Effect of curing method and thermocycling on flexural strength and microhardness of a new composite resin with alkaline filler

BACKGROUND

Cention N has been introduced as an alternative material for amalgam. The purpose was to investigate the flexural strength and microhardness of this material in self-cure and dual-cure modes before and after thermocycling.

MATERIALS AND METHODS

In this experimental study, 40 samples of Cention N were prepared in order to determine and compare the microhardness. Half of the samples were set by self-cure method and the other half with dual-cure method. The Vickers microhardness test was performed once after 24 h and again after 10000 thermocyclings. Three-point flexural test was used to determine and compare the flexural strength of 52 rod-shaped samples. Half of the samples were set by self-cure method and the other half with dual-cure method. Among 26 samples in each group, 13 samples were randomly selected and three-point flexural test was performed after 24 h and for another 13 samples after 10,000 thermocyclings. Data were analyzed using two-way ANOVA and paired samples t-test (P < 0.05).

RESULTS

There was a statistically significant difference between the mean of microhardness values in two curing methods (P < 0.001) and in two storage conditions (P < 0.001). The mean of dual-cure microhardness (100.99 ± 7.22) was higher than that of self-cure (64.61 ± 12.51) and the mean value associated with pre-thermocycling (89.75 ± 15.84) was higher than that of the post-thermocycling (76.44 ± 23.56). There was no statistically significant difference between the mean flexural strength in the two curing methods (self-cure [72.85 ± 16.26], dual cure [79.87 ± 23.07]; [P > 0.05]). However, the mean flexural strength without thermocycling (85.98 ± 21.74) was higher than that of the thermocycled group (64.24 ± 6.40) (P < 0.001).

CONCLUSION

The microhardness of Cention N in dual-cure mode was higher than that of self-cure mode, but the flexural strength of dual-cure was not significantly different from that of self-cure. Thermocycling had a significant effect on the microhardness and flexural strength.

Effect of accelerated aging and double application on the dentin bond strength of universal adhesive system

BACKGROUND

Despite the many advantages of simplified adhesive systems, there are concerns about the durability of the adhesive layer over time. The aim was to investigate the effects of various aging methods and double application of an adhesive layer on the bond strength of the universal adhesive system using etch-and-rinse (ER) and self-etch (SE) strategies.

MATERIALS AND METHODS

In this in vitro study, the occlusal enamel of 120 extracted, intact human third molars was removed to expose the dentin. Then, the samples were randomly divided into four groups of thirty according to All-Bond Universal (ABU) adhesive application strategy (ER and SE) and the number of adhesive layers (1 or 2). Then, each group was subdivided into three subgroups of ten according to aging method (control, thermal cycling, and 10% sodium hypochlorite [NaOCl]). The shear bond strength was measured at the strain rate of 0.5 mm/min. Data were analyzed using three-way ANOVA and Tukey's post hoc tests (P < 0.05).

RESULTS

The effect of adhesive application strategy (P < 0.001) and aging method (P < 0.001) on the bond strength was statistically significant, but the effect of the double application was not statistically significant (P > 0.05). In addition, the interactive effect of adhesive application strategy-aging method was significant (P = 0.005).

CONCLUSION

Using ABU with ER strategy leads to higher dentin bond strength compared to the SE method in the control and thermal cycling groups. However, no significant differences were observed between ER and SE strategies after aging with the NaOCl. Furthermore, the double application might not have any effect on the bond strength and durability.

Comparison of shear bond strength of resin-modified glass ionomer and composite resin to three pulp capping agents

Background and aims. Present study was designed to compare the bonding strength of resin-modified glass ionomer (RMGI) and composite resin to mineral trioxide aggregate (MTA), MTA mixed with Na2HPO4 (NAMTA), and calcium-enriched mixture (CEM).

Materials and methods. Thirty specimens of each CEM, NAMTA, and MTA were prepared. Composite and RMGI restorations were then placed on the samples (15 samples in six subgroups). Shear bond strength was assessed using universal testing machine. Data were analyzed with two-way ANOVA and post-hoc Tukey test. To compare the bond strength in subgroups, one-away ANOVA was applied. Significance level was set at P < 0.05.

Results. Bond strength was significantly higher to composite samples compared to RMGI samples (p<0.001). The difference in bond strength of composite samples between MTA and CEM subgroups (P=0.026) as well as MTA and NAMTA subgroups (P= 0.019) was significant, but the difference between NAMTA and CEM subgroups (P=0.56) was not significant. The differences in bond strength in subgroups of RMGI group were not significant (P>0.05).

Conclusion. Regarding shear bond strength to the tested substrates, composite was shown to be superior to RMGI. The bond of resin composite to MTA was weaker than that to CEM and NAMTA.

Effect of three different mouthrinses on microleakage of composite resin restorations with two adhesive systems after bleaching with 10% carbamide peroxide

AIM

The aim was to evaluate the effects of Oral-B (OB), Listerine (LN) and Rembrandt Plus (RM) mouthrinses on microleakage of composite resin restorations bonded with two adhesive systems after bleaching with 10% carbamide peroxide.

MATERIALS AND METHODS

A total of 60 Cl V cavities were prepared on human premolars. The occlusal and gingival margins were placed 1 mm occlusal to and apical to CEJ respectively. The teeth were randomly divided into two groups based on the adhesive system used: Excite (EX) and Clearfil SE Bond (CSE) groups. After composite resin restoration of cavities, thermocycling and bleaching with 10% carbamide peroxide for 2 hours daily for 14 days, the teeth in each adhesive group were further subdivided into three subgroups and were immersed for 12 hours in the three OB, RM and LN mouthrinses. The teeth were then placed in 2% basic fuschin for 24 hours. After dissecting the teeth, microleakage was evaluated under a stereomicroscope at 16×. Data was analyzed with multifactor ANOVA and Bonferroni test at p < 0.05.

RESULTS

Microleakage with EX was significantly higher than that with CSE (p = 0.009). Microleakage at gingival margins was significantly higher than that at occlusal margins (p = 0.15). Microleakage with OB was higher than that with LN (p = 0.02). However, there were no significant differences in microleakage between LN and RM (p = 1) and between RM and OB (p = 0.15). In addition, with the EX adhesive system, microleakage with OB was higher than that with LN and RM (p = 0.02).

CONCLUSION

In the present study, microleakage of composite resin restorations was influenced by the type of the adhesive system, mouthrinse type and the location of the cavity margin.

CLINICAL SIGNIFICANCE

Use of some mouthrinses, such as OB after bleaching can increase postrestoration microleakage of resin composite restorations bonded with etch-and-rinse adhesive systems.

The Effect of Marginal Ridge Thickness on the Fracture Resistance of Endodontically-treated, Composite Restored Maxillary Premolars

Preserving the marginal ridge of endodontically-treated composite restored maxillary premolars can act as a strengthening factor and improve fracture resistance.