Analysis of strain sensitivity under flexural load of 3D printed carbon nanotube-doped epoxy circuits

A 3D printing system able to print circuits of conductive epoxy resin doped with carbon nanotubes (CNTs) is proposed. Different simple circuits, more specifically lines and strain gauge patterns, made of resins reinforced with 0.3, 0.5, 0.8 and 1 wt% of CNTs were printed on the surface of glass fiber laminates. It was observed that increasing the CNT content reduced the wettability of the printed circuits on the glass fiber substrate. In every case the contact angle was far below 90°. Furthermore, the strain sensing capabilities were analyzed under a flexural load. The results showed that the sensitivity increased with CNT content (with gauge factor values from 1.5 to 2.5) as a result of the prevalent effect of well-dispersed areas due to a reduction in the tunneling distance. On the other hand, the strain gauges showed a lower sensitivity (around 20%-40% less, depending on the condition) compared with line circuits due to localized compressive effects. Furthermore, good repeatability of the strain sensors was proved during cycling tests, with similar baseline and peak values for the electrical resistance in each cycle. Therefore, the proposed materials have a high potential for applications in structural health monitoring.

Influence of the chloride ion concentration on the corrosion of high-purity Mg, ZE41 and AZ91 in buffered Hank's solution

This research studied the influence of the chloride ion concentration on the corrosion behaviour of high-purity magnesium (Mg) and two Mg alloys in Hank's solution, using hydrogen evolution and weight loss. A buffer based on CO2 and NaHCO3 was used to maintain the pH constant. The corrosion behaviour was governed by a partially protective surface film, and film breakdown by the chloride ions. The carbonated calcium phosphate layer that formed in Hank's solution was important in determining the protective properties of the surface film.