A novel non-destructive technique for qualitative and quantitative measurement of dental erosion in its entirety by porosity and bulk tissue-loss

OBJECTIVE

To explore the potential of combining non-contact profilometry (NCP) and confocal laser scanning microscopy (CLSM) data to measure the entire erosive process non-destructively and to validate findings using inductively coupled plasma-atomic emission spectroscopy (ICP-AES), scanning electron microscopy (SEM) and surface microhardness (SMH) using the same samples throughout.

METHODS

Polished bovine enamel samples (n = 35) were divided into groups (7/group) with similar SMH values. Samples underwent individual erosive challenges (1 % citric acid, pH3.8) for 1, 5, 10, 15 or 30 min under stirring and aliquot extracts were analysed for Ca and P by ICP-AES. SMH was used to measure erosive softening. Profilometry was used to assess bulk volume loss (BVL). Images were captured by SEM. Samples were stained with rhodamine-B (0.1 mM, 24 h) and images captured by CLSM. Image processing was used to determine changes in fluorescent volume for the first 10 μm (ΔFV₁₀) for each enamel sample which were combined with BVL to calculate total lesion volume (TLV). ANOVA, linear regression and Pearson correlation analysis were used where applicable.

RESULTS

Surface softening, [Ca], [P], BVL and ΔFV_10μm increased with acid erosion duration which were significant by 10 min (P < .01). The Ca:P ratio increased to 1.57 then decreased after 5 min erosion suggesting a sub/surface phase change, which was observed by SEM and CLSM showing significant changes to the enamel surface and subsurface morphology with time. Combination of BVL and ΔFV₁₀ as TLV strengthened the significant correlations with [Ca], [P], and SMH (P < .01).

CONCLUSION

This novel combination of CLSM and NCP allows for concurrent non-destructive quantification of the entire erosive process by mineral loss, and qualitatively characterise microstructural changes during dental erosion.