and shape of samples can influence the biological outcomes. The aim of this study was to investigate the influence of material form and elution period of Biodentine on dental pulp stem cells (DPSCs)' proliferation and mineralization. Biodentine (0.2 g) discs or powder were immersed in culture media (10 mL) for 1, 3 or 7 days (D1, D3 and D7). The eluents were filtered and used to treat DPSC. The calcium release profile and pH were determined. Cell proliferation was evaluated by MTS for 3 days, and mineralization and differentiation were assessed by alizarin red S staining (Ca2+/ng of DNA) and qRT-PCR (MEPE, DSPP, DMP-1, RUNX2, COL-I and OCN) for 14 days. Statistical analysis was performed with a one or two-way ANOVA and post hoc Tukey's test (pH, calcium release and proliferation) or Mann-Whitney test (α = 0.05). pH and calcium ion release of powdered eluents were significantly higher than disc eluents. Powdered eluent promoted extensive cell death, while the disc form was cytocompatible. All disc eluents significantly increased the gene expression and mineralization after 14 days compared to the untreated control. D7 induced less mineralization and differentiation compared to D1 and D3. Thus, the materials' form and elution time are critical aspects to be considered when evaluating the bioactivity of materials, since this binomial can affect positively and negatively the biological outcomes.