Metallic-Bonded Pt-Co for Atomically Dispersed Pt in the Co4N Matrix as an Efficient Electrocatalyst for Hydrogen Generation

Mechanism insight into the N-C polar bond and Pd-Co heterojunction for improved hydrogen evolution activity

Constructing platinum-like materials with excellent catalytic activity and low cost has great significance for hydrogen evolution reaction (HER) during electrolysis of water. Herein, palladium nanoparticles (NPs) deposition on the surface of Co NPs using nitrogen-doped carbon (NC) as substrate, denoted as N-ZIFC/CoPd-30, are manufactured and served as HER electrocatalysts. Characterization results and density functional theory calculations validate that Pd-Co heterojunctions with NC acting as "electron donators" promote the Pd species transiting to the electron-rich state based on an efficient electron transfer mechanism, namely the N-C polar bonds induced strong metal-support interaction effect. The electron-rich Pd sites are beneficial to HER. Satisfactorily, N-ZIFC/CoPd-30 have only low overpotentials of 16, 162, and 13 mV@-10 mA cm-2 with the small Tafel slopes of 98 mV/decade, 126 mV/decade, and 72 mV/decade in pH of 13, 7, and 0, respectively. The success in fabricating N-ZIFC/CoPd opens a promising path to constructing other platinum-like electrocatalysts with high HER activity.

The impact of support electronegativity on the electrochemical properties of platinum

Modulating the electronic structure of platinum (Pt) through a support is an important strategy for enhancing its electrocatalytic properties. In this work, to explore the impact of support electronegativity on Pt's catalytic activity for hydrogen evolution, we chose diverse metals with varying electronegativities that are stable in acidic solutions, such as titanium (Ti), molybdenum (Mo), and tungsten (W), as supports. Ti is the optimal support according to density functional theory (DFT) calculations. As expected, the Pt@Ti catalyst demonstrated remarkable efficiency in the hydrogen evolution reaction (HER), displaying a minimal overpotential of 13 mV at -10 mA cm-2, a Tafel slope of 34.5 mV dec-1, and sustained durability over 110 h in a 0.5 M H2SO4 solution. To unravel the metal-support interaction (MSI) between Pt and Ti, a comprehensive exploration encompassing both experimental investigations and DFT calculations was undertaken. The results elucidate that the outstanding HER performance of Pt@Ti stems from robust synergies forged between Pt and Ti atoms within the Ti support. This work not only furnishes a technique for producing electrocatalysts with superior efficiency and stability but also streamlines the process of choosing the most appropriate metal support. Moreover, it enhances comprehension of the interaction between Pt and the metal support.

Heterojunction-Induced Rapid Transformation of Ni3+/Ni2+ Sites which Mediates Urea Oxidation for Energy-Efficient Hydrogen Production

Water electrolysis is an environmentally-friendly strategy for hydrogen production but suffers from significant energy consumption. Substituting urea oxidation reaction (UOR) with lower theoretical voltage for water oxidation reaction adopting nickel-based electrocatalysts engenders reduced energy consumption for hydrogen production. The main obstacle remains strong interaction between accumulated Ni3+ and *COO in the conventional Ni3+-catalyzing pathway. Herein, a novel Ni3+/Ni2+ mediated pathway for UOR via constructing a heterojunction of nickel metaphosphate and nickel telluride (Ni2P4O12/NiTe), which efficiently lowers the energy barrier of UOR and avoids the accumulation of Ni3+ and excessive adsorption of *COO on the electrocatalysts, is developed. As a result, Ni2P4O12/NiTe demonstrates an exceptionally low potential of 1.313 V to achieve a current density of 10 mA cm-2 toward efficient urea oxidation reaction while simultaneously showcases an overpotential of merely 24 mV at 10 mA cm-2 for hydrogen evolution reaction. Constructing urea electrolysis electrolyzer using Ni2P4O12/NiTe at both sides attains 100 mA cm-2 at a low cell voltage of 1.475 V along with excellent stability over 500 h accompanied with nearly 100% Faradic efficiency.

Synergistic Effects of Pyrrolic N/Pyridinic N on Ultrafast Microwave Synthesized Porous CoP/Ni2P to Boost Electrocatalytic Hydrogen Generation

Transition metal phosphides are ideal inexpensive electrocatalysts for water-splitting, but the catalytic activity still falls behind that of noble metal catalysts. Therefore, developing valid strategies to boost the electrocatalytic activity is urgent to promote large-scale applications. Herein, a microwave combustion strategy (20 s) is applied to synthesize N-doped CoP/Ni2P heterojunctions (N-CoP/Ni2P) with porous structure. The porous structure expands the specific surface area and accelerates the mass transport efficiency. Importantly, the pyrrolic N/pyridinic N content is adjusted by changing the amount of urea during the synthesis process and then optimizing the adsorption/desorption capacity for H*/OH* to enhance the catalyst activity. Then, the synthesized N-CoP/Ni2P exhibits small overpotentials of 111 and 133 mV for HER in acidic and alkaline electrolytes and 290 mV for OER in alkaline electrolytes. This work provides an original and efficient approach to the synthesis of porous metal phosphides.

Interfacial engineering of CoP/CoS2 heterostructure for efficiently electrocatalytic pH-universal hydrogen production

The design and development of high-performance, low-cost catalysts with long-term durability are crucial for hydrogen generation from water electrolysis. Interfacial engineering is an appealing strategy to boost the catalytic performance of electrode materials toward hydrogen evolution reaction (HER). Herein, we report a simple phosphidation followed by sulfidation treatment to construct heterogeneous cobalt phosphide-cobalt sulfide nanowire arrays on carbon cloth (CoP/CoS2/CC). When evaluated as catalysts toward the HER, the resultant CoP/CoS2/CC exhibits efficient pH-universal hydrogen production due to the heterostructure, synergistic contribution of CoP and CoS2, and conductive substrate. To attain a current density of 10 mA cm-2, overpotentials of only 111.2, 58.1, and 182.9 mV for CoP/CoS2/CC are required under alkaline, acidic, and neutral conditions, respectively. In particular, the as-prepared CoP/CoS2/CC shows markedly improved HER electroactivity in 1.0 M KOH, even outperforming commercial Pt-C/CC at a current density of >50 mA cm-2. In addition, the self-assembled CoP/CoS2||NiFe layered double hydroxide electrolyzer demonstrates efficient catalytic performance and long-time stability, excelling the benchmark Pt-C||IrO2. These findings indicate an effective pathway for the fabrication of high-performance heterogeneous electrocatalysts for hydrogen production in the future.

Microwave Phosphine-Plasma-Assisted Ultrafast Synthesis of Halogen-Doped Ru/RuP2 with Surface Intermediate Adsorption Modulation for Efficient Alkaline Hydrogen Evolution Reaction

Anionic modification engineering is a crucial approach to develop highly efficient electrocatalysts for hydrogen evolution reaction. Herein, halogen elements (X = Cl, Br, and I)-modified Ru-based nanosheets (X-Ru/RuP2 ) are designed by rapid and eco-friendly microwave-phosphide plasma approach within 60 s. Experimental and density functional theory calculations verify that the introduced halogen element, especially Br, can optimize the surface intermediates adsorption. Specially, the designed Br-Ru/RuP2 favors the water dissociation and following hydrogen adsorption/desorption process. Then, the as-synthesized Br-Ru/RuP2 exhibits low overpotential of 34 mV to reach 10 mA cm-2 coupled with small Tafel slope of 27 mV dec-1 in alkaline electrolyte with excellent long-term stability. Moreover, the electrocatalytic performances in acid and neutral media are also boosted via Br element modification. This work paves a novel way to regulate the electronic structure of Ru-based compounds, and then can boost the electrocatalytic kinetics.

Ultrasmall RuM (Mo, W, Cr) Decorated on Nitrogen-doped Carbon Nanosheet with Strong Metal-support Interactions for Electrocatalytic Hydrogen Generation in Wide pH Range

Developing efficient electrocatalysts for hydrogen evolution reaction (HER) in full pH range can promote the practical applications of hydrogen energy. In this work, nitrogen doped carbon nanosheets supported RuM (Mo, W, Cr) (RuM/NCN) are prepared through an ultrafast microwave approach. The carbon nanosheet structure coupled with the ultrasmall RuM nanoparticles can expose rich active sites to optimize the catalytic activity. Moreover, the strong metal-support interactions also favor to accelerate the reactions kinetics and improve stability. Thus, the developed RuMo/NCN (RuW/NCN) show excellent HER catalytic activities with overpotentials of 72 (75) mV, 82 (82) mV and 124 (119) mV to reach current density of 10 mA cm -2 in 1 M KOH, 0.5 M H2SO4 and alkaline seawater, respectively, and also achieve excellent performance in 1 M PBS. This work provides a valid and novel avenue to design efficient electrocatalysts in renewable energy-related fields.

Orange-peel derived carbon-loaded low content ruthenium nanoparticles as ultra-high performance alkaline water HER electrocatalysts

Carbon materials have a very wide range of applications in the field of electrocatalysis, both as catalyst bodies and as excellent supports for catalysts. In this work, we obtained a graphitic-like orange-peel derived carbon (OPC) material through pre-carbonization and KOH activation strategies using discarded orange-peel as a raw material. OPC has good graphitization characteristics and a few-layer structure, making it very suitable as a support for nanoparticle catalysts. In order to compare the performance of OPC, we used commercial graphene as the benchmark, made two carbon materials uniformly loaded with ruthenium nanoparticles under the same conditions, and obtained two HER catalysts (Ru/OPC and Ru/rGO). The results indicate that Ru/OPC has excellent HER catalytic performance under alkaline conditions, not only superior to Ru/rGO, but also surpassing commercial Pt/C. In 1 M KOH; the overpotential of Ru/OPC is only 3 mV at -10 mA cm-2, greatly exceeding those of Ru/rGO (100 mV) and Pt/C (31 mV). Under high current density (j), the performance of Ru/OPC is even better; the overpotential is 79 mV and 136 mV at -100 mA cm-2 and -200 mA cm-2, respectively. More importantly, Ru/OPC also has a very high TOF and long-term stability, with a TOF of up to 10.62 H2 s-1 at an overpotential of 100 mV and almost no attenuation after 72 h of operation at -50 mA cm-2. Ru/OPC also exhibits good catalytic performance under acidic conditions, significantly superior to that of Ru/rGO. For Ru/OPC, the overpotential is 86 mV, 167 mV and 214 mV at -10 mA cm-2, -100 mA cm-2 and -200 mA cm-2, respectively. Under the same conditions, the overpotential of Ru/rGO is 143 mV, 253 mV and 306 mV at -10 mA cm-2, -100 mA cm-2 and -200 mA cm-2, respectively.

Bifunctional vanadium doped mesoporous Co3O4 on nickel foam towards highly efficient overall urea and water splitting in the alkaline electrolyte

Developing more active and stable electrode materials for oxygen evolution reaction (OER) and urea oxidation reaction (UOR) is necessary for electrocatalytic water and urea oxidation which can be used to generate hydrogen. Here, a low-cost vanadium-doped mesoporous cobalt oxide on Ni foam (V/meso-Co/NF) electrodes are obtained via the grouping of an in-situ citric acid (CA)-assisted evaporation-induced self-assembly (EISA) method and electrophoretic deposition process, and work as highly efficient and long-lasting electrocatalytic materials for OER/UOR. In particular, V/meso-Co/NF electrodes require 329 mV overpotential to maintain a 50 mA/cm2, with exceptional long-term durability of 30 h. Interestingly, V/meso-Co/NF also exhibits excellent electrocatalytic UOR performance, reaching 50 and 100 mA/cm2 versus RHE at low potentials of 1.34 and 1.35 V, respectively. By employing the V/meso-Co/NF materials as both the anode and cathode, this urea electrolysis assembly V/meso-Co/NF-5 (+,-) reaches current densities of 100 mA cm-2 at 1.62 V in KOH/urea, which is nearly 340 mV lesser than classical water electrolysis. The V/meso-Co/NF-5 electrocatalysts also exhibit remarkable durability for electrocatalytic OERs and UORs. The obtained findings revealed that the synthesized V/meso-Co/NF might be a promising electrode materials for overall urea-rich wastewater management and H2 generation from wastewater.

Fabricating Ru Atom-Doped Novel FeP4/Fe2PO5 Heterogeneous Interface for Overall Water Splitting in Alkaline Environment

Developing bifunctional electrocatalysts with low-content noble metals and high activity and stability is crucial for water splitting. Herein, we reported a novel Ru doped FeP4/Fe2PO5 heterogeneous interface catalyst (Ru@FeP4/Fe2PO5) for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) by heat treatment coupling electrodeposition strategy. Experiments disclosed that Ru@FeP4/Fe2PO5 proclaimed excellent catalytic activity for the OER (249 mV@100 mA cm-2) and HER (49 mV@10 mA cm-2) in a 1 M KOH environment. More importantly, the mass activity and turnover frequency of Ru@FeP4/Fe2PO5 were 117 and 108 times higher than that of commercial RuO2 at an overpotential of 300 mV during the OER, respectively. In addition, the assembled Ru@FeP4/Fe2PO5 || Ru@FeP4/Fe2PO5 system could retain superior durability in a two-electrode system for 134 h at 300 mA cm-2. Further mechanism studies revealed that Ru atoms in Ru@FeP4/Fe2PO5 act in a key role for the excellent activity during water splitting because the electronic structure of Ru sites could be optimized by the interaction between Ru and Fe atoms at the interface to strengthen the adsorption of reaction intermediates. Besides, the introduction of Ru atoms could also enhance the charge transfer, which effectually accelerates the reaction kinetics. The strategy of anchoring Ru atom on novel heterostructure provides a promising path to boost the overall activity of electrocatalysts for water splitting.

Robust cellulose fiber/fibrous sepiolite coated RuO2-CoP aerogel as monolithic catalyst for hydrogen generation via NaBH4 hydrolysis

Commercial carriers have been used to prepare monolithic NaBH₄ hydrolytic catalysts, but the fixed structure and material limit the application scope and design freedom. Herein, the RuO₂-CoP catalyst is coated on the surface of fibrous sepiolite (RuO₂-CoP@aSep) by in-situ deposition, annealing in air and phosphating, which is constructed into the aerogel with cellulose nanofiber (CNF) and polyvinyl alcohol (PVA) by freeze drying process. The hydrogen generation rate (HGR) of RuO₂-CoP@aSep increases from 3655 to 10713mLmin^-1g_catalyst^-1 by adjusting the mass ratio of cobalt to ruthenium in RuO₂-CoP. Moreover, the optimized composite aerogel can get HGR (5268mLmin^-1g_catalyst^-1) by regulating its formulation, and the catalytic activity and mass loss rate of the aerogel maintains 76.6 and 0.92 % after five cycles of testing. The synergistic interaction between Ru and Co species, micro-nano porous structure, and structural coupling provide good catalytic activity and cycling performance, and show great potential in the design of controllable NaBH₄ hydrolyzed monolithic catalysts.

Ultrafast synthesis of halogen-doped Ru-based electrocatalysts with electronic regulation for hydrogen generation in acidic and alkaline media

Developing a facile and time-saving method for preparing hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) electrocatalysts can accelerate the practical applications of hydrogen energy. In this study, halogen (X = F, Cl, Br and I) doped Ru-RuO₂ on carbon cloth (CC) (X-Ru-RuO₂/MCC) was synthesized via an ultrafast microwave-assisted method for 30 s. Particularly, the doped Br (Br-Ru-RuO₂/MCC) significantly improved the electrocatalytic performances of the catalyst through the regulation of electronic structures. Then, the Br-Ru-RuO₂/MCC catalyst featured HER overpotentials of 44 mV and 77 mV in 1.0 M KOH and 0.5 M H₂SO₄, and the OER overpotential of 300 mV at 10 mA cm^-2 in 1.0 M KOH. This study provides a novel method for developing of halogen-doped catalysts.

In situ synthesis of two-dimensional graphene-like nickel-molybdenum nitride as efficient electrocatalyst towards water-splitting under large-current density

Transition metal nitride (TMNs) electrocatalysts have attracted tremendous attentions for their unique electron structure, high activity, and excellent stability. Herein, a two-dimensional (2D) graphene-like structured nickel-molybdenum nitride (Ni-MoN) on nickel foam (NF), is prepared via facile hydrothermal and following nitridation process. The as-prepared Ni-MoN-450 (pyrolysis at 450 °C) displays good hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) performances in alkaline media. Only 22 mV and 117 mV are needed to achieve current densities of 10 mA cm^-2 and 500 mA cm^-2 in 1.0 M KOH, respectively, toward HER. The assembled two-electrode system, with the synthesized Ni-MoN-450 as the anode and cathode, exhibits good performance to achieve 1000 mA cm^-2 in 1.0 M KOH + 25 °C and 6.0 M KOH + 80 °C. Moreover, it also presents long-term stability under large-current density, which verified its robust property.

Microwave Synthesis of Pt Clusters on Black TiO2 with Abundant Oxygen Vacancies for Efficient Acidic Electrocatalytic Hydrogen Evolution

Oxygen vacancies-enriched black TiO₂ is one promising support for enhancing hydrogen evolution reaction (HER). Herein, oxygen vacancies enriched black TiO₂ supported sub-nanometer Pt clusters (Pt/TiO₂ -O_V ) with metal support interactions is designed through solvent-free microwave and following low-temperature electroless approach for the first time. High-temperature and strong reductants are not required and then can avoid the aggregation of decorated Pt species. Experimental and theoretical calculation verify that the created oxygen vacancies and Pt clusters exhibit synergistic effects for optimizing the reaction kinetics. Based on it, Pt/TiO₂ -O_V presents remarkable electrocatalytic performance with 18 mV to achieve 10 mA cm^-2 coupled with small Tafel slope of 12 mV dec^-1 . This work provides quick synthetic strategy for preparing black titanium dioxide based nanomaterials.

Methylthiophenyl- and Methylthiobiphenyl-Substituted A2B CoIIIcorroles: Modulating Electrocatalyzed Hydrogen Evolution Reactions on Surface-Modified Gold Electrodes

Four A₂B-type Co^IIIcorroles (2a-2d) with electron-donating/withdrawing substituents at the A₂ meso-aryl substituents and a 4-(methylthio)phenyl ring at the B position have been synthesized and characterized, along with a series of meso-extended Co^IIIcorroles (4a-4c) with 4'-(methylthio)biphenyl moieties. The electronic structures and structure-property relationships of the dyes have been analyzed by comparing their redox and optical properties to trends predicted in density functional theory calculations. Au electrodes surface-modified with 2a-2d and 4a-4c are highly efficient catalysts for electrocatalyzed hydrogen evolution reactions, and the electrocatalytic properties can be readily modulated by fine-tuning the electronic structure of the Co^IIIcorrole and the distance between the "Au-S" bond and Co^III center.