Synthesis and characterization of reduced graphene oxide using the aqueous extract of Eclipta prostrata

In this study, biological deoxygenation of graphene oxide (GO) using an Eclipta prostrata phytoextract was performed via the infusion method. The presence of oxide groups on the surface of graphene and removal of oxides groups by reduction were characterized through morphological and structural analyses. Field emission scanning electron microscopy images revealed that the synthesized GO and rGO were smooth and morphologically sound. Transmission electron microscopy images showed rGO developing lattice fringes with smooth edges and transparent sheets. Atomic force microscopy images showed an increase in the surface roughness of graphite oxide (14.29 nm) compared with that of graphite (1.784 nm) due to the presence of oxide groups after oxidation, and the restoration of surface roughness to 2.051 nm upon reduction. Energy dispersive X-ray analysis indicated a difference in the carbon/oxygen ratio between GO (1.90) and rGO (2.70). Fourier-transform infrared spectroscopy spectrum revealed peak stretches at 1029, 1388, 1578, and 1630 cm^-1 for GO, and a decrease in the peak intensity after reduction that confirmed the removal of oxide groups. X-ray photoelectron microscopy also showed a decrease in the intensity of oxygen peak after reduction. In addition, thermogravimetric analysis suggested that rGO was less thermally stable than graphite, graphite oxide, and GO, with rGO decomposing after heating at temperatures ranging from room temperature to 600 °C.

Fabrication of ultrasound-mediated tunable graphene oxide nanoscrolls

In this work, a cost-effective and facile method was adopted for the fabrication of graphene oxide nanoscrolls (GONS) by low frequency (20 kHz) ultrasonication with tunable dimensions. The graphene oxide (GO) was synthesized by modified Hummer's method using synthetic graphite as a base material. Later, GO suspension (0.05 g L^-1) were made using methanol as solvent and subjected to different ultrasonication conditions. It was found that GO sheets curls themselves into nanoscrolls by overcoming the energy barrier for scrolling with the help of bubble cavitation energy provided by ultrasonication. Also, the effect of ultrasonication power (100-150 W) for irradiation time (0.5-3 h) over the GONS dimensions were investigated. The spiral wounded GONS structures were shown using electron microscopy. Raman Spectroscopy, Thin-film X-Ray Diffraction, Energy Dispersive X-Ray, FT Infrared Spectroscopic analysis were also done to endorse GONS formation. Factors affecting GONS formation such as sonication power and solvent selection were studied as scrolling of GO sheets are strongly dependent on sonication parameters and solvent characteristics. It was found that GONS length varies inversely with irradiation time for identical power density. Also, a solvent with relatively large Hansen solubility parameter, lower dipole movement and less negative value of zeta potential support GONS formation of longer length. Raman analysis overlays the rapid oxygen-defect site cleavage mechanism. The obtained GONS unlocks further developments in various engineering applications like adsorption, drug delivery and filtration membrane.