A new microporous material: aluminated sepiolite

Structure and morphology of red pigments based on sepiolite

Sepiolite is an important raw fibrous material. A method to prepare red pigments based on sepiolite through the thermal treatment of sepiolite with sulfur and sodium sulfide hydrate is reported. Sepiolite was heated until 800 °C in order to remove zeolitic water, the first coordinated water, the second coordinated water, and structural hydroxyls. Several [S/Na2S]molar ratios in the range 0.5-7 were employed. The properties of these pigments were studied by different analytical techniques, such as colorimetric analysis, thermal analysis, Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction and scanning electron microscopy. The samples with [S/Na2S] = 0.5 and 1, corresponding to high contents of sodium sulfide in the synthesis procedure, exhibit high values of the colorimetric parameter CIE a* and a maximum reflectance in the visible zone belonging to red, based on the red colour of the samples. Under the reducing conditions of the synthesis, sulfur forms polysulfides of the general formula [Sx]2-. The sodium sulfide reacts with the excess S to form polysulfides as well. From the polysulfides, the radical anions of the general formula [Sx/2]˙- originate and they are identified as the chromophore groups responsible for the color in the sulfur-based pigment analogues of ultramarines. The red colour of the samples could be mainly attributed to the presence of S4 and S4˙- identified by FTIR.

Dye-sensitized Photocatalyst of Sepiolite for Organic Dye Degradation

The photocatalytic activity of sepiolite was examined for degradation of several dye compounds under visible light irradiation. Higher adsorption capacities and greater photocatalytic performance of cationic dyes (rhodamine B and methylene blue) were observed on sepiolite, in comparison with anionic dyes (orange II and trypan blue). Superiority in the photocatalytic activity of cationic dyes is attributed to the strong electrostatic attraction and photosensitization properties of cationic dye molecules. Sepiolite has degraded 45.3% rhodamine B within 120 min, which is the greatest photocatalytic degradation efficiency when compared with other dyes. Subsequently, the reusability of spent sepiolite after adsorption of rhodamine B was evaluated by the degradation of trypan blue under the visible light irradiation. The photocatalytic degradation performance of trypan blue by spent sepiolite after adsorption of rhodamine B increased about twice as much as with pristine sepiolite, indicating that the dye-sensitized photocatalytic process could enhance the photocatalytic degradation ability of sepiolite. Through radical scavenger tests, it was found that a superoxide radical is mainly responsible for rhodamine B degradation. The possible mechanism of rhodamine B degradation under visible light irradiation was proposed. The sepiolite could be a potential catalyst for the degradation of organic pollutants in wastewater under solar light.

Chlorinated polyethylene (CPE)/ethylene methacrylate copolymer (EMA)/sepiolite nanocomposite via a facile one-step covalent modification technique

Facile one-step organo-modification of sepiolite improves polymer–filler interfacial adhesion, thereby advances mechanical properties and thermal stability of the CPE/EMA/sepiolite nanocomposite.