Concentration effect of DMSO-dry bonding on the stability of etch-and-rinse bonds

OBJECTIVES

To examine whether lower dimethyl sulfoxide (DMSO) concentrations would affect long-term bond stability of simplified or multistep water-based adhesives to dry-etched dentin.

METHODS

H3PO4-etched mid-coronal dentin surfaces from human molars were randomly blot- or air-dried for 30 s and pretreated or not with 5 or 50 % (v/v) ethanolic DMSO solutions. Untreated samples served as control. Samples were bonded with a two-step or a three-step etch-and-rinse adhesive. Restored crown segments (n = 5/group) were stored in distilled water for 24 h and sectioned for microtensile bond strength testing. Resin-dentin beams (0.8 mm2) were tested under tension until fracture (0.5 mm/min) after 24 h and one year of storage in artificial saliva at 37 °C. Nanoleakage evaluation and hybrid layer characterization were performed by SEM. Bond strength data was examined by three-way ANOVA followed by the Tukey test (α = 0.05).

RESULTS

Dry bonding produced significantly lower bond strengths than conventional wet bonding for both water-based adhesive systems (p < 0.05). DMSO-dry bonding restored bond strengths and reduced nanoleakage levels, regardless of adhesive type or DMSO concentration (p < 0.05). Bond strengths of DMSO-dry bonded samples were not significantly affected by long-term ageing regardless of adhesive type or DMSO concentration (p < 0.05).

SIGNIFICANCE

Although bonding methacrylate-based resins to etched dentin is normally performed under wet conditions, hybridization of air-dried collagen can outperform conventional wet bonding by employing water-free DMSO solutions with concentrations as low as 5 %. Reduced moisture-related technique sensitivity, higher bonding performance and improved hybrid layer stability may contribute to extend the service life of resin-dentin bonding.

The effect of prime-and-rinse approach using MDP micellar solutions on extrafibrillar demineralization and dentin bond performance

OBJECTIVE

This study investigated the effects of prime-and-rinse approach using 10-methacryloyloxydecyl dihydrogen phosphate (MDP) micellar solutions on extrafibrillar demineralization and dentin bond performance of etch-and-rinse adhesive.

METHODS

The micellar solutions were prepared by adding 15% MDP in two ethanol-aqueous (75:25, 55:45 V/V%) solutions, referring to MDP/EtOH₇₅ and MDP/EtOH₅₅. After mid-coronal dentin surfaces were either etched (control) or conditioned with MDP/EtOH₇₅ and MDP/EtOH₅₅ and rinsed, they were applied with adhesive (Adpter Single Bond 2) in dry- or wet-bonding mode and placed with composite resin (Filtek Z350 XT). They were prepared into multiple micro-beams for micro-tensile bond strengths (MTBS) testing after storage in water for 24 h or subjecting to thermocycling. The other pretreated dentin surfaces were analyzed by TF-XRD, ATR-FTIR, HRTEM, FE-SEM, contact angle measurement and nanoindentation testing. The MTBS data was analyzed with two-way ANOVA followed by LSD post-hoc test.

RESULTS

MDP/EtOH₇₅ produced significantly greater MTBS values than MDP/EtOH₅₅ and control after thermocycling aging in dry- or wet-bonding mode (P < 0.05). The ATR-FTIR spectrums shows that ratios of phosphate/monomer (1,034 cm^-1/1,716 cm^-1) on MDP/EtOH₇₅-, MDP/EtOH₅₅-treated dentin surfaces are 0.51 and 0.23, respectively. This is confirmed by HRTEM images and SAED pattern that intrafibrillar minerals were mostly preserved after treatment with MDP/EtOH₇₅. MDP/EtOH₇₅ produced significantly higher elastic modulus and nanohardness on pretreated dentin surface than MDP/EtOH₅₅ (P < 0.05). TF-XRD pattern shows some MDP-Ca salts remained on the primed dentin surface.

SIGNIFICANCE

Prime-and-rinse approach using MDP/EtOH₇₅ micellar solution could produce mostly extrafibrillar demineralization, and greatly increase dentin bond durability in dry- or wet-bonding mode.

Cross-linked dry bonding: A new etch-and-rinse technique

OBJECTIVE

To determine if acid-etched, cross-linked dentin can be dehydrated without lowering bond strength below that of cross-linked wet-bonded dentin in vitro.

METHODS

Using extracted human third molars, control acid-etched dentin was bonded with Single Bond Plus, using either the wet- or dry-bonding technique. Experimental acid-etched dentin was treated with 5mass% grape seed extract (GSE) in different solvents for 1min before undergoing wet vs dry resin-dentin bonding with Single Bond Plus. Completely demineralized dentin beams were treated with 5% GSE for 0, 1 or 10min, before measuring stiffness by 3-point flexure. Other completely demineralized beams were treated similarly and then incubated in buffer for 1 week to measure the collagen solubilization by endogenous dentin proteases.

RESULTS

24h microtensile bond strengths (μTBS) in wet and dry controls were 53.5±3.6 and 9.4±1.8MPa, respectively (p<0.05). 5% GSE in water gave μTBS of 53.7±3.4 and 39.1±9.7MPa (p<0.05), respectively, while 5% GSE in ethanol gave μTBS of 51.2±2.3 and 35.3±2.0MPa (p<0.05). 5% GSE in 5% EtOH/95% water gave wet and dry μTBS of 53.0±2.3 and 55.7±5.1MPa (p>0.05). Cross-linking demineralized dentin with 5% GSE increased stiffness of dentin and decreased collagen degradation (p<0.05).

SIGNIFICANCE

5% GSE pretreatment of acid-etched dentin for 1min permits the dentin to be completely air-dried without lowering bond strength.