Sorption of Bisphenol A as Model for Sorption Ability of Organoclays

The arrangement of bisphenol A molecules into organoclays and their interactions with the intercalated surfactant were studied. The organoclays were prepared via solid-state intercalation of four cationic surfactants, such as dodecyltrimethyl-, tetradecyltrimethyl-, hexadecyltrimethyl-, and didodecyldimethyl-ammonium, as bromide salts, at different loading levels into the interlayers of two natural clays. The natural clays, the prepared organoclays, and the spent organoclays were characterized by X-ray powder diffraction, infrared spectroscopy, and scanning electron microscopy. X-ray powder diffraction measurements showed successive interlayer expansions of the d₀₀₁ basal spacing due to the intercalation of the cationic surfactants and the bisphenol A sorption. The increased d₀₀₁ basal spacing of the organoclays after bisphenol A sorption indicates that the molecules are integrated between the alkyl chains of the surfactant in the organoclays interlayers. Infrared spectroscopy was employed to probe the intercalation of the cationic surfactants and the sorbed bisphenol A. New characteristic bands attributed to the bisphenol A phenol rings appear in the range 1518-1613 cm^-1 on the infrared spectra of the spent organoclays, proving the presence of bisphenol A in the hydrophobic interlayers. Scanning electron microscopy of the organoclays before and after BPA sorption shows that their morphology becomes fluffy and that the presence of the organic molecules expands the clay structure.

Solid-state synthesis and physico-chemical characterization of modified smectites using natural clays from Burkina Faso

Solid-state intercalation was applied to prepare organo-smectites using cationic surfactants and natural clays containing smectite at various surfactant/smectite ratios. The surfactants enter the interlayers of smectites causing a swelling of the clays. The used clays were collected in Siétougou and Diabari villages located in the eastern part of Burkina Faso. The solid-state intercalation was successful for all four surfactants applied, n-dodecyltrimethylammonium bromide, (n-C12H25(CH3)3NBr), n-tetradecyltrimethylammonium bromide, (n-C14H29(CH3)3NBr), n-hexadecyltrimethylammonium bromide (n-C16H33(CH3)3NBr) and di-n-dodecyldimethyl­ammonium bromide ((n-C12H25)2(CH3)2NBr) at different levels of the cation exchange capacity (CEC). The synthesized organo-smectites were characterized regarding relative density, structural and textural properties. XRPD data showed a systematic increase of the basal spacing of the unit cell of the smectite up to >38 Å at 2.0-CEC loading of the surfactant. This increase indicates that the surfactants penetrated into the smectite interlayers with the surfactants being arranged parallel to the layers at low concentrations and almost perpendicular at high ones. FTIR spectra of the organo-smectites showed a decrease in the intensities of the water bands at around 1630 cm-1 and 3400 cm-1, and new specific bands close to 2920 cm-1 and 2850 cm-1 were assigned to the asymmetric and symmetric stretching of CH2 groups of the surfactants, respectively.                     KEY WORDS: Smectite, Organo-smectite, Surfactant, Intercalation   Bull. Chem. Soc. Ethiop. 2021, 35(1), 43-59. DOI: https://dx.doi.org/10.4314/bcse.v35i1.4