Intertwined synergistic abiotic and biotic degradation of polypropylene pellets in marine mesocosms

Distribution characteristics and microbial synergistic degradation potential of polyethylene and polypropylene in freshwater estuarine sediments

The microbial degradation of polyethylene (PE) and polypropylene (PP) resins in rivers and lakes has emerged as a crucial issue in the management of microplastics. This study revealed that as the flow rate decreased longitudinally, ammonia nitrogen (NH4+-N), heavy fraction of organic carbon (HFOC), and small-size microplastics (< 1 mm) gradually accumulated in the deep and downstream estuarine sediments. Based on their surface morphology and carbonyl index, these sediments were identified as the potential hot zone for PE/PP degradation. Within the identified hot zone, concentrations of PE/PP-degrading genes, enzymes, and bacteria were significantly elevated compared to other zones, exhibiting strong intercorrelations. Analysis of niche differences revealed that the accumulation of NH4+-N and HFOC in the hot zone facilitated the synergistic coexistence of key bacteria responsible for PE/PP degradation within biofilms. The findings of this study offer a novel insight and comprehensive understanding of the distribution characteristics and synergistic degradation potential of PE/PP in natural freshwater environments.

Setting new standards: Multiphasic analysis of microplastic mineralization by fungi

Plastic materials provide numerous benefits. However, properties such as durability and resistance to degradation that make plastic attractive for variable applications likewise foster accumulation in the environment. Fragmentation of plastics leads to the formation of potentially hazardous microplastic, of which a considerable amount derives from polystyrene. Here, we investigated the biodegradation of polystyrene by the tropical sooty mold fungus Capnodium coffeae in different experimental setups. Growth of C. coffeae was stimulated significantly when cultured in presence of plastic polymers rather than in its absence. Stable isotope tracing using 13C-enriched polystyrene particles combined with cavity ring-down spectroscopy showed that the fungus mineralized polystyrene traces. However, phospholipid fatty acid stable isotope probing indicated only marginal assimilation of polystyrene-13C by C. coffeae in liquid cultures. NMR spectroscopic analysis of residual styrene contents prior to and after incubation revealed negligible changes in concentration. Thus, this study suggests a plastiphilic life style of C. coffeae despite minor usage of plastic as a carbon source and the general capability of sooty mold fungi to stimulate polystyrene mineralization, and proposes new standards to identify and unambiguously demonstrate plastic degrading capabilities of microbes.