The number of lymphocytes increases in the periprosthetic tissues with increasing time of implant service in non-metal-on-metal total joint arthroplasties: A role of metallic byproducts?

BACKGROUND

The objective of the study was to determine the association between periprosthetic concentrations of selected metals and changes induced in periprosthetic tissues (PT).

METHODS

PT from 24 patients with metal-on-polyethylene or ceramic-on-polyethylene total joint replacements (TJRs) were examined. Samples underwent histological examination including quantification of cellular populations. Determination of metals was performed according to the published methodology. Results were processed using correlation analysis and Principal Component Analysis (PCA), respectively.

RESULTS

Growing concentration of metals in the PT was found as a function of length of exposure (LoE). Differences in Ti, Co, Cr and V concentrations (per α = 0.05) depended on the type of alloy the implants were made from. On the contrary, the implant composition did not reflect in the different numbers of immune cells per 1 high power field, not even in distribution of the membrane type according to the Krenn classification. PCA revealed several clusters in dependence on the LoE, type of the membrane and presence of immune cells. High representation of lymphocytes in the PT was typical for clusters with the longest LoE while a higher representation of neutrophils was typical for a shorter time to reoperation.

CONCLUSIONS

Correlation between the LoE and concentrations of metals in its surroundings was demonstrated. However, the tissue image analysis cannot differentiate finer, potentially metal-induced tissue changes. Importantly, the tissues become more similar with an increasing LoE. We draw a conclusion about predominantly non-specific stimulation of the PT jointly by metal and polyethylene particles in non-metal-on-metal TJRs.

Content of distinct metals in periprosthetic tissues and pseudosynovial joint fluid in patients with total joint arthroplasty

This prospective study examined the content of metals released from total joint arthroplasty into joint fluid, whole blood and periprosthetic tissues. We determined the levels of Ti, V, Nb, Co, Cr, and Mo, using inductively coupled plasma mass spectrometry, in samples from patients who underwent reoperation of total hip or knee arthroplasty. All of the patients (n = 117) included in the study had either metal on polyethylene or ceramic on polyethylene-bearing pairs. First, our results conclusively showed that the majority of released metals were deposited in periprosthetic tissues. In this context, the bloodstream turned out to be an ineffective biomarker of the effects occurring in local tissues. Second, there was a clear time-dependent nature of metallic accumulation. Based on our extensive dataset, we found significantly elevated levels of the released metals in joint fluid and periprosthetic tissues originating from loosened implants compared to stable ones, as well as recognizable differences between the groups with stable implants and aseptic loosening. Finally, it was proved that the concentrations of metals decreased dependent on the distance of the tissue from the implant. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 107B: 454-462, 2019.

[Wear and Roughness of Bearing Surface in Retrieved Polyethylene Bicon-Plus Cups]

PURPOSE OF THE STUDY By 7th December 2016, 4,755 Bicon-Plus cups in total were implanted in the Czech Republic. Some of them have been continuously re-operated, while the most frequent reason of failure is polyethylene wear and aseptic loosening. The present study is focused on surface analysis of retrieved polyethylene Bicon-Plus cups and the determination of the roughness of their bearing surfaces. MATERIAL AND METHODS In this study, we had 13 high molecular weight polyethylene cups with the average time in situ of 8.11 years (3.6-13.7, SD 3.2) before the retrieval. The study population was composed of 3 men, 10 women, with the mean age of 53.31 years. An optical scanning method, based on the principle of active triangulation, was used to determine wear rate. The rate of wear was identified by means of an obtained scan subsequently processed with the use of the GOM Inspect software. The roughness of surfaces was analysed with the application of Contour GT-X8 profiler using the principle of phase shifting interferometry. Measurements of surface topography of the retrieved cups were performed on the entire bearing surfaces. For the individual surface changes, a typical range of surface roughness, describing the particular wear character, was determined. By means of morphology analysis of the tested implants, three areas were identified: unworn area; area representing the worn part of the cup; and the area roughened by parallel grooving. The total surface roughness was evaluated as an arithmetic mean of the measured values. Subsequently, the values were sorted based on frequency and were classified into categories defining the particular wear mechanisms. RESULTS Wear rate of the retrieved acetabular cups was evaluated based on the wear direction vector and the size of linear wear. The average linear wear was equal to 0.13 mm/year (ranging from 0.26 to 2.29 mm/year), and the mean value of total volumetric material loss was 44.37 mm3/year (the range being from 51.80 to 1,119.7 mm3/year). Using the optical profilometer, a map of roughness distribution of the individual cups was obtained. For each implant, 76 values of roughness were evaluated. With the respect to average roughness, the samples were sorted to various categories describing: surface polishing; abrasiveadhesive wear; surfaces with preserved grooving; substantial plastic deformation. DISCUSSION The results clearly showed an increase of wear depending on implant survival; however, the tendency is not linear. This fact can be attributed to a larger amount of abrasive particles, causing an increase of wear or occurrence of surface wear in terms of micro cracks and oxidation degradation of polyethylene. This study indicates that geometry, positioning, and cup alignment during the implantation have a fundamental impact on the cup durability. Further correlation, which was observed in the case of the cup with prevailing roughness in the range from 0.1 to 0.3 μm, is a relatively wide wear vector angle determined with the use of the optical method. Considering the implants with the longest survival time with no loosening of the acetabular cup, the mean angle of direction vector was 56.8° (SD 2.1°). CONCLUSIONS The present study provides the results of morphology analysis of the retrieved Bicon-Plus cups. In general, relatively high wear rate, mainly of abrasive-adhesive character was identified. The dependence between wear and implant in situ longevity was not clearly linear, which suggests the influence of other parameters on the polyethylene wear rate. An important role of implant positioning on survival was also revealed. Moreover, it seems that it can be a more important parameter than the characteristics of the patient. Key words: total hip arthroplasty, Bicon-Plus cup, retrieval analysis, surface analysis, wear measurement, roughness, deformation, survivorship.

Silver Nanocoating Technology in the Prevention of Prosthetic Joint Infection

Prosthetic joint infection (PJI) is a feared complication of total joint arthroplasty associated with increased morbidity and mortality. There is a growing body of evidence that bacterial colonization and biofilm formation are critical pathogenic events in PJI. Thus, the choice of biomaterials for implanted prostheses and their surface modifications may significantly influence the development of PJI. Currently, silver nanoparticle (AgNP) technology is receiving much interest in the field of orthopaedics for its antimicrobial properties and a strong anti-biofilm potential. The great advantage of AgNP surface modification is a minimal release of active substances into the surrounding tissue and a long period of effectiveness. As a result, a controlled release of AgNPs could ensure antibacterial protection throughout the life of the implant. Moreover, the antibacterial effect of AgNPs may be strengthened in combination with conventional antibiotics and other antimicrobial agents. Here, our main attention is devoted to general guidelines for the design of antibacterial biomaterials protected by AgNPs, its benefits, side effects and future perspectives in PJI prevention.