Photoexcited-induced sensitivity of InGaAs surface QDs to environment

Carrier Injection to In0.4Ga0.6As/GaAs Surface Quantum Dots in Coupled Hybrid Nanostructures

Stacking growth of the InGaAs quantum dots (QDs) on top of a carrier injection layer is a very useful strategy to develop QD devices. This research aims to study the carrier injection effect in hybrid structures with a layer of In0.4Ga0.6As surface quantum dots (SQDs), coupled to an injection layer of either one layer of In0.4Ga0.6As buried QDs (BQDs) or an In0.15Ga0.85As quantum well (QW), both through a 10 nm GaAs thin spacer. Spectroscopic measurements show that carrier capture and emission efficiency for SQDs in the BQD injection structure is better than that of the QW injection, due to strong physical and electrical coupling between the two QD layers. In the case of QW injection, although most carriers can be collected into the QW, they then tunnel into the wetting layer of the SQDs and are subsequently lost to surface states via non-radiative recombination. Therefore, the QW as an injection source for SQDs may not work as well as the BQDs for stacking coupled SQDs structures.

Photoluminescence characterization of wetting layer and carrier dynamics for coupled InGaAs/GaAs surface quantum dot pair structures

The optical properties are investigated by spectroscopic characterizations for bilayer InGaAs/GaAs quantum dot (QD) structures consisting of a layer of surface quantum dots (SQDs) separated from a layer of buried quantum dots (BQDs) by different GaAs spacers with thicknesses of 7 nm, 10.5 nm and 70 nm. The coupling from the BQDs to SQDs leads to carrier transfer for the two samples with thin spacers, 7 nm and 10.5 nm, in which QD pairs are obtained while not for the 70 nm spacer sample. The carrier tunneling time is measured to be 0.145 ns and 0.275 ns from BQDs to SQD through the 7 nm and 10.5 nm spacers, respectively. A weak emission band can be observed at the wavelength of ∼ 960 nm, while the excitation intensity dependent PL and PLE spectra show that this is from the wetting layer (WL) of the SQDs. This WL is very important for carrier dynamics in bilayer structures of BQDs and SQDs, including for carrier generation, capture, relaxation, tunneling, and recombination. These results provide useful information for understanding the optical properties of InGaAs SQDs and for using such hybrid structures as building blocks for surface sensing devices.

Scanning tunneling spectroscopic monitoring of surface states role on water passivation of InGaAs uncapped quantum dots

A detailed local analysis of the impact of water coverage on the density of surface states in In_0.5Ga_0.5As surface nanostructures is reported by spectroscopy monitoring the surface conductivity at the nanometer-scale.