Ambient-Pressure Stabilization of β-GdB3 O6 by Doping with Bi3+ and Color-Tunable Emissions by Co-Doping with Tb3+ and Eu3+ : The First Photoluminescence Study of a High-Pressure Polymorph

Two new rare-earth oxyborates Ba4BiTbO(BO3)4 and Ba1.54Sr2.46BiTbO(BO3)4 and luminescence properties of the Ba4BiTb1-xEuxO(BO3)4 phosphors

Single crystals of two new terbium oxyborates Ba4BiTbO(BO3)4 and Ba1.54Sr2.46BiTbO(BO3)4 were obtained by the high-temperature solution method. They crystallize in the hexagonal P63/mmc group (Z = 2) with lattice parameters of a = 5.41865(9) Å, c = 26.3535(5) Å, V = 670.12(3) Å3 and a = 5.36534(19) Å, c = 26.0661(10) Å, V = 649.83(5) Å3, respectively. Their crystal structures feature two kinds of layers: [Tb(BO3)2]n3n- formed by corner-sharing TbO6 octahedra and BO3 triangles, as well as [Bi(BO3)2O]n5n- consisting of Bi2O13 dimers and BO3 groups, with alkali-earth cations sitting inside and between the layers. In addition, solid solutions of Ba4BiTb1-xEuxO(BO3)4 (0 ≤ x ≤ 0.2) were prepared via the solid-state reaction method. The obtained products were characterized by powder XRD, SEM, IR/Raman, XPS, DRS, and luminescence spectroscopy. It was found that as the Eu3+ doped content varies from x = 0 to 0.2, the emission color of the Ba4BiTb1-xEuxO(BO3)4 phosphors can be adjusted from cyan to near-white and then to orange-red or from green to orange and then to red under the excitation of 349 and 377 nm, respectively. Furthermore, the emission intensities and chromaticity coordinates were found to be sensitive to the temperature for the phosphor Ba4BiTb0.999Eu0.001O(BO3)4 upon 377 nm excitation. The above results demonstrate that Ba4BiTb1-xEuxO(BO3)4 phosphors have potential as multifunctional materials for solid-state lighting and temperature sensing applications.

Single-Composition White Light Emission from Dy3+ Doped Sr₂CaWO₆

A series of Dy³⁺ ion doped Sr₂CaWO₆ phosphors with double perovskite structure were synthesized by traditional high temperature solid-state method. It was found that there is significant energy transfer between Dy³⁺ and the host lattice, and the intensities of emission peaks at 449 nm (blue), 499 nm (cyan), 599 nm (orange), 670 nm (red), and 766 nm (infra-red) can be changed by adjusting the concentration of dopant amount of Dy³⁺ ion in Sr₂CaWO₆. The correlated color temperature of Dy³⁺ ion doped Sr₂CaWO₆ phosphors can be tuned by adjusting the concentration of Dy³⁺ ion. Upon optimal doping at 1.00 mol% Dy³⁺, white light with chromaticity coordinate (0.34, 0.33) was emitted under excitation at 310 nm. Thus, single composition white emission is realized in Dy³⁺ doped Sr₂CaWO₆.