Effect of zinc oxide nanoparticles on physical and antimicrobial properties of resin-modified glass ionomer cement

Background:

To improve the limitations, many modifications in the resin-modified glass ionomer (RMGI) composition have been proposed. In this study, we evaluated the effect of different concentrations of zinc oxide (ZnO) nanoparticles incorporated into RMGI cement on its physical and antimicrobial properties.

Materials and Methods:

In this in vitro study, ZnO nanoparticles with 0–4 wt.% concentrations were incorporated into RMGI. The following tests were carried out: (a) Antibacterial activity against Streptococcus mutans tested by disc diffusion method, (b) mechanical behavior assessment by measuring flexural strength (FS) and flexural modulus (FM), (c) micro-shear bond strength (μ-SBS), and (d) fluoride and zinc release. Data were analyzed using the statistical tests of ANOVA, t-test, and Tukey's HSD post hoc in SPSS V22. The level of significancy was 0.05.

Results:

In the disc diffusion method, specimens with 2 wt.% ZnO nanoparticles showed the highest antimicrobial efficacy (P < 0.05). After 1 month of water storage, no significant difference was observed in FS and FM of the samples (P > 0.05). In 2 wt.% ZnO nanoparticles group, μSBS increased in the first 7 days but decreased by 17% after one month, which showed a significant difference with that of the control group. The fluoride release did no change in the ZnO nanoparticle-containing group compared with the control group at all time intervals.

Conclusion:

Incorporation of 2 wt.% ZnO nanoparticles into the RMGI cement adds antimicrobial activity to the cement without sacrificing FS and fluoride release properties, while decreased μSBS.

The Effect of Incorporation of 0.5 %wt. Silica Nanoparticles on the Micro Shear Bond Strength of a Resin Modified Glass Ionomer Cement

STATEMENT OF THE PROBLEM

The clinical success of glass ionomer restorations depends on the strength of resin-modified glass ionomer (RMGI) cement bonding to dentin and there is limited information available regarding the bond strength of resin modified glass ionomers containing silica nanoparticles to dental structures.

PURPOSE

The aim of this study was to compare the microshear bond strength (µSBS) of RMGI with and without silica (SiO2) nanoparticles to dentin of permanent teeth.

MATERIALS AND METHOD

In this experimental study, the occlusal surfaces of 30 freshly extracted intact third molars were ground to expose the flat dentin and after conditioning with 20% poly acrylic acid, were randomly assigned to two main groups (n=15). The first group was filled with RMGI (Fuji II LC, GC) and the second group was filled with RMGI plus 0.5%wt. silica nanoparticles. Then, each main group was divided into three subgroups, and then stored in an incubator at 37 oC with 100% humidity for 1, 7, and 30 days. The µSBS test was performed using a universal testing machine (1 mm/min). The data were analyzed by t-test, repeated measures ANOVA and Tukey test (p< 0.05).

RESULTS

There were no statistically significant differences between the mean µSBS of the groups with and without nanoparticles along the different storage periods (p> 0.05). There was significant difference in µSBS values among the three different storage periods in all the tested materials (p< 0.05).

CONCLUSION

Incorporation of 0.5 %wt. silica nanoparticles did not compromise the µSBS of Fuji II LC RMGI to dentin.