In vivo approach of calcium deficient hydroxyapatite filler as bone induction factor

Tissue engineering combine biomaterials, cells and biologically active molecules having as a goal create functional tissues; many of the compositions are blends of a polymeric matrix with ceramic fillers, however, reduction of mechanical resistance can be a drawback on ceramic-polymer systems. In this manuscript, we investigate the potential of calcium-deficient hydroxyapatite (CDHA) whiskers, a needle shape bioceramic, to enhance mechanical and osteoconduction properties on the polymeric matrix. For this purpose, PCL scaffolds incorporating CDHA whiskers were produced by combining solvent casting and particulate leaching techniques to develop a composite scaffold that possess mechanical and biological properties which is useful for bone tissue engineering regeneration. We produced CDHA whiskers using alkaline hydrolysis of α-tricalcium phosphate and characterized by XRD, XRF and SEM. PCL/CDHA scaffolds were fabricated with a final porosity of ~70%, quantified by SEM images. Mechanical properties were evaluated by compression test. As an initial test, PCL/CDHA scaffolds were immersed in simulated body fluid to quantify apatite deposition. In vitro and in vivo studies were performed to assess cytotoxicity and bioactivity. CDHA whiskers exhibited a needle-like morphology and a Ca/P ratio equal to calcium deficient hydroxyapatite. The composite scaffolds contained interconnected pores 177 to 350 μm in size and homogeneous ceramic distribution. The addition of CDHA whiskers influences the mechanical results: higher elastic modulus and compressive strength was observed on PCL/CDHA samples. In vitro results demonstrated biocompatibility on PCL and PCL/CDHA films. In vivo data demonstrated cellular infiltration from the surrounding tissue with new bone formation that suggests bioactive potential of CDHA whiskers. Our goal was to produce a scaffold with a potential induction factor and a favorable morphology, which was proved according to this study's findings.

Porous and dense poly(L-lactic acid) and poly(D,L-lactic acid-co-glycolic acid) scaffolds: in vitro degradation in culture medium and osteoblasts culture

The use of bioresorbable polymers as a support for culturing cells has received special attention as an alternative for the treatment of lesions and the loss of tissue. The aim of this work was to evaluate the degradation in cell culture medium of dense and porous scaffolds of poly(L-lactic acid) (PLLA) and poly(D,L-lactic acid-co-glycolic acid) (50:50) (PLGA50) prepared by casting. The adhesion and morphology of osteoblast cells on the surface of these polymers was evaluated. Thermal analyses were done by differential scanning calorimetry and thermogravimetric analysis and cell morphology was assessed by scanning electron microscopy. Autocatalysis was observed in PLGA50 samples because of the concentration of acid constituents in this material. Samples of PLLA showed no autocatalysis and hence no changes in their morphology, indicating that this polymer can be used as a structural support. Osteoblasts showed low adhesion to PLLA compared to PLGA50. The cell morphology on the surface of these materials was highly dispersed, which indicated a good interaction of the cells with the polymer substrate.

Synthesis and characterization of poly(L-lactic acid) membranes: studies in vivo and in vitro

The use of biodegradable polyesters as temporary structural supports in the recuperation of damaged live tissue is a promising area of research. Poly(L-lactic acid) (PLLA) membranes can act as a support for cell fixation and growth or as a barrier against soft tissues invasion in recuperating bone tissues. In this work, five different types of PLLA membranes, which varied in their polymer-solvent ratio and their content of plasticizer were studied. For the study in vivo, 6 mm diameter disks were inserted subcutaneously in the dorsal region of 15 Wistar rats, and the reactions on rats were studied 15 days later. In another series of experiments the samples were immersed in phosphate buffer, pH 7.4 at 37 degrees C, for 30 days. Membranes without plasticizer were morphologically dense and did not allow cell invasion nor tissue adherence, in contrast to membranes with plasticizer. While porosity enhanced cell fixation and growth, it made the membrane more fragile mechanically when compared to membranes without pores.