Analysis of stress gradients in physical vapour deposition multilayers by X-ray diffraction at fixed depth intervals

The objective of this article is to develop and apply a model for the design and evaluation of X-ray diffraction experiments to measure phase-specific residual stress profiles in multilayer systems. Using synchrotron radiation and angle-dispersive diffraction, the stress measurements are performed on the basis of the sin2ψ method. Instead of the traditional Ω or χ mode, the experiments are carried out by a simultaneous variation of the goniometer angles χ, Ω and φGto ensure that the penetration and information depth and the measuring direction φ remain unchanged when the polar angle ψ is varied. The applicability of this measuring and evaluation strategy is demonstrated by the example of a multilayer system consisting of Ti and TiAlN layers, alternately deposited on a steel substrate by means of physical vapour deposition.

In vitro and in vivo evaluation of biodegradable, open-porous scaffolds made of sintered magnesium W4 short fibres

A cytocompatible and biocompatible, degradable, open-porous, mechanically adaptable metal scaffold made of magnesium alloy W4 melt-extracted short fibres was fabricated by liquid phase sintering. Cylindrical samples (3×5 mm) of sintered W4 short fibres were evaluated under in vitro (L929, HOB, eudiometer, weight loss) and in vivo conditions (rabbits: 6 and 12 weeks). The in vitro corrosion environment (e.g., temperature, flow, composition of corrosion solution, exposure time) significantly influenced the corrosion rates of W4 scaffolds compared with corrosion in vivo. Corrosion rates under cell culture conditions for 72 h varied from 1.05 to 3.43 mm y(-1) depending on the media composition. Corrosion rates measured in eudiometric systems for 24 h were ~24-27 times higher (3.88-4.43 mm y(-1)) than corrosion in vivo after 6 weeks (0.16 mm y(-1)). Moreover, it was found that the cell culture media composition significantly influences the ionic composition of the extract by selectively dissolving ions from W4 samples or their corrosion products. A pilot in vivo study for 6 and 12 weeks demonstrated active bone remodelling, no foreign body reaction and no clinical observation of gas formation during W4 scaffold implantation. Long-term in vivo studies need to be conducted to prove complete degradation of the W4 scaffold and total replacement by the host tissue.

In vivo corrosion and corrosion protection of magnesium alloy LAE442

The aim of this study was to investigate whether the extruded magnesium alloy LAE442 reacts in vivo with an appropriate host response and to investigate how an additional magnesium fluoride (MgF(2)) coating influences the in vivo corrosion rate. Forty cylinders were machined from extruded LAE442 and 20 of these were coated additionally with MgF(2) and implanted into the medial femur condyle of adult rabbits. Synchrotron-radiation-based X-ray computed micro-tomography (SRmicroCT) was used to quantitatively analyse corrosion non-destructively in vivo and comparisons were made to magnesium degradation rates based on area measurements of the remaining metal on uncalcified sections. Blood concentrations of the alloying elements were measured below toxicological limits. The MgF(2) layer was no longer detected after 4 weeks of implantation by particle-induced gamma emission, and the MgF(2) coating reduced the blood content of alloying elements during the first 6 weeks of implantation with no elevated fluoride concentration in the adjacent bone. Histopathological examinations of liver showed in 9 out of 40 cases minimal infiltrations of heterophil granulocytes of unknown origin (5 LAE442, 4 LAE442+MgF(2)). The kidneys were mainly regular in structure. The synovial tissue showed a granular cell infiltration as a temporary observation in the LAE442+MgF(2) group after 2 weeks. No subcutaneous gas cavities were observed clinically and on postoperative X-rays in all animals. All specimens were scanned by SRmicroCT at 2, 4, 6 and 12 weeks postoperatively before uncalcified sections were performed. All magnesium implants have been observed in direct bone contact and without a fibrous capsule. Localized pitting corrosion occurred in coated and uncoated magnesium implants. This study shows that the extruded magnesium alloy LAE442 provides low corrosion rates and reacts in vivo with an acceptable host response. The in vivo corrosion rate can be further reduced by additional MgF(2) coating.

[Improved osseointegration of titanium implants after surface coating with polymers in a rabbit model]

In this study we present the first results of the investigation of polymer-coated titanium implants implanted in the proximal tibia and distal femora of New Zealand white rabbits. The results of DEXA scans, micro-CT, and histological analysis showed an increase of osseointegration. We suggest that controlled release kinetics after coupling of these polymers with BMP-2 can additionally increase osseointegration.