Bleaching gel mixed with MI Paste Plus reduces penetration of H2O2 and damage to pulp tissue and maintains bleaching effectiveness

OBJECTIVES

MI Paste Plus remineralizer (Rem) strengthens dental structures after bleaching. We investigated the effect of Rem on the penetration of hydrogen peroxide (H₂O₂), bleaching effectiveness, and pulp inflammation after bleaching.

MATERIALS AND METHODS

Bovine disks were grouped as follows (n = 10): control (untreated), bleached (Ble; 35% H₂O₂, 30 min), Ble-Rem (H₂O₂ followed by Rem, 30 min), Rem-Ble (Rem followed by H₂O₂), Rem-Ble-Rem (Rem before and after H₂O₂), and Ble+Rem (mixture of Rem with H₂O₂, 1:1, 30 min). The penetration of H₂O₂ was quantified and bleaching efficacy was analyzed. Upper rat molars (n = 10) received the same treatments at random. The rats were euthanized after two days and 30 days, and their jaws were removed for histological analysis. Statistical tests were performed (P < 0.05).

RESULTS

The bleached groups, except Ble+Rem (P > 0.05), showed significant H₂O₂ penetration compared with control (P < 0.05). Color alteration analysis showed that ΔL and ΔE were significantly higher in the bleached groups than those in control (P < 0.05); the Δb of the bleached groups differed from that of control at 24 h (P < 0.05). At two days, necrosis or inflammation was observed in the bleached groups compared with control (P < 0.05), except Ble+Rem, which was similar to control (P > 0.05). At 30 days, tertiary dentin formation was significant in the bleached groups (P < 0.05), except Ble+Rem (P > 0.05).

CONCLUSION

The mixture of MI Paste Plus and bleaching gel reduces H₂O₂ penetration and pulp damage and maintains bleaching effectiveness.

CLINICAL RELEVANCE

Because bleaching can damage dental tissues, we studied a new bleaching protocol that reduces damage to the pulp tissue while maintaining bleaching efficiency: a single application of 30 min of MI Paste Plus mixed with 35% H₂O₂ bleaching gel (1:1).

Combined effects of Er: YAG laser and casein phosphopeptide-amorphous calcium phosphate on the inhibition of enamel demineralization: An in vitro study

BACKGROUND

Development of white spot lesions on enamel is a significant and common problem during the fixed orthodontic treatment. Various preventive methods have been suggested. The purpose of this study was to evaluate the preventive potential of MI Paste Plus, Er: YAG Laser and combined under similar in vitro conditions against demineralization.

MATERIALS AND METHODS

In this experimental in vitro study, 60 extracted premolars were randomly allocated to four groups (n = 15) of control, MI Paste Plus, Laser and MI + Laser (MIL). Enamel surface of each group was treated with one of above materials before and during the pH cycling for 12 days through a daily procedure of demineralization and remineralization for 3 h and 20 h, respectively. Teeth were sectioned and evaluated quantitatively by cross-sectional microhardness testing at 20 μm intervals from the outer enamel surface toward dentinoenamel junction up to 160 μm and data were analyzed using the one-way analysis of variance and Tukey test. P < 0.05 was considered as significant.

RESULTS

MIL group had the least amount of demineralization (P < 0.001). Control group (C group) had the greatest relative mineral loss and the laser group (L group) had 45% less mineral loss than the C group and there was no significant difference between the MI Paste Plus and L group (P = 0.154).

CONCLUSION

BASED ON THESE RESULTS, ER: YAG laser was able to decrease demineralization and was a potential alternative to preventive dentistry and was more effective when combined with casein phosphopeptide-amorphous calcium phosphate products.