Histomorphometric and biomechanical evaluation of the osseointegration around micro- and nano-level boron-nitride coated titanium dental implants

INTRODUCTION

Titanium dental implants has been coated with different materials such as polymers and biomimetic agents, bone morphogenetic protein, calcium phosphate to enhance surface properties of the titanium implants for osseointegration. The aim of this study was to evaluate the bone tissue healing around Boron Nitride-coated (BN-coated) titanium implants histomorphometrically and biomechanically and also observe the effect of different coating thicknesses on osseointegration.

MATERIALS AND METHODS

BN was coated on dental titanium implants with two different coating thicknesses by using RF magnetron sputtering system. Totally fifty-four implants were inserted into the tibias' of 12 New Zealand rabbits bilaterally under general anesthesia. All animals were sacrificed after 4-weeks. Bone-implant contact (BIC) and new bone area/total area ratios (BATA) were calculated. Also, the removal torque (RT) test was performed.

RESULTS

The highest new bone area in the medullary cavity was around the nano-BN-coated surface with 15.70%. In micro-BN-coated surface and control group, this ratio was determined as 10.48% and 8.23%, respectively. The BIC ratios in upper-side of implants and cortical-associated BIC ratios in lower-side were found significantly higher in control and micro-BN-coated group than nano-BN-coated group (p < 0.05). Similar BIC values were observed between control and micro-BN-coated groups (p > 0.05). BATA values did not show statistically significant differences between all three groups (p > 0.05). The RT values measured in all groups were found comparable and no statistically significant differences were found (p > 0.05).

CONCLUSION

No inflammatory reaction developed around any implant. Relatively more new bone formation around nano-BN-coated titanium implants indicates the promising osseoinductive effect of BN coating. BN-coated implants showed similar biomechanical and histomorphometrical outcomes to that of the conventional titanium implants through a 4-week evaluation period.

Intramedullary implants coated with cubic boron nitride enhance bone fracture healing in a rat model

BACKGROUND

Boron nitride is a biocompatible and an osteo-inductive material for orthopedic applications. The aim of this study was to evaluate the effects of two different allotrope boron nitride coated implants, cubic boron nitride and hexagonal boron nitride, on fracture healing.

METHODS

In this experimental study, a total of 24 rats were divided into three groups. Group A was the control group with Kirschner wire without coating, while the wires were coated dominantly by cubic boron nitride in Group B and hexagonal boron nitride in Group C. Then a mid-third femoral fracture was created. The fracture healing was examined in terms of new bone formation with micro-CT analysis and histopathological examination, quantitative measurement of bone turnover metabolites and scintigraphic examination of osteoblastic activity on 28th day post fracture.

RESULTS

Micro-CT measurement results revealed a statistically significant increase in bone volume/tissue volume ratio and bone surface values in group B compared to group A. Cortex diameter and osteoblast counts were statistically higher in group B compared to group A. Inflammatory response was increased in group C compared to groups A and B. Biochemical test results showed significantly increased alkaline phosphatase levels and decreased osteocalcin levels in group B compared to group A. The increase in serum phosphorus and decrease in serum calcium levels was statistically significant in group C compared to Group A.

CONCLUSION

Both types of boron nitride coating had superior fracture healing features compared to control group. Therefore, c-BN coating can accelerate the fracture healing and could lead to shorten of union time.