Fabrication of Fe3 O4 /ZIF-67 composite for removal of direct blue 80 from water

Kiwi peel waste as a recyclable adsorbent to remove textile dyes from water: Direct Blue 78 removal and recovery

According to circular bioeconomy principles, the use of kiwi peels to remove Direct Blue 78 (DB) from water is investigated during this work, proposing food waste as a recyclable adsorbent substrate. Direct Blue 78 (DB) was adopted as a model pollutant, employing its visible spectrum to monitor its adsorption. The adsorption process was thus fully characterized, investigating the roles of ionic strength, pH values, adsorbent/pollutant amounts, and temperature. The thermodynamics, kinetics, and adsorption isotherms were also studied. To extend the kiwi peels' lifetime, quite complete desorption was obtained by adopting hot water as a safe and eco-friendly strategy. Despite the relatively low kiwi peels' maximum adsorption capacity (6 mg g-1) for DB when adsorbed in the presence of NaCl, 10 cycles of adsorption/desorption were attempted, proposing the recycling of both the dye and kiwi peels as dictated by circular economy principles. Dyeing experiments were also performed, evidencing the dye's ability to color cotton fabrics after its recycling. Finally, the removal of other textile dyes, Direct Red 83 : 1 and Direct Yellow 86, was demonstrated in a mixture with DB. A preliminary investigation was performed to find the best working conditions for inducing the solid-state dye photodegradation, proposing a possible alternative for the adsorbent regeneration.

Rational synthesis and characterization of highly water stable MOF@GO composite for efficient removal of mercury (Hg2+) from water

The present study is aimed at adsorptive removal of Mercury (Hg²⁺) using highly functionalized nanomaterials based on Graphene Oxide Zeolitic Imidazolate Framework composite (ZIF-67@GO). Solvothermal methodology was used to synthesize ZIF-67@GO composite. Synthesized compounds were confirmed by FTIR, SEM, PXRD and EDX analysis. The as-prepared ZIF-67@GO was tested as efficient adsorbent for effective removal of Mercury (Hg²⁺) from aquatic environment. The atomic adsorption spectrophotometer was used to monitor the process of adsorption of Hg⁺² on ZIF-67@GO. From the adsorption data, the maximum removal efficiency achieved was 91.1% using 10 mg amount of composite for 50 mL using 20 ppm Mercury (Hg²⁺) solution. Different parameters like pH, contact time, concentration, adsorption kinetics and isotherm were also examined to explore adsorption process. Adsorption data fitted well for Freundlich Model having R² value of 0.9925 than Langmuir Isotherm with R² value of 0.9238. Kinetics were rapid and excellently described via 2nd order model with R² = 0.99946 than 1st order model with R² value of 0.8836. Freundlich and pseudo 2nd order models validated that multilayer chemisorption occurs during adsorption process due to the presence of highly functionalized sites on ZIF-67@GO composite. The synthesized composite material has shown excellent reusability. Thus, water stable ZIF-67@GO composites can efficiently be used for Mercury (Hg²⁺) confiscation from water.

Synthesis of ferroferric oxide@silicon dioxide/cobalt-based zeolitic imidazole frameworks for the removal of doxorubicin hydrochloride from wastewater

Due to its low-cost, eco-friendliness and easy mode of separation biosynthesized magnetic ferroferric oxide (Fe₃O₄) can be successfully used for the removal of organic contaminants from wastewater. However, there are some challenges that to date have limited this compound's practical removal efficiency. Thus, in this study, a cobalt-based zeolitic imidazole frameworks (ZIF-67) coated biosynthesized ferroferric oxide@silicon dioxide (Fe₃O₄@SiO₂) magnetic composite (Fe₃O₄@SiO₂/ZIF-67) was prepared to address these issues and subsequently used to remove doxorubicin hydrochloride (DOX). Characterization results showed that the fabricated composite exhibited significant magnetic properties (16.1 emu·g^-1) with a size ranging between 50 and 250 nm. The amount of DOX adsorbed by the composite (90.7 mg·g^-1) was much higher than either of the component parts, which were only 35.7 and 82.5 mg·g^-1 for Fe₃O₄@SiO₂ and ZIF-67 respectively. This indicated enhanced DOX adsorption by Fe₃O₄@SiO₂/ZIF-67. The DOX adsorption best fit a pseudo-second order kinetic and Langmuir adsorption model. These studies suggested that the DOX adsorption mechanism involved a combination of electrostatic interactions, π-π stacking, hydrogen bonding and pore filling. Regeneration and application studies, exposing Fe₃O₄@SiO₂/ZIF-67 to real water samples, practically demonstrated that Fe₃O₄@SiO₂/ZIF-67 with propensity for magnetic separation and recycle is a promising nanomaterial for DOX removal.

Water stable graphene oxide metal-organic frameworks composite (ZIF-67@GO) for efficient removal of malachite green from water

Malachite green (MG) is extensively applied in aquaculture worldwide as a therapeutic agent. MG and its primary metabolite leucomalachite green (LMG) are commonly detected in aquaculture products. MG can cause serious health concerns (in vivo carcinogenic/genotoxic). The extensive water solubility of MG leads to water pollution and hence it is mandatory to remove MG from water. The current study explores adsorptive removal of MG from water using highly water stable Zeolitic Imidazolate framework/graphene oxide composites (ZIF-67@GO). Adsorption performance of newly synthesized composites is justified for MG removal with excellent results of pseudo second order (R² = 0.99955) which is well-fitted in this case. ZIF-67@GO data of adsorption isotherm for MG is observed using Freundlich Model (R² = 0.99999) and with adsorption capacity value observed (134.79 mg/g) with removal efficiency of 99.18%, indicates π-staking and electrostatic association between ZIF-67@GO and MG molecules. Synthesized material has retained reusability while removal efficiency reduced only by 6% after many cycles. Furthermore, factors effecting absorption like contact time, pH, adsorbent dose and quantity and temperature are also determined.

Halloysite nanotubes (HNTs)@ZIF-67 composites—a new type of heterogeneous catalyst for the Knoevenagel condensation reaction

Halloysite nanotubes (HNTs) are encapsulated in 50 nm thick shells of ZIF-67, producing novel nano-sized composites HNTs@ZIF-67.