Influence of an internal firing of feldspathic porcelain before or after sintering on adaptation of high-translucent zirconia laminate veneers

The aim of the present study was to evaluate the influence of two different internal surface treatments, namely, the firing of feldspathic porcelain before or after zirconia sintering, on the marginal and internal adaptation of laminate veneers (LVs) made of high-translucent zirconia. A total of 33 zirconia LVs were fabricated using a CAD/CAM system and divided into three groups based on the internal surface treatment method: the pre-firing (PRE) group involved firing feldspathic porcelain before zirconia sintering, the post-firing (POS) group involved firing feldspathic porcelain after zirconia sintering, and the no treatment (NT) group involved no application of feldspathic porcelain. The adaptation of the LVs was measured using a silicone replica technique. Data were analyzed using the Kruskal-Wallis and Steel-Dwass tests (α = .05). The POS group showed significantly higher marginal discrepancy values than the PRE group across all sites. The internal space values of the PRE groups were significantly lower than those of the NT group at all sites. The internal firing of feldspathic porcelain before zirconia sintering resulted in better marginal adaptation of the high-translucent zirconia LVs than the internal firing of feldspathic porcelain after zirconia sintering. The internal firing of feldspathic porcelain before zirconia sintering can achieve uniform internal adaptation of high-translucent zirconia LVs.

Effect of firing procedures and layering thickness of porcelain on internal adaptation of zirconia cantilever resin-bonded fixed dental prostheses

PURPOSE

This study evaluated the influence of firing procedures and layering thickness of porcelain on internal adaptation of maxillary anterior cantilever zirconia resin-bonded fixed dental prostheses (RBFDPs).

METHODS

The maxillary right central incisor on a model was prepared for a single-retainer zirconia RBFDP. A total of 36 frameworks of cantilever zirconia RBFDPs were classified into three groups (CB0.5, CB1.0, and CB2.0 groups) based on the thickness of the cut-back on the facial surface (0.5 mm, 1.0 mm, and 2.0 mm, respectively). Feldspathic porcelain was layered onto the facial surface of the zirconia RBFDP frameworks. Internal space widths between the abutment tooth and the framework were measured before and after porcelain firing by a replica technique. The internal space values before and after porcelain firings were compared using the paired t-test within the same group (α = 0.05). Differences in internal space values (distortion) between before and after porcelain firing were compared using one-way analysis of varianc e and Tukey multiple comparison tests.

RESULTS

For all framework designs, internal space values after porcelain firing were significantly higher than those before firing. Among all groups, the CB0.5 group showed the lowest internal distortion values for the whole measured area. The CB2.0 group showed higher distortion values than the CB1.0 group.

CONCLUSIONS

Porcelain firing procedures negatively impacted the internal space in cantilever zirconia RBFDPs. In addition, the increased volume of layering porcelain had a negative effect on the internal distortion of ma xillary anterior cantilever zirconia RBFDPs.

Influence of roughening procedures and priming agents on shear bond strength of CAD/CAM materials to zirconia frameworks

This study investigated the influence of roughening procedures and application of primers on shear bond strengths of CAD/CAM composite resin material or ceramic material to zirconia frameworks. A CAD/CAM composite resin block (Katana Avencia Block; AVE) and lithium disilicate glass-ceramic block (IPS e.max CAD; IEC) were used as veneer materials. The veneers were divided into three surface treatment groups; HF, hydrofluoric acid etching; AB, airborne-particle abrasion; and CON, no surface treatment. Each veneer was primed with four agents: Clearfil Porcelain Bond Activator (ACT), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Porcelain Bond Activator (CPB+ACT), and no priming (UP). The zirconia frameworks and AVE or IEC veneers were resin-bonded. In the AVE specimen, AB treatment showed significantly higher shear bond strength than the other treatments at 0 and 20,000 thermocycles, except for UP and CPB+ACT groups at 20,000 thermocycles. Airborne-particle abrasion is necessary for resin bonding to Avencia blocks.