Influence of Non-Thermal Atmospheric Pressure Plasma Treatment on Retentive Strength between Zirconia Crown and Titanium Implant Abutment

Influence of cold atmospheric-pressure-plasma in combination with different pretreatment methods on the pull-off tensile load in two-piece abutment-crowns: an in-vitro study

BACKGROUND

In implant prosthetic dentistry, the adhesive connection of individualized ceramic crowns and prefabricated titanium bases leads to several benefits. However, the durability of the bonding could be a weak point and especially depends on sufficient surface pretreatment. Cold atmospheric-pressure plasma (CAP) is a pretreatment method that should improve the surface properties without physical damage. Thus, the purpose of this study was to investigate the influence of CAP treatment on pull-off tensile load in two-piece abutment crowns.

METHODS

Eighty zirconia crowns and titanium bases were divided into eight groups (n = 10) according to their surface pretreatment prior to cementation with Panavia V5: no treatment (A); sandblasting (B); 10-MDP primer (C); sandblasting and primer (D); CAP (AP); sandblasting and CAP (BP); CAP and primer (CP); sandblasting, CAP and primer (DP). The specimens were thermocycled (5°/55°, 5000 cycles), and then the pull-off tensile load (TL) was measured. Statistical analyses were performed using three-way ANOVA with Tukey post-hoc and Fisher's exact tests.

RESULTS

The results showed that the TL was highest in group D (p < 0.0001). Some combinations of different treatments led to effects that were greater than the sum of the individual effects. These effects were modified by interactions. Only in combination with primer, CAP treatment had a small but positive significant effect (group CP vs. C and CP vs. AP, p < 0.0001) which however did not come close to the strong interaction effect that resulted from the combination of sandblasting and primer.

CONCLUSION

Within the limitations of this study, CAP treatment cannot be recommended in this specific field of indication due to its unreliable influence on TL in combination with other pretreatment methods.

Influence of Cold Atmospheric Plasma on Surface Characteristics and Bond Strength of a Resin Nanoceramic

The purpose of this study was to investigate the effect of cold atmospheric plasma (CAP) treatment on resin nanoceramic (RNC) surface state and its bond strength with resin cement. RNC with different surface treatments were prepared: control, sandblasting treatment (SB), hydrofluoric acid etching (HF) and plasma treatment of helium gas (CAP-He) and argon gas (CAP-Ar). The prepared samples were measured by SEM, Ra, Rz, contact angle goniometer, and XPS for surface characteristics. The shear bond test of RNC was examined in nine groups: SB + saline coupling agent (SL), HF + SL, CAP-He/Ar, CAP-He/Ar + SL, SB + CAP-He/Ar + SL, and control. The bond strength between RNC and resin cement was compared using shear bond strength test, before and after thermocycling. After CAP irradiation, the surface topography maintained, while the surface water contact angle was significantly reduced to 10.18° ± 1.36° (CAP-He) and 7.58° ± 1.79° (CAP-Ar). The removal of carbon contamination and inducing of oxygen radicals was detected after CAP treatment. The bond strength was improved by CAP treatment, but varied on CAP gas species and combination methods. CAP of Ar gas had better SBS than He gas. After thermocycling, CAP-Ar + SL showed the maximized shear bond strength (32.38 ± 1.42 MPa), even higher than SB + SL group (30.08 ± 2.80 MPa, p < 0.05). In conclusion, CAP treatment of helium and argon can improve the bonding properties of RNC by improving surface wettability, and CAP of argon gas combined with silane coupling agent shows the highest bond strength.

The Effect of a 10-MDP-Based Dentin Adhesive as Alternative for Bonding to Implant Abutment Materials

Bonding to different dental restorative materials is challenging. This study aimed to evaluate the effect of a 10-MDP-based dentin adhesive on the shear bond strength (SBS) of self-adhesive resin cement (RC) to implant abutment materials. One hundred and twenty specimens were obtained from zirconia (ZO), cobalt-chromium alloy (CoCr), and commercially pure titanium (Ti), which were treated as follows (n = 10): control group-non-treated (CG), 10-MDP-based dentin adhesive (SB), light-cured SB (SB-LC), and zirconia primer (ZP). Blocks of RC were buildup and, after 24 h, were tested for bond strength. Data of SBS (MPa) were submitted to two-way ANOVA and Tukey test (α = 0.05). There was no difference in SBS among materials for CG and ZP, higher SBS were recorded for Ti SB and Ti SB-LC compared to ZO upon the same surface treatments. For the comparisons among treatments, SB-LC showed the highest SBS for CoCr. For ZO and Ti, higher SBS were recorded with SB and SB-LC. No cohesive failures were observed. It was concluded that the surface treatment with 10-MDP-based materials increased the bond strength of the resin cement to abutment materials, which showed to be material dependent.

Novel dual-functional implants via oxygen non-thermal plasma and quaternary ammonium to promote osteogenesis and combat infections

OBJECTIVE

Implant-related infections are a primary reason for implant failures that affect millions of patients. It is of paramount importance to develop novel implants that possess the dual functions of osteogenesis-promotion and antibacterial activity. The objectives of this study were to: (1) develop novel dual-functional titanium (Ti) implants by combining oxygen non-thermal plasma and covalent bonding of antibacterial organosilicon quaternary ammonium monomers; (2) investigate the physicochemical properties, bioactivity and antibacterial effects of the modified implants for the first time.

METHODS

Surface characteristics of the modified Ti surfaces were tested. Adherence and viability of rat bone marrow-derived stem cells (rBMSCs) on the surface were evaluated. Metabolic activity of biofilm on the surfaces were measured. The stability of the dual-function after 5000 thermal cycles was also evaluated.

RESULTS

The presence of chemical bonding between Ti and organosilicon monomers demonstrated covalent immobilization of the antibacterial agents. The water contact angle of the treated Ti surfaces decreased from 70.98 ± 3.68° to 59.86 ± 4.91°. The adhesion and proliferation of rBMSCs on the modified Ti were increased by 40%, compared to control group (P < 0.05). The metabolic level of biofilms on modified Ti were reduced by more than half, compared to control (P < 0.05). The modified Ti implants exhibited cell-promotion and antibacterial stability after thermal cycles.

SIGNIFICANCE

The new dual-functional Ti implant is promising to promote osteogenesis while simultaneously preventing infections. Furthermore, the novel surface modification and processing methods have applicability to enhancing a wide range of other implants to improve bioactivity and combat infections.