Synergistic toughening of epoxy resin by CTBN and CM‐β‐CD

Multi-functional konjac glucomannan/chitosan bilayer films reinforced with oregano essential oil loaded β-cyclodextrin and anthocyanins for cheese preservation

In this work, a multifunctional bilayer film was prepared by solvent casting method. Elderberry anthocyanins (EA) were incorporated into konjac glucomannan (KGM) film as the inner indicator layer (KEA). β-cyclodextrin (β-CD) loaded with oregano essential oil (OEO) inclusion complexes (β-CD@OEO) was prepared and incorporated into chitosan (CS) film as the outer hydrophobic and antibacterial layer (CS-β-CD@OEO). The impacts of β-CD@OEO on the morphological, mechanical, thermal, water vapor permeability and water resistance properties, pH sensitivity, antioxidant, and antibacterial activities of bilayer films were thoroughly evaluated. The incorporation of β-CD@OEO into bilayer films can significantly improve the mechanical properties (tensile strength (TS): 65.71 MPa and elongation at break (EB): 16.81 %), thermal stability, and water resistance (Water contact angle (WCA): 88.15°, water vapor permeability (WVP): 3.53 g mm/m² day kPa). In addition, the KEA/CS-β-CD@OEO bilayer films showed color variations in acid-base environments, which could be used as pH-responsive indicators. The KEA/CS-β-CD@OEO bilayer films also presented controlled release of OEO, good antioxidant, and antimicrobial activity, which exhibited good potential for the preservation of cheese. To sum up, KEA/CS-β-CD@OEO bilayer films have potential applications in the field of food packaging industry.

Enhancement of Mechanical Properties and Bonding Properties of Flake-Zinc-Powder-Modified Epoxy Resin Composites

As a typical brittle material, epoxy resin cannot meet its application requirements in specific fields by only considering a single toughening method. In this paper, the effects of carboxyl-terminated polybutylene adipate (CTPBA) and zinc powder on the mechanical properties, adhesion properties, thermodynamic properties and medium resistance of epoxy resin were studied. A silane coupling agent (KH-550) was used to modify zinc powder. It was found that KH-550 could significantly improve the mechanical properties and bonding properties of epoxy resin, and the modification effect of flake zinc powder (f-Zn) was significantly better than that of spherical zinc powder (s-Zn). When the addition amount of f-Zn was 5 phr, the tensile shear strength and peel strength of the composites reached a maximum value of 13.16 MPa and 0.124 kN/m, respectively, which were 15.95% and 55% higher than those without filler. The tensile strength and impact strength reached a maximum value of 43.09 MPa and 7.09 kJ/m², respectively, which were 40.54% and 91.11% higher than those without filler. This study provides scientific support for the preparation of f-Zn-modified epoxy resin.

Preparation and research of epoxy modified by carboxyl-terminated polybutylene adipate at room temperature

In this study, carboxyl-terminated polybutylene adipate (CTPBA) was used to modify epoxy resin, and the modified epoxy resin was cured by a room temperature rapid curing agent (T-31). The effects of CTPBA modification on bonding properties and mechanical properties of epoxy resin adhesive at room temperature were carefully studied. Epoxy-terminated prepolymer was synthesized by pre-polymerization and its structure was characterized. Compared with the addition method of direct blending, the bonding properties and mechanical properties of pre-polymerized epoxy resin adhesive were significantly better. Compared with unmodified epoxy resin, CTPBA modification significantly improved the bonding strength. Furthermore, with the increase of CTPBA content, the shear strength of the material increased first and then decreased, and reached the maximum when the addition amount was 40 phr. This shows that the tensile strength of the material decreased with the increase of CTPBA content, and the elongation at break increased with the increase of CTPBA content. Dynamic mechanical analyzer (DMA) test results showed that the addition of CTPBA reduced the glass transition temperature, but broadened the damping temperature range. TG analysis showed that the thermal stability of the modified epoxy resin was good, and compared with pure epoxy resin, the initial temperature of thermal weight loss and the maximum thermal decomposition rate decreased, but the overall thermal stability was not significantly different. In summary, CTPBA modification of epoxy resin is expected to improve the comprehensive mechanical properties at room temperature.

In this study, carboxyl-terminated poly(butylene adipate) (CTPBA) was synthesized, which was terminated with epoxy and used as a toughening agent to modify the epoxy resin, and the modified epoxy resin was cured at room temperature.