Yu L, Sun F, Wang Y, Li W, Zheng Y, Shen G, Wang Y, Chen M. Effects of MgO nanoparticle addition on the mechanical properties, degradation properties, antibacterial properties and in vitro and in vivo biological properties of 3D-printed Zn scaffolds. Bioact Mater 2024; 37:72-85. [PMID: 38523703 PMCID: PMC10958222 DOI: 10.1016/j.bioactmat.2024.03.016] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/19/2023] [Revised: 02/29/2024] [Accepted: 03/11/2024] [Indexed: 03/26/2024] Open
Abstract
Bone tissue engineering is the main method for repairing large segment bone defects. In this study, a layer of bioactive MgO nanoparticles was wrapped on the surface of spherical Zn powders, which allowed the MgO nanoparticles to be incorporated into 3D-printed Zn matrix and improved the biodegradation and biocompatibility of the Zn matrix. The results showed that porous pure Zn scaffolds and Zn/MgO scaffolds with skeletal-gyroid (G) model structure were successfully prepared by selective laser melting (SLM). The average porosity of two porous scaffolds was 59.3 and 60.0%, respectively. The pores were uniformly distributed with an average pore size of 558.6-569.3 μm. MgO nanoparticles regulated the corrosion rate of scaffolds, resulting in a more uniform corrosion degradation behavior of the Zn/MgO scaffolds in simulated body fluid solution. The degradation ratio of Zn/MgO composite scaffolds in vivo was increased compared to pure Zn scaffolds, reaching 15.6% at 12 weeks. The yield strength (10.8 ± 2.4 MPa) of the Zn/MgO composite scaffold was comparable to that of cancellous bone, and the antimicrobial rate were higher than 99%. The Zn/MgO composite scaffolds could better guide bone tissue regeneration in rat cranial bone repair experiments (completely filling the scaffolds at 12 weeks). Therefore, porous Zn/MgO scaffolds with G-model structure prepared with SLM are a promising biodegradable bone tissue engineering scaffold.
Collapse
Affiliation(s)
- Leiting Yu
- School of Materials Science and Engineering, Tianjin University of Technology, Tianjin, 300384, China
| | - Fengdong Sun
- School of Materials Science and Engineering, Tianjin University of Technology, Tianjin, 300384, China
| | - Yuanyuan Wang
- School of Stomatology, Tianjin Medical University, Tianjin, 300070, China
| | - Wei Li
- School of Materials Science and Engineering, Tianjin University of Technology, Tianjin, 300384, China
| | - Yufeng Zheng
- School of Materials Science and Engineering, Peking University, Beijing, 100871, China
| | - Guangxin Shen
- Changzhi Medical College, Changzhi, 046000, Shanxi, China
| | - Yao Wang
- School of Stomatology, Tianjin Medical University, Tianjin, 300070, China
| | - Minfang Chen
- School of Materials Science and Engineering, Tianjin University of Technology, Tianjin, 300384, China
- National Demonstration Center for Experimental Function Materials Education, Tianjin University of Technology, Tianjin, 300384, China
| |
Collapse
|