Long term aging of selenide glasses: evidence of sub-Tg endotherms and pre-Tg exotherms

Long term aging, extending from months to several years, is studied on several families of chalcogenide glasses including the Ge-Se, As-Se, and Ge-As-Se systems. Special attention is given to the As-Se binary, a system that displays a rich variety of aging behavior intimately tied to sample synthesis conditions and the ambient environment in which samples are aged. Calorimetric (modulated DSC) and Raman scattering experiments are undertaken. Our results show all samples display a sub-Tg endotherm typically 10-70 °C below Tg in glassy networks possessing a mean coordination number r in the 2.25 < r < 2.45 range. Two sets of As(x)Se(100-x) samples aged for eight years were compared, set A consisted of slow cooled samples aged in the dark, and set B consisted of melt-quenched samples aged at laboratory environment. Samples of set B in the As concentration range, 35% < x < 60%, display a pre-T(g) exotherm, but the feature is not observed in samples of set A. The aging behavior of set A presumably represents intrinsic aging in these glasses, while that of set B is extrinsic due to the presence of light. The reversibility window persists in both sets of samples, but is less well defined in set B. These findings contrast with a recent study by Golovchak et al (2008 Phys. Rev. B 78 014202), which finds the onset of the reversibility window moved up to the stoichiometric composition (x = 40%). Here we show that the up-shifted window is better understood as resulting due to demixing of As4Se4 and As4Se3 molecules from the backbone, i.e., nanoscale phase separation (NSPS). We attribute sub-Tg endotherms to compaction of the flexible part of the networks upon long term aging, while the pre-Tg exotherm is to NSPS. The narrowing and sharpening of the reversibility window upon aging is interpreted as the slow 'self-organizing' stress relaxation of the phases just outside the intermediate phase, which itself is stress free and displays little aging.

Performance of laser bonded glass/polyimide microjoints in cerebrospinal fluid

In this paper, laser bonded microjoints between glass and polyimide is considered to examine their potential applicability in encapsulating neural implants. To facilitate bonding between polyimide and glass, a thin titanium film with a thickness of 2 microm was deposited on borosilicate glass plates by a physical vapor deposition (PVD) process. Titanium coated glass was then joined with polyimide by using a cw fiber laser emitting at a wavelength of 1.1 microm (1.0 W) to prepare several tensile samples. Some of the samples were exposed to artificial cerebrospinal fluid (aCSF) at 37 degrees C for two weeks to assess long-term integrity of the joints. Both the as-received and aCSF soaked samples were subjected to uniaxial tensile loads for bond strengths measurements. The bond strengths for the as-received and aCSF soaked samples were measured to be 7.31 and 5.33 N/mm, respectively. Although the long-term exposure of the microjoints to aCSF has resulted in 26% reduction of bond strength, the samples still retain considerably high strength as compared with the titanium-polyimide samples. The failed glass/polyimide samples were also analyzed using optical microscopy, and failure mechanisms are discussed. In addition, a two dimensional finite element analysis (FEA) was conducted to understand the stress distribution within the substrate materials while the samples are in tension. The FEA results match reasonably well with the experimental load-displacement curves for as-received samples. Detailed discussion on various stress contours is presented in the paper, and the failure mechanisms observed from the experiment are shown in good agreement with the FEA predicted ones.

A comparison between glass/polyimide and titanium/polyimide microjoint performances in cerebrospinal fluid

Assessment of neural biocompatibility requires that materials be tested with exposure in neural fluids. Laser bonded microjoint samples made from Ti coated glass substrate and polyimide film (GPI) and titanium foil and polyimide film (TIPI) were evaluated for mechanical performance before and after exposure in artificial cerebrospinal fluid (CSF) for two, four, and 12 weeks at 37 degrees C. These samples represent a critical feature, i.e., the microjoint-a major weakness in the bioencapsulation system. Both material systems showed initial degradation up to 4 weeks which then stabilized afterwards and retained similar strength until 12 weeks. The TIPI system appears to exhibit better overall performance with less degradation compared to its as-received strength. The CSF exposed TIPI samples predominantly failed at the interface, while GPI samples had mixed glass and polyimide substrate and interface failure. The amount of glass failure decreases and interface failure increases with increase in CSF exposure time. The failure mechanism of the as-received (not exposed to CSF) GPI samples under tension was predominantly flexure type failure of the glass substrate.

Laser bonded microjoints between titanium and polyimide for applications in medical implants

Bioencapsulation of medical implant devices, and neural implant devices in particular, requires development of reliable hermetic joints between packaging materials that are often dissimilar. Titanium-polyimide is one of the biocompatible material systems, which are of interest to our research groups at Wayne State University and Fraunhofer USA. We have found processing conditions for successful joining of titanium with polyimide using near-infrared diode lasers or fiber lasers along transmission bonding lines with widths ranging from 200 to 300 microm. Laser powers of 2.2 and 3.8 W were used to create these joints. Laser-joined samples were tested in a microtester under tensile loading to determine joint strengths. In addition, finite element analysis (FEA) was conducted to understand the stress distribution within the bond area under tensile loading. The FEA model provides a full-field stress distribution in and around the joint that cause eventual failure. Results from the investigation provide an initial approach to characterize laser-fabricated microjoints between dissimilar materials that can be potentially used in optimization of bio-encapsulation design.

Ageing, fragility and the reversibility window in bulk alloy glasses

Non-reversing relaxation enthalpies (ΔH(nr)) at glass transitions T(g)(x) in the P(x)Ge(x)Se(1-2x) ternary display wide, sharp and deep global minima ([Formula: see text]) in the 0.09<x<0.145 range, within which T(g) s become thermally reversing. In this reversibility window, glasses are found not to age, in contrast to ageing observed for fragile glass compositions outside the window. Thermal reversibility and lack of ageing seem to be paradigms of self-organization which molecular glasses share with protein structures which repetitively and reversibly change conformation near T(g) and the folding temperature respectively.