Chang YC, Lin IC, Chin NC, Juang SE, Chou CM. Na
2Ti
3O
7@RF@Ag Heterostructures as Efficient Substrates for SERS and Photocatalytic Applications.
Molecules 2023;
29:218. [PMID:
38202801 PMCID:
PMC10780028 DOI:
10.3390/molecules29010218]
[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/09/2023] [Revised: 12/18/2023] [Accepted: 12/27/2023] [Indexed: 01/12/2024] Open
Abstract
A multi-step procedure was effectively employed to synthesize innovative three-dimensional (3D) heterostructures encompassing sodium titanate (Na2Ti3O7) nanowire cores, an intermediate resorcinol-formaldehyde (RF) layer, and outer silver (Ag) nanoparticle sheaths, referred to as Na2Ti3O7@RF@Ag heterostructures. Initially, a one-step hydrothermal technique facilitated the direct growth of single-crystal Na2Ti3O7 nanowires onto a flexible Ti foil. Subsequently, a two-step wet chemical process facilitated the sequential deposition of an RF layer and Ag nanoparticles onto the Na2Ti3O7 nanowires at a low reaction temperature. Optimal concentrations of silver nitrate and L-ascorbic acid can lead to the cultivation of Na2Ti3O7@RF@Ag heterostructures exhibiting heightened surface-enhanced Raman scattering (SERS), which is particularly beneficial for the detection of rhodamine B (RhB) molecules. This phenomenon can be ascribed to the distinctive geometry of the Na2Ti3O7@RF@Ag heterostructures, which offer an increased number of hot spots and surface-active sites, thereby showcasing notable SERS enhancement, commendable reproducibility, and enduring stability over the long term. Furthermore, the Na2Ti3O7@RF@Ag heterostructures demonstrate remarkable follow-up as first-order chemical kinetic and recyclable photocatalysts for the photodecomposition of an RhB solution under UV light irradiation. This result can be attributed to the enhanced inhibition of electron-hole pair recombination and increased surface-active sites.
Collapse