Dentin bond strength of bioactive cement in comparison to conventional resin cement when photosensitized with Er,Cr:YSGG Laser

Comparative evaluation of effect of chlorhexidine application on dentin bond strength with two different adhesives after ER, CR: YSGG phototherapy: an in vitro study

This study aimed to assess the efficacy of phototherapy with an Er, Cr:YSGG laser on the bond strength of dentin using two different adhesive systems after chlorhexidine (CHX) application. Twenty-four non-carious human molar teeth were separated into three main groups: negative control Group A (Group A), CHX and phototherapy with an Er, Cr:YSGG laser (Group PC), and CHX with conventional diamond bur (no phototherapy) (Group C). These groups were divided into two subgroups based on adhesives: Clearfil Universal Quick Bond and Clearfil SE Bond. To evaluate the microtensile bond strength, the occlusal enamel surfaces of the teeth were removed with a low-speed, water-cooled diamond bur to expose hard dentin tissue. The teeth within Group PC were treated with Er, Cr:YSGG phototherapy. The surfaces were then disinfected with 0.2% chlorhexidine gluconate. Subgroups were applied according to the manufacturer's instructions using the adhesive systems mentioned above. Following adhesive application, the teeth were restored with composite resin. A microtensile bond strength test was performed on the test sticks obtained from the teeth using a universal test device. Data were analyzed using variance analysis (ANOVA) at a significance level of p < 0.05. Among all groups, the highest bond strength was achieved with Clearfil SE Bond with CHX + phototherapy (45.6 ± 4.2), while the lowest was achieved with Clearfil Universal Quick Bond without phototherapy (control group) (27.0 ± 6.7) (p < 0.05). Phototherapy with Er, Cr: YSGG following chlorhexidine application enhanced the bond strength of both the bond systems (p < 0.05).

PEEK for Oral Applications: Recent Advances in Mechanical and Adhesive Properties

Polyetheretherketone (PEEK) is a thermoplastic material widely used in engineering applications due to its good biomechanical properties and high temperature stability. Compared to traditional metal and ceramic dental materials, PEEK dental implants exhibit less stress shielding, thus better matching the mechanical properties of bone. As a promising medical material, PEEK can be used as implant abutments, removable and fixed prostheses, and maxillofacial prostheses. It can be blended with materials such as fibers and ceramics to improve its mechanical strength for better clinical dental applications. Compared to conventional pressed and CAD/CAM milling fabrication, 3D-printed PEEK exhibits excellent flexural and tensile strength and parameters such as printing temperature and speed can affect its mechanical properties. However, the bioinert nature of PEEK can make adhesive bonding difficult. The bond strength can be improved by roughening or introducing functional groups on the PEEK surface by sandblasting, acid etching, plasma treatment, laser treatment, and adhesive systems. This paper provides a comprehensive overview of the research progress on the mechanical properties of PEEK for dental applications in the context of specific applications, composites, and their preparation processes. In addition, the research on the adhesive properties of PEEK over the past few years is highlighted. Thus, this review aims to build a conceptual and practical toolkit for the study of the mechanical and adhesive properties of PEEK materials. More importantly, it provides a rationale and a general new basis for the application of PEEK in the dental field.

Assessment of Caries-Affected Dentin Adhesive Interface Treated with Contemporary Conditioning Techniques

Objective: The aim of this study was to assess shear bond strength (SBS) and failure analysis of adhesion of composite resin (CR) to caries-affected dentin (CAD) pretreated with the Er,Cr:YSGG (ECY) laser, photodynamic therapy (PDT), and etch and rinse (ER) used for cavity disinfection. Materials and methods: Methods used in this study included scanning electron microscopy (SEM), SBS analysis, failure analysis, and digital microscopy. The methods were adopted to assess bond integrity, CAD interface, smear layer, and hybridization. Thirty human third molars assessed clinically and having scores of 4 and 5 based on International Caries Detection and Assessment System (ICDAS) criteria were inspected. Infected dentin was removed. Dentin that was hard and stained pink was categorized as CAD. Ten samples were used in each group for pretreatment of CAD. Ten samples of healthy dentin [sound dentin (SD)] were collected separately and taken as controls. Samples were divided into the following groups: group 1: SD+ER; group 2: CAD+ER; group 3: CAD+ECY; and group 4: CAD+PDT after the pretreatment bonding agent was applied and the restorative procedure was performed using CR. Results: CAD conditioned with PDT before bonding to CR demonstrated the lowest SBS values (11.22 ± 0.77 MPa), whereas the highest SBS values were observed in the SD surface treated with ER (18.25 ± 1.22 MPa). In CAD and SD pretreated with ER, majority of failure modes were cohesive failure and admixed failure, whereas in CAD pretreated with PDT and the ECY laser, the adhesive failure mode was pertinent. Conclusions: The use of the ECY laser and PDT on CAD for cavity disinfection does not have potential for application in clinical settings as it decreases bond integrity of CR. Moreover, the ER pretreatment method for CAD and SD remains the gold standard.

Interaction of zirconium oxide nanoparticle infiltrated resin adhesive with dentin conditioned by phosphoric acid and Er, Cr: YSGG laser

The aim was to prepare experimental adhesive (EA) with ZrO₂ nanoparticles (ZEA) and without it; and its interaction with dentin conditioned with photodynamic therapy (PDT), etch and rinse, and Er, Cr: YSGG laser (ECL). Methods consisted of the scanning electron microscope (SEM), energy dispersive X-ray (EDX), shear bond strength (SBS) failure mode, and rheological property analysis. The methods were employed to assess bond integrity; the shape of ZrO₂ NPs and interfacial dentin and adhesive interaction. Ninety premolar teeth were collected and pre-bonding, conditioning of dentin was performed utilizing phosphoric acid (H3PO4), photodynamic therapy (PDT), and ER-CR-YSGG laser (ECL). The teeth were set to form bonded specimens using two adhesives EA and ZEA. The microscopic imagery of ZrO₂ revealed irregular-shaped, non-edged particles. EDX analysis revealed Zr to be 75.7% whereas, O2 by weight was 25.3%. The highest SBS was demonstrated in dentin conditioned with etch and rinse and ZEA (19.05 ± 0.13 MPa). Whereas, the lowest SBS was observed in dentin surface treated with PDT and EA (12.25 ± 0.14 MPa). Most of the reported failure modes were adhesive. Rheological analysis revealed that with increasing frequencies the viscosities of adhesives were reduced. The presence of 10% ZrO by weight in adhesive improves SBS of restoration and this improvement in bond values is statistically significant compared to EA. Bond values may be influenced by surface treatment of dentin.

Polymer-Based Bioactive Luting Agents for Cementation of All-Ceramic Crowns: An SEM, EDX, Microleakage, Fracture Strength, and Color Stability Study

The aim of the study was to compare microleakage and fracture loads of all ceramic crowns luted with conventional polymer resins and polymeric bioactive cements and to assess the color stability of polymeric bioactive cements. Seventy-five extracted premolar teeth were tested for fracture loads and microleakage in all-ceramic crowns cemented with two types of polymeric bioactive cements and resin cements. In addition, the degree of color change for each cement with coffee was assessed. Thirty maxillary premolar teeth for fracture loads and thirty mandibular premolar teeth for microleakage were prepared; standardized teeth preparations were performed by a single experienced operator. All prepared specimens were randomly distributed to three groups (n = 20) based on the type of cement, Group 1: resin cement (Multilink N); Group 2: polymeric bioactive cement (ACTIVA); Group 3: polymeric bioactive cement (Ceramir). The cementation procedures for all cements (Multilink, ACTIVA, and Ceramir) were performed according to the manufacturers' instructions. All specimens were aged using thermocycling for 30,000 cycles (5-55 °C, dwell time 30 s). These specimens were tested using the universal testing machine for fracture strength and with a micro-CT for microleakage. For the color stability evaluation, the cement specimens were immersed in coffee and evaluated with a spectrometer. Results: The highest and lowest means for fracture loads were observed in resin cements (49.5 ± 8.85) and Ceramir (39.8 ± 9.16), respectively. Ceramir (2.563 ± 0.71) showed the highest microleakage compared to resin (0.70 ± 0.75) and ACTIVA (0.61 ± 0.56). ACTIVA cements showed comparable fracture loads, microleakage, and stain resistance compared to resin cements.

Influence of synthetic and natural photosensitizers activated by photodynamic therapy on extrusion bond strength of fiber post to radicular dentin

OBJECTIVE

To assess the effect of different photosensitizers activated by low-level laser therapy on EBS of glass fiber post to radicular dentin.

METHODS

This study was conducted at King Saud University from January 2021 to March 202. Fifty maxillary central incisors were sanitized and decoronated. NiTi was used for mechanical instrumentation of the canal. All canals were shaped, cleaned and obturated with gutta-percha. Post space was made using peso reamers. Four Division of groups were made according to photosensitizers used (n=10). Group-1: MBP at 100mg/l, Group-2: Phycocyanin at 100mg/l, Group-3: CP at 500mg/l, and Group-4 toluidine blue photosensitizer (TB). Lasers were used for activation of photosensitizers. In Group-5 samples were irrigated using sodium hypochlorite NaOCl +17% EDTA. Posts were cemented and teeth sectioned into apical, coronal and middle. For EBS all samples were subjected to a universal testing machine. Fracture patterns were analyzed using stereomicroscope. To compare EBS at different segments One-way analysis of variance (ANOVA) and Tukey multiple comparison tests (p=0.05) was performed.

RESULTS

The maximum value of EBS was shown in Group-2 radicular canal treated with CP with 17% EDTA at all three levels cervical (8.61±1.32 MPa), middle (6.81±0.73 MPa), and apical (5.51±0.25 MPa). Similarly, the minimum value of EBS was displayed in Group-5 canal irrigated with 2.25% NaOCl +17% EDTA (control) coronal (6.10±1.77 MPa), middle (5.11±0.75MPa), and apical (3.60±0.94 MPa). Intragroup assessment disclosed a decrease in EBS from cervical one-third to apical one-third in all groups.

CONCLUSION

P, CP, and TB along with EDTA have the potential to be used as canal disinfectant and favors the bonding of GFP to radicular dentin using self-etch adhesive resin.