Activity boosting of gold nanoparticles supported on V2O5/TiO2 nanostructures for CO oxidation at low temperature

Mixed-metal nanoparticles: phase transitions and diffusion in Au-VO clusters

Nanoparticles with diameters in the range of a few nanometers, consisting of gold and vanadium oxide, are synthesized by sequential doping of cold helium droplets in a molecular beam apparatus and deposited on solid carbon substrates. After surface deposition, the samples are removed and various measurement techniques are applied to characterize the created particles: scanning transmission electron microscopy (STEM) at atomic resolution, temperature dependent STEM and TEM up to 650 °C, energy-dispersive X-ray spectroscopy (EDXS) and electron energy loss spectroscopy (EELS). In previous experiments we have shown that pure V₂O₅ nanoparticles can be generated by sublimation from the bulk and deposited without affecting their original stoichiometry. Interestingly, our follow-up attempts to create Au@V₂O₅ core@shell particles do not yield the expected encapsulated structure. Instead, Janus particles of Au and V₂O₅ with diameters between 10 and 20 nm are identified after deposition. At the interface of the Au and the V₂O₅ parts we observe an epitaxial-like growth of the vanadium oxide next to the Au structure. To test the temperature stability of these Janus-type particles, the samples are heated in situ during the STEM measurements from room temperature up to 650 °C, where a reduction from V₂O₅ to V₂O₃ is followed by a restructuring of the gold atoms to form a Wulff-shaped cluster layer. The temperature dependent dynamic interplay between gold and vanadium oxide in structures of only a few nanometer size is the central topic of this contribution to the Faraday Discussion.

Catalytic behavior of gold nanoparticles supported on a TiO2-Al2O3 mixed oxide for CO oxidation at low temperature

The present work highlights the versatility of a TiO₂-Al₂O₃ mixed oxide bearing highly dispersed gold nanoparticles that was applied in the CO oxidation reaction at room temperature. The TiO₂, Al₂O₃, and TiO₂-Al₂O₃ supports were synthesized by the sol-gel method, while gold nanoparticles were added by the deposition-precipitation with urea method using a theoretical Au loading of 2 wt.%. A promotional effect of the TiO₂-Al₂O₃ support on the activity of gold catalysts with respect to TiO₂ and Al₂O₃ was observed; Au/TiO₂-Al₂O₃ showed outstanding CO oxidation, being active from 0 °C and stable throughout a 24-h test. As for the alumina content (5, 10, and 15 wt.%) in TiO₂, it improved the textural properties by retarding the crystal growth and anatase-rutile phase transformation of TiO₂, suppressing the deposition of carbon on the catalyst surface and stabilizing the Au nanoparticles even at high temperatures. Gold was highly dispersed with nanoparticle sizes ranging from 1 to 2 nm when H₂ was used to treat thermally the Au/TiO₂-Al₂O₃, Au/TiO_2, and Au/Al₂O₃ materials. In addition, the XPS technique helped elicit that Au⁰ and Au¹⁺ boosted their interaction with the TiO₂, Al₂O₃, and TiO₂-Al₂O₃ supports by means of charge transfer, which resulted in outstanding CO oxidation activity from 0 °C. Likewise, the key factors that control the peculiar catalytic performance in the CO oxidation reaction are discussed, which represents a step forward in the versatility behavior of gold catalysts supported on mixed oxide catalysts.