Reliability Prediction of Acrylonitrile O-Ring for Nuclear Power Applications Based on Shore Hardness Measurements

A Leakage Prediction Model for Sealing Performance Assessment of EPDM O-Rings under Irradiation Conditions

In this work, a model for predicting the leakage rate was developed to investigate the effect of irradiation on the sealing performance of ethylene propylene diene monomer (EPDM) O-rings. The model is based on a mesoscopic interfacial gap flow simulation and accurately predicts the sealing performance of irradiated and non-irradiated materials by utilizing the gap height as an indicator in a mechanical simulation of the O-ring under operating conditions. A comparison with vacuum test results indicates that the model is a good predictor of leak initiation. The positive pressure leakage of the O-rings was investigated numerically. The results show the following. The sealing performance of the non-irradiated O-ring is much better than that of the irradiated one. The sealing performance is the worst at 0. 713 MGy and the best at 1.43 MGy, and the seal is maintained at an absorbed dose of 3.55 MGy. A theoretical analysis of the non-monotonic variation using the proposed model shows that the leakage behavior of the O-rings depends not only on the material properties but also on the roughness and prestressing properties. Finally, a method was proposed to classify the sealing performance, using the maximum allowable leakage rate as an indicator.

Automatic Method for Vickers Hardness Estimation by Image Processing

Hardness is one of the most important mechanical properties of materials, since it is used to estimate their quality and to determine their suitability for a particular application. One method of determining quality is the Vickers hardness test, in which the resistance to plastic deformation at the surface of the material is measured after applying force with an indenter. The hardness is measured from the sample image, which is a tedious, time-consuming, and prone to human error procedure. Therefore, in this work, a new automatic method based on image processing techniques is proposed, allowing for obtaining results quickly and more accurately even with high irregularities in the indentation mark. For the development and validation of the method, a set of microscopy images of samples indented with applied forces of 5N and 10N on AISI D2 steel with and without quenching, tempering heat treatment and samples coated with titanium niobium nitride (TiNbN) was used. The proposed method was implemented as a plugin of the ImageJ program, allowing for obtaining reproducible Vickers hardness results in an average time of 2.05 seconds with an accuracy of 98.3% and a maximum error of 4.5% with respect to the values obtained manually, used as a golden standard.

Can Accelerated Aging Procedures Predict the Long Term Behavior of Polymers Exposed to Different Environments?

During their useful life, polymers are subject to degradation processes due to exposure to specific environmental conditions over long times. These processes generally lead to changes, almost always irreversible, of properties and performances of polymers, changes which would be useful to be able to predict in advance. To meet this need, numerous investigations have been focused on the possibility to predict the long-term performance of polymers, if exposed to specific environments, by the so called “accelerated aging” tests. In such procedures, the long-term behavior of polymeric materials is typically predicted by subjecting them to cycles of radiations, temperatures, vapor condensation, and other external agents, at levels well above those found in true conditions in order to accelerate the degradation of polymers: this can produce effects that substantially deviate from those observable under natural exposure. Even following the standard codes, different environmental parameters are often used in the diverse studies, making it difficult to compare different investigations. The correlation of results from accelerated procedures with data collected after natural exposure is still a debated matter. Furthermore, since the environmental conditions are a function of the season and the geographical position, and are also characteristic of the type of exposure area, the environmental parameters to be used in accelerated aging tests should also consider these variables. These and other issues concerning accelerated aging tests applied to polymers are analyzed in the present work. However, bearing in mind the limitations of these practices, they can find useful applications for rating the durability of polymeric materials.