Niobium oxyhydroxide as a bioactive agent and reinforcement to a high-viscosity bulk-fill resin composite

OBJECTIVE

The present in vitro study incorporated niobium oxyhydroxide fillers into an experimental high-viscosity bulk-fill resin composite to improve its mechanical performance and provide it a bioactive potential.

METHODOLOGY

Scanning electron microscopy synthesized and characterized 0.5% niobium oxyhydroxide fillers, demonstrating a homogeneous morphology that represented a reinforcement for the feature. Fillers were weighed, gradually added to the experimental resin composite, and homogenized for one minute, forming three groups: BF (experimental high-viscosity bulk-fill resin composite; control), BF0.5 (experimental high-viscosity bulk-fill resin composite modified with 0.5% niobium oxyhydroxide fillers), and BFC (commercial bulk-fill resin composite Beautifil Bulk U, Shofu; positive control). In total, 10 specimens/groups (8 × 2 × 2 mm) underwent flexural strength (FS) tests in a universal testing machine (Instron) (500N). Resin composites were also assessed for Knoop hardness (KH), depth of cure (DoC), degree of conversion (DC), elastic modulus (E), and degree of color change (ΔE). The bioactive potential of the developed resin composite was evaluated after immersing the specimens into a simulated body fluid in vitro solution and assessing them using a Fourier-transformed infrared spectroscope with an attenuated total reflectance accessory. One-way ANOVA, followed by the Tukey's test (p<0.05), determined FS, DC, KH, and ΔE. For DoC, ANOVA was performed, which demonstrated no significant difference between groups (p<0.05).

CONCLUSIONS

The high-viscosity bulk-fill resin composite with 0.5% niobium oxyhydroxide fillers showed promising outcomes as reinforcement agents and performed well for bioactive potential, although less predictable than the commercial resin composite with Giomer technology.

Pirólise catalítica do PEBD usando como catalisador a vermiculita modificada

Resumo O polietileno de baixa densidade (PEBD) é um dos polímeros mais usados atualmente, e a grande quantidade desse polímero produzida resulta em toneladas de resíduos, que necessitam ser tratados. Neste trabalho foi realizada a pirólise termocatalítica do PEBD usando como catalisador a argila vermiculita modificada, como alternativa para o tratamento dos resíduos. A argila foi tratada com solução de ácido nítrico a diferentes concentrações e calcinada a 400 °C. Os materiais foram caracterizados por técnicas de difratometria de raios X, termogravimetria, adsorção de nitrogênio e espectroscopia de energia dispersiva. A pirólise térmica e termocatalítica foi realizada em um micro reator acoplado com GC/MS, a 500 °C. O intuito da pirólise de resíduos poliméricos é a obtenção de hidrocarbonetos leves (C<16), que possam ser empregados na indústria química e petroquímica, através de quebras na cadeia polimérica. Os resultados foram satisfatórios, com aumento no rendimento para hidrocarbonetos leves ao empregar os catalisadores chegando a 71,4% de produtos com C<16, enquanto a pirólise térmica resultou apenas de 25,8%.