Behavior of osteoblasts on a type I atelocollagen grafted ozone oxidized poly L-lactic acid membrane

With oxidizing poly-L-lactic acid (PLLA) surface by ozone, peroxide groups are easily generated on the surface. Those peroxides are broken down by redox-coupling reaction, and provide active species that initiate grafting by reaction with the collagen molecules. The surface density of generated peroxide on a PLLA surface was determined by an iodide method. The maximum concentration of peroxide was about 2.87 x 10(-8) mol/cm2 when ozone oxidation was performed at 60 V for 60 min. After the surface oxidation, type I atelocollagen was grafted onto PLLA surface. All physical measurements on the collagen-grafted surface indicated that the PLLA surface was effectively grafted with type I atelocollagen. Behavior of rat calvaria osteoblasts on type I atelocollagen grafted PLLA (PLLA + COL) surface was observed. Initial attachment of osteoblasts on the surface was significantly enhanced, and it is assumed that the atelocollagen matrix supported the initial attachment and growth of cells. Collagenous protein synthesis of osteoblasts was maintained at relatively low level in the early stage of proliferation due to the primarily existing grafted type I atelocollagen, and then increased in 7 days as the osteoblast differentiated. After 7 days, collagenous protein synthesis in osteoblasts was activated. Alkaline phosphatase (ALPase) activity and mineralization by osteoblasts were promoted on PLLA + COL surface. In comparison with PLLA + COL, non-treated PLLA and tissue culture plate (TCPS) did not show any feature expressed in osteoblasts' maturation up to 9 days in this experiment. The grafted type I atelocollagen provided a favorable matrix for cell migration in relation with collagenase expression. Ozone oxidation might be a favorable method for surface modification of PLLA membranes by collagen grafting, and cell behavior could be modulated by the grafted collagen.

Type I atelocollagen grafting onto ozone-treated polyurethane films: cell attachment, proliferation, and collagen synthesis

An approach is presented for the graft copolymerization of type I atelocollagen onto the surface of polyurethane (PU) films treated with ozone. Through inducing oxidization to modify PU surface by ozone, peroxide groups are easily generated on the surface. Those peroxides are broken by redox-polymerization, and provide active species which initiate graft polymerization by reacting with amines in the collagen molecules. The ozone oxidation time and voltage could readily control the amount of peroxide production. The surface density of generated peroxides on PU surface was determined by iodide method. The maximum concentration of peroxide was about 10.20 x 10(-8)mol/cm(2) when ozone oxidation was performed at 60 V for 30 min. After the reaction of PU by ozone oxidation, type I atelocollagen was graft-copolymerized onto the PU film. All the physical measurements on the collagen-grafted surface indicated that the PU surface was effectively covered with type I atelocollagen. The interaction of the collagen-grafted PU surface with fibroblasts could be greatly enhanced by the surface graft polymerization with type I atelocollagen. Attachment and proliferation of fibroblasts on the grafted type I atelocollagen were significantly enhanced, and it is assumed that the atelocollagen matrix supported the initial attachment and growth of cells. In the early stage of proliferation, collagen synthesis in fibroblasts was not activated and remained at a relatively low level due to the grafted type I atelocollagen, increasing only with fibroblast differentiation.

Development of small-diameter vascular prostheses which release bioactive agents

A porous, distensible, tubular membrane which incorporates albumin and basic Fibroblast Growth Factor (bFGF), and is potentially utilizable as a bioactive small-diameter vascular prosthesis, was fabricated by a combined spraying, phase-inversion technique using a suspension of albumin and bFGF into a polyetherurethane-urea (Biomer) solution in dimethylacetamide (DMA). Scanning electron microscopy showed a material with an open-cell trabecular structure and small particles of albumin and/or bFGF entrapped in the bulk of the polyurethane trabeculae. The material released albumin and bFGF at an approximately constant rate for at least 2 weeks. The bFGF initially incorporated in the polymer remained biologically active as shown by in-vitro proliferation of human endothelial cells.