One-step CZT electroplating from alkaline solution on flexible Mo foil for CZTS absorber

In this work, Cu-Zn-Sn (CZT) is co-electrodeposited onto a flexible Mo substrate exploiting an alkaline bath (pH 10). The plating solution is studied by cyclic voltammetry, highlighting the effects of potassium pyrophosphate (K4P2O7) and EDTA-Na2 on the electrochemical behavior and stability of the metallic ionic species. The optimized synthesis results in a homogeneous precursor layer, with composition Cu 44 ± 2 at. %, Zn 28 ± 1 at. %, and Sn 28 ± 2 at. %. Soft and reactive annealing are employed respectively to promote intermetallic phase formation and sulfurization of the precursor to obtain CZTS. Microstructural (XRD, Raman), morphological (SEM), and compositional (EDX, XRF) characterization is carried out on CZT and CZTS films, showing a minor presence of secondary phases. Finally, photo-assisted water splitting tests are performed considering a CZTS/CdS/Pt photoelectrode, showing a photocurrent density of 1.01 mA cm−2 at 0 V vs. RHE under 1 sun illumination.

Graphical abstract

CZTS thin film solar cells on flexible Molybdenum foil by electrodeposition-annealing route

Abstract

Earth-abundant and non-toxic Kesterite-based Cu2ZnSnS4 (CZTS) thin film solar cells are successfully fabricated on flexible Molybdenum (Mo) foil substrates by an electrodeposition-annealing route. A well-adherent, densely packed, homogeneous, compact, and mirror-like CZT precursor is initially produced through electrodeposition by using a rotating working electrode. Subsequently, the co-electrodeposited CuZnSn (CZT) precursor is sulfurized in quartz tube furnace at 550 °C for 2 h in N2 atmosphere with the presence of elemental sulfur in order to form CZTS. Different characterization techniques like XRD, SEM, HR-TEM, Raman, and Photoluminescence demonstrate that almost phase-pure CZTS formed after sulfurization. A flexible Al/Al-ZnO/i-ZnO/CdS/CZTS/Mo foil solar cell is produced, where CdS is deposited by chemical bath deposition and transparent conducting oxide (TCO) is deposited by DC sputtering. The CZTS solar device shows a 0.55% power conversion efficiency on flexible Mo foil substrate and it constitutes the first prototype of this kind of solar cell produced by electrodeposition-annealing route without any surface modification of the Mo substrate.

Graphic abstract

Graphite particles induce ROS formation in cell free systems and human cells

It is commonly accepted that the toxicity of carbonaceous particulate matter (PM) is due to the production of reactive oxygen species (ROS) which induce biological damage in the exposed cells. It is also known that PM produced during the combustion processes consists of a carbonaceous core "dressed" with other organic and/or inorganic materials. In spite of this knowledge, the role of these materials in the production of ROS has not yet been clear. This work aims at understanding whether "naked" carbonaceous particles are capable of forming ROS either in cell-free or in-cell systems. The problem has been treated based on the data collected from pure graphite samples of different sizes obtained by ball-milling pure graphite for various lengths of time. The experimental approach considered Raman, ESR (spin trapping), cell viability and fluorescence spectroscopy measurements. These techniques allowed us to carry out measurements both in cell and cell-free systems and the results consistently indicate that also pure naked carbonaceous particles can catalyze the electron transfer that produces superoxide ions. The process depends on the particle size and enlightens the role of the edges of the graphitic platelets. Evidence has been collected that even "naked" graphitic nanoparticles are capable of producing ROS and decreasing the cell viability thus representing a potential danger to human health.