Morphology-Dependent Immunomodulatory Coating of Hydroxyapatite/PEO for Magnesium-Based Bone Implants

One of the most critical issues concerning orthopedic implants is the risk of chronic inflammation, which poses a threat to the bone healing process. Osteo-immunomodulation plays a pivotal role in implant technology by influencing proinflammatory and anti-inflammatory responses, ultimately promoting bone healing. This study aims to investigate the morphology-dependent osteo-immunomodulatory properties of a hydroxyapatite (HA)/plasma electrolytic oxidation (PEO)-coated WE43 alloy. In this context, following the PEO process with various operational parameters (duty cycles of 50-40, 50-20, 70-40%, and frequencies of 0.5, 0.8, and 1 kHz), a layer of HA was applied as the top coating using a straightforward hot-dip process. The results revealed the formation of the PEO layer with distinct morphologies and pore sizes, depending on the operational parameters. Specifically, a uniform PEO coating with small pore sizes (5.2-5.3 μm) led to the creation of plate-like HA particles, while a random-like HA structure formed on nonuniform surfaces with large pores (7.0-11.1 μm) of PEO. Moreover, it was observed that the plate-like HA coating exhibited higher adhesion strength than the random one (classified as class 2 vs class 3 based on cross-cut standards). Furthermore, electrochemical impedance spectroscopy (EIS) and polarization studies confirmed a substantial increase in the polarization resistance (680 kΩ) and total impedance (48 559.6 Ω) for the plate-like HA/PEO as compared to the substrate (an increase of 1511-fold and 311-fold, respectively) and the random HA/PEO samples (an increase of 85-fold and 18-fold, respectively). In addition, compared to random HA coatings, there was a significant enhancement in the viability (150% control vs 96% control), proliferation, and differentiation of MG63 cells when exposed to plate-like HA coatings. Moreover, surface morphology and chemistry pronouncedly impacted macrophages' viability, morphology, and phenotype. Notably, plate-like HA coatings resulted in a higher upregulation of BMP-2 and TGF-β than proinflammatory cytokines (IL-6 and M-CSF), indicating a polarization of macrophage type 1 (M1) toward type 2 (M2). In summary, the bilayer HA/PEO coating exhibited remarkable osteo-immunomodulatory activity, making it highly appealing for use in bone implant applications.

Highly Efficient and Low-Temperature Preparation of Plate-Like ZrB₂-SiC Powders by a Molten-Salt and Microwave-Modified Boro/Carbothermal Reduction Method

To address the various shortcomings of a high material cost, energy-intensive temperature conditions and ultra-low efficiency of the conventional boro/carbothermal reduction method for the industrial preparation of ZrB₂-SiC powders, a novel molten-salt and microwave-modified boro/carbothermal reduction method (MSM-BCTR) was developed to synthesize ZrB₂-SiC powders. As a result, phase pure ZrB₂-SiC powders can be obtained by firing low-cost zircon (ZrSiO₄), amorphous carbon (C), and boron carbide (B₄C) at a reduced temperature of 1200 °C for only 20 min. Such processing conditions are remarkably milder than not only that required for conventional boro/carbothermal reduction method to prepare phase pure ZrB₂ or ZrB₂-SiC powders (firing temperature of above 1500 °C and dwelling time of at least several hours), but also that even with costly active metals (e.g., Mg and Al). More importantly, the as-obtained ZrB₂ particles had a single crystalline nature and well-defined plate-like morphology, which is believed to be favorable for enhancing the mechanical properties, especially toughness of their bulk counterpart. The achievement of a highly-efficient preparation of such high-quality ZrB₂-SiC powders at a reduced temperature should be mainly attributed to the specific molten-salt and microwave-modified boro/carbothermal reduction method.