In vivo wear pattern of experimental composite resins based on different resin monomers

In vitro wear behavior of restorative resin composites against bovine enamel

The purpose of this study was to clarify the effects of fabrication method of restorative resin-based composites on its wear using enamel as antagonist teeth. Wear evaluation was performed via two-body wear test using hemispherical samples of restorative resin-based composite (abrader specimen) fabricated through direct restoration method, indirect restoration method, and CAD/CAM, and bovine enamel (substrate specimen). As a result, there was a difference in wear volume between resin-based composite and bovine enamel depending on the fabrication method. Resin composite used for indirect restoration method showed more wear in both the abrader and substrate specimens. Resin composite used for CAD/CAM crowns showed greater wear volume in the abrader specimen. In conclusion, results clarified that fabrication method of restorative resin-based composite has an influence on the wear of the resin composite itself and enamel as antagonist teeth.

Three-body wear of 3D printed temporary materials

OBJECTIVE

The aim of this study was to investigate the three-body wear of different additively manufactured temporary materials, one temporary PMMA material for CAD/CAM milling and one resin-based composite for direct restorations as a control group by using an ACTA machine.

METHODS

Specimens (n=8) of the 3D printing materials 3Delta temp, NextDent C&B, Freeprint temp were additively manufactured by DLP 3D printer. Postprocessing was carried out according to the manufacturer's specifications. Telio CAD were cut out of blocks, Tetric EvoCeram was applied directly and light cured. Three-body wear was simulated with an ACTA machine. Data were statistically analysed (ANOVA, post hoc test: Tukey, p<0.05). The worn surfaces of the specimens were examined with a FE-SEM.

RESULTS

The average mean wear was 50±15μm for Tetric EvoCeram<62±4μm for 3Delta temp<236±31μm for Telio CAD<255±13μm for NextDent C&B<257±24μm for Freeprint temp. After 200,000 cycles, the wear and wear rates for Tetric EvoCeram and 3Delta temp were significantly lower than those for the other materials. SEM revealed that 3Delta temp has a higher filler proportion than the other 3D printing materials but less than Tetric EvoCeram.

SIGNIFICANCE

The filler content influences the wear behaviour of additively manufactured materials as well as dental restorative composite materials. While most 3D printing materials have a low inorganic filler load, which qualifies the materials for temporary use only, one 3D printing material has an optimized composition that would qualify the material for longer clinical service time if wear is considered as the outcome variable.

Evaluation of the surface hardness, roughness, gloss and color of composites after different finishing/polishing treatments and thermocycling using a multitechnique approach

The objectives of this study were to evaluate the mechanical and physical properties of resin composites. The materials evaluated were the Clearfil Majesty Posterior, Filtek Z550 and G-aenial Posterior composites. A total of 189 specimens were fabricated for microhardness, roughness, gloss and color tests. The specimens were divided into three finishing and polishing systems: Enhance, OneGloss and Sof-Lex Spiral. Microhardness, roughness, gloss and color were measured after 24 h and after 10,000 thermocycles. Two samples from each group were evaluated using SEM and AFM. G-aenial Posterior exhibited the lowest microhardness values. The mean roughness ranged from 0.37 to 0.61 µm. The smoothest surfaces were obtained with Sof-Lex Spiral for each material. G-aenial Posterior with Enhance was determined to be the glossiest surfaces. All of the materials exhibited similar ΔE values ranging between 1.69 and 2.75. Sof-Lex Spiral discs could be used successfully to polish composites.

Resin composite monomers alter MTT and LDH activity of human gingival fibroblasts in vitro

OBJECTIVES

Substances such as monomers may be released from composite resin systems and may induce adverse effects in biological tissues. The aim of this study is to investigate the cytotoxic concentrations of resin composite monomers on cultures of human gingival fibroblasts.

METHODS

A range of dilutions of five resin composite monomers (HEMA, HPMA, DMAEMA, TEGDMA, and Bis-GMA) were added to the culture medium of human gingival fibroblasts for 24 h. Their cytotoxic effects were measured by using two colorimetric functional assays, mitochondrial dehydrogenase activity (MTT) and lactate dehydrogenase activity (LDH) assay. The logP values (water/octanol partition) of test monomers were also calculated computationally.

RESULTS

Mitochondrial reducing activity assessed with the MTT test was inhibited by all monomers and all the monomers increased the LDH release in a reproducible dose dependent manner. A wide range of TC 50 values (concentrations altering MTT and LDH activity by 50%) (0.32-5.8 mM by MTT assay and 0.36-6.7 mM by LDH assay) was observed. Ranking of composite resin monomer cytotoxicities (TC 50) were similar for both the MTT and LDH assays, (Bis-GMA>TEGDMA>DMAEMA>HPMA >HEMA). However, the MTT assay was found to be more sensitive than the LDH assay, particularly when lower doses of the tested monomers were determined. The ranking of TC 50 concentrations correlated with the calculated logP values.

SIGNIFICANCE

Monomers used in dental restorative materials show a variety of toxic effects on gingival fibroblasts. A combination approach using MTT and LDH assays provides valuable information about their toxic effects.

Mechanical properties of resin composites with filler particles aligned by an electric field

OBJECTIVES

To explore possible enhancement of the mechanical properties of resin composites by aligning the filler particles.

METHODS

The resin for the composites consisted of urethane dimethacrylate (UDMA) and 1,6-hexanediol dimethacrylate (HDDMA) mixed in the ratio of 90 to 10; the filler was silica-zirconia in two particle sizes, 1.7 microns (P50), which was mixed with the resin in the volume fractions of 29 and 48 vol%, and 0.7 micron (Z100), which was mixed with the resin in the volume fractions of 37 and 57 vol%. Particle alignment was obtained by applying a 60 Hz AC electric field across the composite before the resin was photopolymerized. The stress-strain behavior and the elastic modulus of the hardened composite were measured along the alignment axis in compression.

RESULTS

The elastic moduli of the aligned composites increased by as much as 20%, and the maximum stress sustainable in compression before significant deformation occurred was elevated. An electric field strength of the order of 1 kV mm-1 was required to obtain sufficient alignment.

SIGNIFICANCE

Besides conferring a structure to resin composites that is more like that of the natural tooth, particle alignment increased some of the mechanical properties and may have improved durability.