[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/11/2023] [Revised: 03/16/2023] [Accepted: 03/19/2023] [Indexed: 03/30/2023]
Abstract
OBJECTIVE
The study aimed to evaluate and compare the surface micro-hardness, roughness, color, and morphology of enamel after Er,Cr:YSGG laser irradiation, followed by application of three types of bioactive glasses-based resin infiltrants, and the samples groups were challenged with the pH cycle.
METHODOLOGY
Experimental photoactivated resin infiltrants were synthesized using dimethacrylate resins, whereby three different types of bioactive glasses (BGs), i.e., 45S5, fluoridated-BG (F-BG), and borosilicate-BG (B-BG), were incorporated into the resin system. Initially, white spot lesions were created artificially on the toosth enamel surface, then irradiated with Er,Cr:YSGG laser. Then, the resin-only and BG-based resins were infiltrated on the enamel surface. All samples were pH challenged for 14 days, and the micro-hardness, surface roughness, surface morphology, and color stability (ΔE) analyses were conducted before and after the 14 days pH challenge.
RESULTS
After laser irradiation, the micro-hardness was significantly high with 45S5 group compared to resin-only (p = 0.021), F-BG (p = 0.042), and B-BG (p = 0.001) groups. After the pH challenge, the micro-hardness values for all groups were reduced significantly (p ≤ 0.05). The surface roughness was least with the resin-only group and showed a non-significant difference with F-BG (p = 0.34) and significant differences with both B-BG (p = 0.005), and 45S5 (p = 0.010) groups. After the pH cycle, the roughness of all groups was increased significantly (p ≤ 0.05), except B-BG group showed a non-significant difference (p = 0.528). The B-BG group showed significantly high ΔE between day 0 and baseline compared to resin-only (p = 0.0008), F-BG (p = 0.017), and 45S5 (p = 0.029), whereas between day 14 and baseline, the lowest ΔE value was observed for B-BG (14.2 ± 2.10) and maximum for the resin-only (20.57 ± 2.47) group. The SEM images showed pitting on the surface of all resin infiltrant groups after 14 days of pH challenge.
CONCLUSION
The morphological difference was observed after the laser irradiation on the enamel surface. The differences in micro-hardness, surface roughness, and color were observed after the application of experimental resin infiltrants and significant differences were observed after the pH challenge.